record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
6,191 | ornl_16 | annealed JPCA | austenitic_steel | irradiated | null | 250 | null | null | null | 25 | Mechanical Fracture | null | null | null | null | 235 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,192 | ornl_16 | annealed JPCA | austenitic_steel | irradiated | null | 250 | null | null | null | 110 | Mechanical Fracture | null | null | null | null | 170 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,193 | ornl_16 | annealed JPCA | austenitic_steel | irradiated | null | 250 | null | null | null | 250 | Mechanical Fracture | null | null | null | null | 165 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,194 | ornl_16 | cold-worked JPCA | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Fracture | null | null | null | null | 260 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,195 | ornl_16 | cold-worked JPCA | RAFM_steel | unirradiated | null | null | null | null | null | 100 | Mechanical Fracture | null | null | null | null | 235 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,196 | ornl_16 | cold-worked JPCA | RAFM_steel | unirradiated | null | null | null | null | null | 250 | Mechanical Fracture | null | null | null | null | 175 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,197 | ornl_16 | cold-worked JPCA | RAFM_steel | irradiated | null | 90 | null | null | null | 100 | Mechanical Fracture | null | null | null | null | 175 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,198 | ornl_16 | cold-worked JPCA | RAFM_steel | irradiated | null | 250 | null | null | null | 250 | Mechanical Fracture | null | null | null | null | 145 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,199 | ornl_16 | weldment in JPCA | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Fracture | null | null | null | null | 380 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,200 | ornl_16 | weldment in JPCA | RAFM_steel | unirradiated | null | null | null | null | null | 100 | Mechanical Fracture | null | null | null | null | 435 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,201 | ornl_16 | weldment in JPCA | RAFM_steel | unirradiated | null | null | null | null | null | 250 | Mechanical Fracture | null | null | null | null | 415 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,205 | ornl_16 | JPCA | RAFM_steel | irradiated | null | 90 | null | null | null | 90 | Mechanical Fracture | null | null | null | null | 410 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,207 | ornl_16 | US316 | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Fracture | null | null | null | null | 220 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,208 | ornl_16 | US316 | RAFM_steel | unirradiated | null | null | null | null | null | 90 | Mechanical Fracture | null | null | null | null | 215 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,209 | ornl_16 | US316 | RAFM_steel | unirradiated | null | null | null | null | null | 250 | Mechanical Fracture | null | null | null | null | 210 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,210 | ornl_16 | US316 | RAFM_steel | irradiated | null | 90 | null | null | null | 90 | Mechanical Fracture | null | null | null | null | 160 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,211 | ornl_16 | US316 | RAFM_steel | irradiated | null | 250 | null | null | null | 250 | Mechanical Fracture | null | null | null | null | 95 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,212 | ornl_16 | cold-worked US316 | RAFM_steel | unirradiated | null | null | null | neutron | null | 25 | Mechanical Fracture | null | null | null | null | 90 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,213 | ornl_16 | cold-worked US316 | RAFM_steel | unirradiated | null | null | null | null | null | 90 | Mechanical Fracture | null | null | null | null | 88 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,214 | ornl_16 | cold-worked US316 | RAFM_steel | unirradiated | null | null | null | null | null | 250 | Mechanical Fracture | null | null | null | null | 75 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,216 | ornl_16 | cold-worked US316 | RAFM_steel | irradiated | null | 250 | null | null | null | 250 | Mechanical Fracture | null | null | null | null | 72 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,218 | ornl_16 | HT-9 | RAFM_steel | unirradiated | null | null | null | null | null | 90 | Mechanical Fracture | null | null | null | null | 295 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,219 | ornl_16 | HT-9 | RAFM_steel | unirradiated | null | null | null | null | null | 250 | Mechanical Fracture | null | null | null | null | 280 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,220 | ornl_16 | HT-9 | RAFM_steel | irradiated | null | 90 | null | null | null | 90 | Mechanical Fracture | null | null | null | null | 245 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,221 | ornl_16 | HT-9 | RAFM_steel | irradiated | null | 250 | null | null | null | 250 | Mechanical Fracture | null | null | null | null | 160 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,222 | ornl_16 | HT-9 | RAFM_steel | irradiated | null | 250 | null | null | null | 25 | Mechanical Fracture | null | null | null | null | 40 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,223 | ornl_16 | F82H | RAFM_steel | unirradiated | null | null | null | null | null | 250 | Mechanical Fracture | null | null | null | null | 260 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,226 | ornl_16 | EC316L | RAFM_steel | irradiated | null | 90 | null | neutron | null | 22 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,227 | ornl_16 | EC316L | RAFM_steel | irradiated | null | 250 | null | neutron | null | 25 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,229 | ornl_16 | annealed J316 | austenitic_steel | irradiated | null | 250 | null | neutron | null | 250 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,231 | ornl_16 | annealed JPCA | austenitic_steel | irradiated | null | 90 | null | null | null | 100 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,232 | ornl_16 | annealed JPCA | austenitic_steel | irradiated | null | 90 | null | null | null | 200 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,234 | ornl_16 | annealed JPCA | austenitic_steel | irradiated | null | 250 | null | null | null | 100 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,235 | ornl_16 | annealed JPCA | austenitic_steel | irradiated | null | 250 | null | null | null | 250 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,236 | ornl_16 | 316 stainless steel | austenitic_steel | irradiated | 1 | 288 | light-water reactor | neutron | null | 288 | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
6,237 | ornl_16 | austenitic steels | other | irradiated | 10 | 288 | null | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
6,242 | ornl_16 | V-4Cr-4Ti | vanadium_alloy | irradiated | 31 | 425 | DHCE | neutron | 35 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,244 | ornl_16 | V-4Cr-4Ti | vanadium_alloy | irradiated | 31 | 425 | DHCE | neutron | 35 | 425 | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
6,245 | ornl_16 | V-4Cr-4Ti | vanadium_alloy | irradiated | 0 | 425 | DHCE | neutron | 10 | 425 | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
6,246 | ornl_16 | V-18Ti | vanadium_alloy | irradiated | null | 420 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
6,247 | ornl_16 | V-20Ti | vanadium_alloy | irradiated | null | 420 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
6,251 | ornl_16 | V-4.1Cr-4.3Ti | vanadium_alloy | irradiated | 18 | 425 | DHCE | neutron | 225 | null | Swelling | null | null | null | null | null | null | null | null | null | 1.2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,253 | ornl_16 | V-4.1Cr-4.3Ti | vanadium_alloy | irradiated | 31 | 425 | DHCE | neutron | 550 | null | Swelling | null | null | null | null | null | null | null | null | null | 2.1 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,254 | ornl_16 | V-4Cr-4Ti | vanadium_alloy | irradiated | 18 | 600 | DHCE | neutron | 5 | null | Swelling | null | null | null | null | null | null | null | null | null | 0.6 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,255 | ornl_16 | V-4Cr-4Ti | vanadium_alloy | irradiated | 31 | 425 | DHCE | neutron | 35 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,256 | ornl_16 | V-4Cr-4Ti | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | 23.2 | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,258 | ornl_16 | V-4Cr-4Ti | vanadium_alloy | irradiated | null | 500 | FFTF | neutron | 29 | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,259 | ornl_16 | V-4Cr-4Ti | vanadium_alloy | irradiated | null | 600 | FFTF | neutron | 6.7 | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,260 | ornl_16 | V-4Cr-4Ti | vanadium_alloy | irradiated | 34 | 600 | FFTF | neutron | null | -196 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
6,262 | ornl_16 | V-4Cr-4Ti | vanadium_alloy | irradiated | 31 | 425 | FFTF | neutron | 9.9 | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
6,263 | ornl_16 | V-4Cr-4Ti | vanadium_alloy | irradiated | 18 | 425 | FFTF | neutron | 5.5 | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
6,264 | ornl_16 | V-4Cr-4Ti | vanadium_alloy | irradiated | 18 | 500 | FFTF | neutron | 11.5 | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
6,265 | ornl_16 | V-4Cr-4Ti | vanadium_alloy | irradiated | 18 | 600 | FFTF | neutron | 2.9 | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
6,266 | ornl_16 | V-4.1Cr-4.3Ti | vanadium_alloy | unirradiated | 0 | null | null | null | null | -200 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,267 | ornl_16 | V-4.1Cr-4.3Ti | vanadium_alloy | irradiated | 28 | 600 | null | neutron | null | -200 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,268 | ornl_16 | V-4.1Cr-4.3Ti | vanadium_alloy | irradiated | 20 | 600 | null | neutron | null | -100 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,269 | ornl_16 | V-4.1Cr-4.3Ti | vanadium_alloy | irradiated | 34 | 425 | null | neutron | null | -200 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,270 | ornl_16 | V-4.1Cr-4.3Ti | vanadium_alloy | irradiated | 18 | 425 | null | neutron | null | -200 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,272 | ornl_16 | V-4Cr-4Ti | vanadium_alloy | irradiated | 18 | 600 | DHCE | neutron | 5 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,273 | ornl_16 | V-4Cr-4Ti | vanadium_alloy | irradiated | 31 | 425 | DHCE | neutron | 35 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,276 | ornl_16 | V-4.1Cr-4.3Ti | vanadium_alloy | irradiated | 18 | 600 | DHCE | neutron | 130 | -200 | Mechanical Fracture | null | null | null | null | null | 73.15 | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
6,277 | ornl_16 | DHCE capsule 5C1 | other | irradiated | null | 600 | FFTF/MOTA | neutron | 16 | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
6,278 | ornl_16 | DHCE capsule 5E2 | other | irradiated | null | 425 | FFTF/MOTA | neutron | 26 | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
6,280 | ornl_16 | DHCE capsule 5E1 | other | irradiated | null | 500 | FFTF/MOTA | neutron | 57 | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
6,281 | ornl_16 | DHCE capsule 4D2 | other | irradiated | null | 425 | FFTF/MOTA | neutron | 70 | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
6,283 | ornl_16 | DHCE capsule 4D1 | other | irradiated | null | 425 | FFTF/MOTA | neutron | 99 | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
6,284 | ornl_16 | V-5Cr-5Ti Alloy Weldments (Base metal) | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 259.9 | 457.8 | 19.3 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
6,288 | ornl_16 | V-5Cr-5Ti Alloy Weldments (Glovebox weld <10 ppm O2) | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 402 | 533.7 | 11.6 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
6,289 | ornl_16 | V-5Cr-5Ti Alloy Weldments (Glovebox weld <10 ppm O2) | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 357.1 | 637.8 | 9.2 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
6,290 | ornl_16 | V-5Cr-5Ti Alloy Weldments (Conventional gas shielded weld) | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 155.8 | 426.8 | 2 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
6,291 | ornl_16 | V-5Cr-5Ti Alloy Weldments (Conventional gas shielded weld) | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 266.8 | 475 | 0.7 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
6,292 | ornl_16 | V-5Cr-5Ti Alloy Weldments (Glove box weld in Argon + 2% O2) | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 201.3 | 329.6 | 0.3 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
6,294 | ornl_16 | V-5Cr-5Ti Alloy Weldments (Glove box weld in Argon + 2% O2) | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 235.8 | 235.8 | 0.3 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
6,297 | ornl_16 | V alloy | vanadium_alloy | irradiated | 30 | 420 | ANL | neutron | null | 25 | Mechanical Tensile | null | null | null | null | null | 273.15 | 290 | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
6,298 | ornl_16 | V alloy | vanadium_alloy | irradiated | 30 | 420 | ANL | neutron | null | 25 | Mechanical Tensile | 690 | null | null | null | null | 273.15 | 330 | null | null | null | null | null | null | 1 | false | ornl_extraction | null | null | null | null |
6,299 | ornl_16 | V alloy | vanadium_alloy | irradiated | 30 | 420 | ANL | neutron | null | 25 | Mechanical Tensile | 800 | null | null | null | null | 273.15 | 370 | null | null | null | null | null | null | 1 | false | ornl_extraction | null | null | null | null |
6,301 | ornl_16 | V alloy | vanadium_alloy | irradiated | 30 | 420 | ANL | neutron | null | 25 | Mechanical Tensile | 1,060 | null | null | null | null | 483.15 | 440 | null | null | null | null | null | null | 1 | false | ornl_extraction | null | null | null | null |
6,302 | ornl_16 | V alloy | vanadium_alloy | irradiated | 30 | 420 | ANL | neutron | null | 25 | Mechanical Tensile | null | null | null | null | null | 523.15 | 550 | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
6,303 | ornl_16 | V alloy | vanadium_alloy | irradiated | 30 | 420 | ANL | neutron | null | 25 | Mechanical Tensile | 1,180 | null | null | null | null | 523.15 | 570 | null | null | null | null | null | null | 1 | false | ornl_extraction | null | null | null | null |
6,304 | ornl_16 | V-10Ti | vanadium_alloy | irradiated | 17.7 | 400 | HFIR | neutron | 50 | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,306 | ornl_16 | V-1Ni | vanadium_alloy | irradiated | 17.7 | 400 | HFIR | neutron | 50 | null | Swelling | null | null | null | null | null | null | null | null | null | 15.3 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,307 | ornl_16 | V-1Ni | vanadium_alloy | irradiated | 17.7 | 400 | HFIR | neutron | 50 | null | Swelling | null | null | null | null | null | null | null | null | null | 0.25 | 5 | 50,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,308 | ornl_16 | V-10Ti | vanadium_alloy | irradiated | 17.7 | 400 | HFIR | neutron | 50 | null | Swelling | null | null | null | null | null | null | null | null | null | 2.33 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,309 | ornl_16 | V-10Ti-1Ni | vanadium_alloy | irradiated | 17.7 | 400 | HFIR | neutron | 50 | null | Swelling | null | null | null | null | null | null | null | null | null | 1.53 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,310 | ornl_16 | V-Cr binaries | vanadium_alloy | irradiated | 42 | 400 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,311 | ornl_16 | V-Cr binaries | vanadium_alloy | irradiated | 77 | 600 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,312 | ornl_16 | V-10Ti | vanadium_alloy | irradiated | 36 | 420 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,313 | ornl_16 | V-10Ti | vanadium_alloy | irradiated | 77 | 420 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,314 | ornl_16 | V-Ti-Cr alloys | vanadium_alloy | irradiated | 39 | 420 | FFTF | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 523.15 | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,315 | ornl_16 | V-3Ti-1Si | vanadium_alloy | irradiated | null | 420 | FFTF | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,316 | ornl_16 | V alloy | vanadium_alloy | irradiated | 44 | 520 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
6,317 | ornl_16 | V alloy | vanadium_alloy | irradiated | 44 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
6,318 | ornl_16 | V alloy | vanadium_alloy | irradiated | 15 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.4 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
6,319 | ornl_16 | V-Cr binary alloys | vanadium_alloy | irradiated | 50 | 600 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,320 | ornl_16 | pure V | vanadium_alloy | irradiated | null | 500 | HFIR | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,321 | ornl_16 | pure V | vanadium_alloy | irradiated | null | 600 | HFIR | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
6,322 | ornl_16 | Cu-2%Be (CWA) | copper_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 950 | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,323 | ornl_16 | CuNiBe (TMT) | copper_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 900 | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,324 | ornl_16 | 316 SS (CW) | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 750 | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
6,325 | ornl_16 | CuNiBe (CWA) | copper_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 750 | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.