train_900 | What is described in this image? | In Figures 9(a), it can be seen the micrograph obtained for the synthesized PLGA sample. In Figure 9 | |
train_901 | What is described in this image? | As shown in Fig. 7, the VO2 composite coatings are uniform, with an intrinsic yellowish green color | |
train_902 | What is described in this image? | Fig. 11(a) shows the CV response for P111i4FSI with 0.5 mol kg-1 LiFSI at 25 ℃ as a function of the | |
train_903 | What is described in this image? | Fig. 7. Variation of the reduced isothermal cure rate, a, defined by eqn (4) with the fractional ext | |
train_904 | What is described in this image? | An example of the theoretical signal of the first-order phase transition is shown in Fig. 2. It begi | |
train_905 | What is described in this image? | reduce the computation time, only a single pipe with surrounding storage material should be calculat | |
train_906 | What is described in this image? | Fig. 8. Temperature evolution of experimental infrared spectra. The FT-IR spectra of titled compound | |
train_907 | What is described in this image? | 100, Jilin Province Jinli Test Technology Co., Ltd.) adapted to the standard GB/T 1440-92. Specimens | |
train_908 | What is described in this image? | Fig. 5 shows the SEM micrographs of pure PVDF membrane, PVDF/SiO2 8%, PVDF/SiO2 32%, PVDF/MCM-41 8%, | |
train_909 | What is described in this image? | The phase-transition behaviors of the compounds were observed under an optical polarizing microscope | |
train_910 | What is described in this image? | Figure 4 shows the TGA results for the triiodide perovskite powder formed from solutions of a 1 to 1 | |
train_911 | What is described in this image? | Steam-assisted gravity drainage (SAGD) [64] is one of the fastest growing methods that has been abun | |
train_912 | What is described in this image? | Fig. 8. TEM images of NEPCM before/after freeze-thaw test. The thermal and mechanical stability of t | |
train_913 | What is described in this image? | are plotted as a function of the logarithmic cooling rate in Fig. 7. The data scattering is due to e | |
train_914 | What is described in this image? | Fig. 6 shows the melting temperature and latent heat of the modified SAT sample with 0.5 wt% CMC and | |
train_915 | What is described in this image? | Fig. 5 Isothermal crystallization experiment on 5 mg isotactic polypropylene (iPP) at 122℃ after coo | |
train_916 | What is described in this image? | In order to quantify the mechanical strength, the stress–strain behavior of solid polymer electrolyt | |
train_917 | What is described in this image? | Fig. 8(a) and (b) shows the PL emission spectra of the un-annealed and annealed samples, respectivel | |
train_918 | What is described in this image? | showed exceptional behaviour as it had only a glass transition while melting observed in Fig. 1 was | |
train_919 | What is described in this image? | Heat capacity measurement during isothermal curing The ability to measure a sample's heat capacity c | |
train_920 | What is described in this image? | Figure 8. Optical polarisation of microstructure of HNSPE | |
train_921 | What is described in this image? | Fig. 10 shows the variation of the dielectric permittivity ( 8 ) with frequency for the PVP:KBrO4 (9 | |
train_922 | What is described in this image? | In order to determine and compare the biocompatibility of levan-pNIPA hydrogels with pNIPA hydrogel, | |
train_923 | What is described in this image? | Fig. 1. Shaped specimen used for the uniaxial (a) and the biaxial (b) experiments. The extrusion-cas | |
train_924 | What is described in this image? | Fig. 2. Pareto chart of the standardized effects for SLM parameters on the relative density. 3.1. Ef | |
train_925 | What is described in this image? | Amphiphilic conetworks (APCN) and their gels are mechanically more stable than their pure homopolyme | |
train_926 | What is described in this image? | The TG and DTG curves, obtained in air, are shown in Fig. 6. The mechanism of thermo-oxidative degra | |
train_927 | What is described in this image? | Fig. 2A shows the XRD patterns of Sr-HAp samples produced at varying synthesis times from 20 to 40 m | |
train_928 | What is described in this image? | Fig. 11. PY-PI-TOFMS of HPAPOA. preset at 500 °C with nitrogen as the carrier gas. The accumulated s | |
train_929 | What is described in this image? | Figure 4. A schematic diagram of the influence of aging on a glass transition. (A) A rapidly cooled | |
train_930 | What is described in this image? | The XRD of the PVA/SER blend nanocomposites offers details on the structural changes of blend matrix | |
train_931 | What is described in this image? | also cannot be too high because severe salt leakage will appear if the void space within the porous | |
train_932 | What is described in this image? | The curves of the heat release rate (HRR) of PCEP and PCEP/OVPOSS hybrids are shown in Figure 8. The | |
train_933 | What is described in this image? | Fig. 8(a), (b) and (c) shows the variation of COF with sliding speed for the neat bio-epoxy and the | |
train_934 | What is described in this image? | Fig. 5. Change of specific heat as a function of total water at the glass transition temperature: se | |
train_935 | What is described in this image? | sule was carried out and presented in Fig. 17 which includes (1) the broken particles of the polymer | |
train_936 | What is described in this image? | | by linear fitting of T, "N versus concentration for 7, 9 and 10 (see Figure 6); however, these mat | |
train_937 | What is described in this image? | Fig. 6. Variation of PLA conversion derivative with temperature during the thermal decomposition of | |
train_938 | What is described in this image? | formalism. The huge discrepancies between experimental X-ray and theoretical data are observed. Thes | |
train_939 | What is described in this image? | Fig. 4 DSC curves of PN-free samples (heating rate = 2 K min-1) (AN/CMCA (9:0.3) or AN/PVA (9:1)), i | |
train_940 | What is described in this image? | 3.4. Structure analysis of the obtained rigid polyurethane foams The analysis and correlation of th | |
train_941 | What is described in this image? | Another problem with interpretation of DSC curves arises sometimes in the case of existence of incon | |
train_942 | What is described in this image? | Fig. 8. Optical micrographs and the 2D-FFT images for 25 wt% UHMWPE isothermally phase separation at | |
train_943 | What is described in this image? | (P21/c), and tetragonal rutile-type VO2 (R) (P42/mnm) [1]. Their crystal structures are listed in Fi | |
train_944 | What is described in this image? | (E'), loss modulus (E"), and damping factor (tan 8) of TPU/organoclay nanocomposites and their prist | |
train_945 | What is described in this image? | In this case, we used a similar method as the one presented for the saline solutions to determine Th | |
train_946 | What is described in this image? | Fig. 2. XRD patterns of the (a) SiO2, (b) paraffin and (c) MEPCM3. SiO2 shell The XRD patterns of th | |
train_947 | What is described in this image? | Fig. 4. (a) Melt peak temperature, Tm, plotted against number-average molar mass Fig. 4a shows the d | |
train_948 | What is described in this image? | Shown in Figure 29 is the time derivative plot of the same normalized curve of alpha with all three | |
train_949 | What is described in this image? | Contact Angle is a good indication of hydrophilic property of the material. The static contact angle | |
train_950 | What is described in this image? | Fig. 9. Average flexural strength and standard deviation of unconditioned and saturated GFRP bars te | |
train_951 | What is described in this image? | The aqueous aggregation behavior of multiblock copolymers composed solely of thermo-responsive block | |
train_952 | What is described in this image? | The results are shown in Tables 5a and 5b and Figure 5. The phase transition process was controlled | |
train_953 | What is described in this image? | For a porous material with a narrow pore size distribution, the melting point depression AT of the d | |
train_954 | What is described in this image? | 10-4 and a 29 nm thick film with B = 7.7 x 10-4 aged at 338 K for 360 min. We have previously explor | |
train_955 | What is described in this image? | To measure the viscosity of the beeswax fluid, a characterization was performed. The viscosity was m | |
train_956 | What is described in this image? | The synthesized iron oxide nanoparticles and annealed iron oxide-SiO2 coreshell powders displayed th | |
train_957 | What is described in this image? | Fig. 2 shows the FT-IR spectra of polystyrene, palmitoyl chloride and polystyrene-graft-PA copolymer | |
train_958 | What is described in this image? | Fig. 7 The schematics view of molecules of indomethacin in the pore at room temperature (a) and high | |
train_959 | What is described in this image? | The dynamic mechanical behaviour of the different samples has been studied. Fig. 7 depicts the tempe | |
train_960 | What is described in this image? | against logio[ 7-r (1)] in Fig. 18. The present Raman results also reveal that as viewed by CS mode | |
train_961 | What is described in this image? | Figure 4 represents an illustrative DSC curve of the synthesized glassy sample of the system 50P2O5- | |
train_962 | What is described in this image? | The effect of durian skin fibre content from 0 to 40 wt% and pretreatment of DSF on the impact stren | |
train_963 | What is described in this image? | Materials and sample preparation 2.1 NTO and TZTN (Fig. 1) were synthesized according to literatures | |
train_964 | What is described in this image? | Anomalies in the definition of Tg from cp curves alone are clearly illustrated in Figure 2 in which | |
train_965 | What is described in this image? | Fig. 7. Shape memory properties of EP-60 after several fold-deploy cycles. because most of the const | |
train_966 | What is described in this image? | 3. The morphology of PLA and W7p is observed with SEM and the results are shown in Fig. 2. From Fig. | |
train_967 | What is described in this image? | Fig. 7. PXRD plots of (a) IND 50:50 milled HMEs, (b) ITZ 50:50 milled HMEs, (c) GSF 30:70 milled HME | |
train_968 | What is described in this image? | Figure 9. DSC thermograms of IND/GLU blends showing the presence of two distinct Ty's (cycle 3). The | |
train_969 | What is described in this image? | Figure 3 shows DSC thermograms of PHB samples in the first and second heating runs and in the coolin | |
train_970 | What is described in this image? | where To is the initial temperature (300 K) and a is the heating rate. The objective of all these me | |
train_971 | What is described in this image? | The tan 8 of the cured films as a function of reactive diluent content is shown in Fig. 8. The Tg an | |
train_972 | What is described in this image? | DSC analysis is the most valid method to determine the thermal energy storage properties of PCMs, si | |
train_973 | What is described in this image? | Figure 2. Domain spacing and grain size as a function of salt concentration for SEO(16-16) and SEO(4 | |
train_974 | What is described in this image? | Under careful control of the amount of hydrazine hydrate and hydrothermal reaction temperature, pure | |
train_975 | What is described in this image? | This peak (heat flow graph) provides us with important information regarding the PCM's thermal prope | |
train_976 | What is described in this image? | Figure 8. Influence of polyethylene glycol (PEG) molecular weight on V-notched Charpy impact strengt | |
train_977 | What is described in this image? | Thermal degradation measurements were carried out in the temperature range of 25-600 ℃ for SKF 32, F | |
train_978 | What is described in this image? | CSBO had four cyclic carbonate groups per soy oil molecule and a viscosity of 41.9 Pa s. The charact | |
train_979 | What is described in this image? | Figure 3. Raman spectra of [C6H5NH3]2SiFg  and 213 K, as evidenced by | |
train_980 | What is described in this image? | where Qnorm is the normalized heat flux of a sample, with no thermal gradients and exhibiting a ther | |
train_981 | What is described in this image? | at which the local segmental motion start up. Similar peak is not obvious for PLA in Fig. 7 but it i | |
train_982 | What is described in this image? | The presence of a Ca2p photoelectron peak in the XPS spectra of as-received PLA spool material, Figu | |
train_983 | What is described in this image? | increases. However, in stark contrast to the neat system, the transition of PEG confined in the chan | |
train_984 | What is described in this image? | Based on the cold crystallization enthalpy and the melting enthalpy, the degree of crystallinity of | |
train_985 | What is described in this image? | tallization behavior of a Zr-based BMG [16], we found that the quenched-in crystalline phase indeed | |
train_986 | What is described in this image? | Mixtures with the Same Anion. Mixing Pyr14TFSI with Pyr13TFSI and Pyr14FSI with Pyr13FSI results in | |
train_987 | What is described in this image? | plot (figure 8) for this glass including the @bos values after QES subtraction. It is evident that, | |
train_988 | What is described in this image? | (obtained by in situ quenching from 748 K at a rate of 5000 K s-1) transforms on heating into the su | |
train_989 | What is described in this image? | Fig. 11 shows the measured flexural properties of the neat PLA and PLA/GF composite samples annealed | |
train_990 | What is described in this image? | Experimental data of the quasi-isothermal Figure 1. The raw heat capacity data of the three quasi-is | |
train_991 | What is described in this image? | Fig. 10 shows the change in tan 8 with frequency for the prepared films at RT. It is obvious that th | |
train_992 | What is described in this image? | is 29.5 kg/mol.61 The experimental results in Figures 1-8 were recorded from a PMMA oligomer with mo | |
train_993 | What is described in this image? | In the cold crystallisation transition in Fig. 5, shown expanded in Fig. 7, there again appears to b | |
train_994 | What is described in this image? | (Table 1, entry 3) to allow for monitoring of the monomer conversion and the growth of the polymer c | |
train_995 | What is described in this image? | On the other hand, it is known that the crystal morphology plays an important role in the developmen | |
train_996 | What is described in this image? | Fig. 12 Heat flow during the cooling of the plaster with PCM addition | |
train_997 | What is described in this image? | Lipid-metal Ion Complexes-The interaction of different divalent cations with 1,2-dipalmitoyl lecithi | |
train_998 | What is described in this image? | melting polymorph phenomenon was obtained having several melting peaks (Fig. 3). A broad peak was ob | |
train_999 | What is described in this image? | Hypothetical model outputs are shown in Fig. 3, with low, intermediate and high values for k selecte |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.