<table cellpadding="10" cellspacing="3" class="wikitable">
<tr>
<th>Property</th>
<th>Test method</th>
<th>units</th>
<th>4275</th>
<th>4301</th>
<th>4435</th>
<th>4630</th>
<th>4645</th>
</tr>
<tr>
<td>Tensile Strength</td>
<td>ASTM D 638</td>
<td>MPa (kpsi)</td>
<td>117 (16.9)</td>
<td>113 (16.4)</td>
<td>94 (13.6)</td>
<td>81 (11.8)</td>
<td>114 (16.6)</td>
</tr>
<tr>
<td>Tensile Modulus</td>
<td>ASTM D 638</td>
<td>GPa (kpsi)</td>
<td>8.8 (1,280)</td>
<td>6.8 (990)</td>
<td>14.5 (2,100)</td>
<td>7.4 (1,080)</td>
<td>18.6 (2,700)</td>
</tr>
<tr>
<td>Tensile Elongation</td>
<td>ASTM D 638</td>
<td> %</td>
<td>2.6</td>
<td>3.3</td>
<td>1.0</td>
<td>1.9</td>
<td>0.8</td>
</tr>
<tr>
<td>Flexural Strength</td>
<td>ASTM D 790</td>
<td>MPa (kpsi)</td>
<td>208 (30.2)</td>
<td>215 (31.2)</td>
<td>152 (22.0)</td>
<td>131 (19.0)</td>
<td>154 (22.4)</td>
</tr>
<tr>
<td>Flexural Modulus</td>
<td>ASTM D 790</td>
<td>GPa (kpsi)</td>
<td>7.3 (1.060)</td>
<td>6.9 (1,000)</td>
<td>14.8 (2,150)</td>
<td>6.8 (990)</td>
<td>12.4 (1,800)</td>
</tr>
<tr>
<td>Compressive Strength</td>
<td>ASTM D 695</td>
<td>MPa (kpsi)</td>
<td>123 (17.8)</td>
<td>166 (24.1)</td>
<td>138 (20.0)</td>
<td>99 (14.4)</td>
<td>157 (22.8)</td>
</tr>
<tr>
<td>Izod Impact Strength, Notched</td>
<td>ASTM D 256</td>
<td>J/m (ft-lb/in)</td>
<td>85 (1.6)</td>
<td>64 (1.2)</td>
<td>43 (0.8)</td>
<td>48 (0.9)</td>
<td>37 (0.7)</td>
</tr>
<tr>
<td>Izod Impact Strength, Unnotched</td>
<td>ASTM D 4812</td>
<td>J/m (ft-lb/in)</td>
<td>270 (5)</td>
<td>430 (8)</td>
<td>210 (4)</td>
<td>160 (3)</td>
<td>110 (2)</td>
</tr>
<tr>
<td>Heat Deflection Temperature at 264 psi</td>
<td>ASTM D 648</td>
<td>°C (°F)</td>
<td>280 (536)</td>
<td>279 (534)</td>
<td>278 (532)</td>
<td>280 (536)</td>
<td>281 (538)</td>
</tr>
<tr>
<td>Coefficient Linear Thermal Expansion</td>
<td>ASTM D 696</td>
<td>ppm/°C (ppm/°F)</td>
<td>25 (14)</td>
<td>25 (14)</td>
<td>14 (8)</td>
<td>16 (9)</td>
<td>9 (3)</td>
</tr>
</table>