record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
2,350 | ornl_10 | 12Cr-1MoVW | RAFM_steel | irradiated | 5 | 365 | FFTF | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,352 | ornl_10 | 12Cr-1MoVW | RAFM_steel | irradiated | 4 | 365 | FFTF | neutron | 1 | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,353 | ornl_10 | 9Cr steel | RAFM_steel | unirradiated | null | 365 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 254.15 | null | null | null | null | null | null | 10.5 | 0.8 | false | ornl_extraction | null | null | null | null |
2,354 | ornl_10 | 9Cr steel | RAFM_steel | irradiated | null | 365 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | 254.15 | null | null | null | null | null | null | 7.6 | 0.8 | false | ornl_extraction | null | null | null | null |
2,355 | ornl_10 | 12Cr-1MoVW Steel | RAFM_steel | unirradiated | null | 365 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 370.15 | null | null | null | null | null | null | 6 | 0.8 | false | ornl_extraction | null | null | null | null |
2,356 | ornl_10 | 12Cr-1MoVW Steel | RAFM_steel | irradiated | null | 365 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | 370.15 | null | null | null | null | null | null | 3.6 | 0.8 | false | ornl_extraction | null | null | null | null |
2,357 | ornl_10 | 9Cr steel | RAFM_steel | irradiated | 13 | 390 | EBR-II | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,360 | ornl_10 | 12Cr-1MoVW | RAFM_steel | irradiated | 26 | 390 | EBR-II | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,361 | ornl_10 | 12Cr-1MoVW | RAFM_steel | irradiated | 10 | 365 | FFTF | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,362 | ornl_10 | 12Cr-1MoVW | RAFM_steel | irradiated | 17 | 365 | FFTF | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,363 | ornl_10 | 9Cr steel | RAFM_steel | irradiated | 5 | 365 | FFTF | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,364 | ornl_10 | 12Cr-1MoVW | RAFM_steel | irradiated | 4 | 365 | FFTF | neutron | 1 | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,367 | ornl_10 | F82H | RAFM_steel | unirradiated | 0 | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 679 | 811 | 5 | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,368 | ornl_10 | F82H | RAFM_steel | irradiated | 6.7 | 365 | null | neutron | null | 25 | Mechanical Tensile | 697 | 780 | 6.9 | null | null | null | 679 | 811 | 5 | null | null | null | null | 0.95 | false | ornl_extraction | null | null | null | null |
2,369 | ornl_10 | F82H | RAFM_steel | irradiated | 35.8 | 405 | null | neutron | null | 25 | Mechanical Tensile | 671 | 764 | 7.8 | null | null | null | 679 | 811 | 5 | null | null | null | null | 0.95 | false | ornl_extraction | null | null | null | null |
2,370 | ornl_10 | F82H | RAFM_steel | irradiated | 37 | 550 | null | neutron | null | 25 | Mechanical Tensile | 470 | 717 | 9.5 | null | null | null | 679 | 811 | 5 | null | null | null | null | 0.95 | false | ornl_extraction | null | null | null | null |
2,371 | ornl_10 | F82H | RAFM_steel | irradiated | 28.3 | 670 | null | neutron | null | 25 | Mechanical Tensile | 253 | 442 | 24.8 | null | null | null | 679 | 811 | 5 | null | null | null | null | 0.95 | false | ornl_extraction | null | null | null | null |
2,372 | ornl_10 | F82H | RAFM_steel | irradiated | 37.1 | 750 | null | neutron | null | 25 | Mechanical Tensile | 213 | 355 | 28.3 | null | null | null | 679 | 811 | 5 | null | null | null | null | 0.95 | false | ornl_extraction | null | null | null | null |
2,375 | ornl_10 | F82H | RAFM_steel | unirradiated | null | null | null | null | null | 600 | Mechanical Tensile | null | null | null | null | null | null | 320 | 380 | 28 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,377 | ornl_10 | F82H | RAFM_steel | irradiated | 21.5 | 400 | null | neutron | null | 20 | Mechanical Tensile | 780 | 810 | 14 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,380 | ornl_10 | type 316 (12-13 wt % Ni) | austenitic_steel | irradiated | 13 | 600 | ORR | neutron | 12 | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,381 | ornl_10 | PCA (16 wt % Ni) | austenitic_steel | irradiated | 7 | 400 | ORR | neutron | 12 | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,382 | ornl_10 | austenitic stainless steels (SA and CW) | austenitic_steel | irradiated | 10 | 330 | ORR | neutron | null | 330 | Mechanical Tensile | 1,000 | 1,000 | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,383 | ornl_10 | SAJ316 | RAFM_steel | irradiated | 7 | 60 | ORR | neutron | null | 60 | Mechanical Tensile | 850 | null | 1 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,385 | ornl_10 | PCA 25% C. W | RAFM_steel | irradiated | 10 | 400 | ORR | neutron | 10 | 400 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,386 | ornl_10 | PCA 25% C. W | RAFM_steel | irradiated | 50 | 400 | ORR | neutron | 130 | 400 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,388 | ornl_10 | 25% CW PCA austenitic Steel | austenitic_steel | irradiated | 7 | 200 | ORR | neutron | 12 | 200 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,389 | ornl_10 | 25% CW PCA austenitic Steel | austenitic_steel | irradiated | 7 | 400 | ORR | neutron | 12 | 400 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,390 | ornl_10 | 25% CW PCA | austenitic_steel | irradiated | 7 | 400 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,391 | ornl_10 | 25% CW PCA | austenitic_steel | unirradiated | 0 | null | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,392 | ornl_10 | SA PCA | RAFM_steel | irradiated | 11 | 500 | ORR MFE 4A/4B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,395 | ornl_10 | 25% CW PCA | austenitic_steel | irradiated | 7 | 400 | ORR-MFE-6J/7J | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,396 | ornl_10 | SA PCA | RAFM_steel | irradiated | 13 | 400 | ORR-MFE-4 | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.4 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,398 | ornl_10 | 20% Cold-worked 316 SS | austenitic_steel | irradiated | 10 | 250 | null | neutron | null | 250 | Mechanical Fracture | null | null | null | null | 75 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,399 | ornl_10 | Annealed 316 SS | austenitic_steel | irradiated | 30 | 250 | null | neutron | null | 250 | Mechanical Fracture | null | null | null | null | 85 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,401 | ornl_10 | SA PCA austenitic stainless steel | austenitic_steel | irradiated | 13 | 400 | ORR | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.35 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,402 | ornl_10 | CW PCA austenitic stainless steel | austenitic_steel | irradiated | 13 | 400 | ORR | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,403 | ornl_10 | SA PCA austenitic stainless steel | austenitic_steel | irradiated | 13 | 330 | ORR | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,404 | ornl_10 | CW PCA austenitic stainless steel | austenitic_steel | irradiated | 13 | 330 | ORR | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,405 | ornl_10 | PCA austenitic stainless steel | austenitic_steel | irradiated | 7.4 | 500 | ORR | neutron | 15 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,406 | ornl_10 | SA PCA | RAFM_steel | irradiated | 13 | 400 | ORR | neutron | 230 | null | Swelling | null | null | null | null | null | null | null | null | null | 0.38 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,407 | ornl_10 | 25% CW PCA | austenitic_steel | irradiated | 13 | 400 | ORR | neutron | 230 | null | Swelling | null | null | null | null | null | null | null | null | null | -0.05 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,408 | ornl_10 | 25% CW PCA | austenitic_steel | irradiated | 7.4 | 400 | ORR | neutron | 130 | null | Swelling | null | null | null | null | null | null | null | null | null | -0.08 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,409 | ornl_10 | SA PCA | RAFM_steel | irradiated | 13 | 330 | ORR | neutron | 230 | null | Swelling | null | null | null | null | null | null | null | null | null | 0.18 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,410 | ornl_10 | 25% CW PCA | austenitic_steel | irradiated | 13 | 330 | ORR | neutron | 230 | null | Swelling | null | null | null | null | null | null | null | null | null | 0.16 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,411 | ornl_10 | 25% CW PCA | austenitic_steel | irradiated | 13 | 330 | ORR | neutron | 230 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | 15,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,412 | ornl_10 | 25% CW PCA | austenitic_steel | irradiated | 7.4 | 60 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,414 | ornl_10 | 25% CW PCA | austenitic_steel | irradiated | 7.4 | 330 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,416 | ornl_10 | 25% CW PCA | austenitic_steel | irradiated | 7.4 | 400 | ORR | neutron | 130 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | 35,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,417 | ornl_10 | 25% CW PCA | austenitic_steel | irradiated | 7.4 | 60 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,418 | ornl_10 | 25% CW PCA | austenitic_steel | irradiated | 7.4 | 200 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,420 | ornl_10 | 25% CW PCA | austenitic_steel | irradiated | 7.4 | 400 | ORR | neutron | 130 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,421 | ornl_10 | SA PCA | RAFM_steel | irradiated | 13 | 330 | ORR | neutron | 230 | null | Swelling | null | null | null | null | null | null | null | null | null | 0.2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,422 | ornl_10 | CW PCA | RAFM_steel | irradiated | 13 | 330 | ORR | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,423 | ornl_10 | CW PCA | RAFM_steel | irradiated | 7.4 | 60 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,426 | ornl_10 | CW PCA | RAFM_steel | irradiated | 7.4 | 400 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,427 | ornl_10 | CW PCA | RAFM_steel | irradiated | 7.4 | 330 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 8 | 30,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | 1.5 | null |
2,428 | ornl_10 | SA PCA | RAFM_steel | irradiated | 13 | 330 | ORR | neutron | 230 | null | Swelling | null | null | null | null | null | null | null | null | null | 0.35 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,430 | ornl_10 | SA PCA | RAFM_steel | irradiated | 13 | 400 | ORR | neutron | 230 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,431 | ornl_10 | 25% CW PCA | austenitic_steel | irradiated | 13 | 400 | ORR | neutron | 230 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,432 | ornl_10 | 316+Ti (R1-heat) | austenitic_steel | irradiated | 44 | 300 | HFIR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,433 | ornl_10 | SA 316 | austenitic_steel | irradiated | 0.03 | 90 | RTNS-II | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,434 | ornl_10 | SA PCA | RAFM_steel | irradiated | 13 | 400 | ORR | neutron | 230 | null | Swelling | null | null | null | null | null | null | null | null | null | 0.3 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,436 | ornl_10 | 25% CW PCA | austenitic_steel | irradiated | 13 | 330 | ORR | neutron | 230 | null | Swelling | null | null | null | null | null | null | null | null | null | 0.2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,437 | ornl_10 | SA PCA | RAFM_steel | irradiated | 13 | 330 | ORR | neutron | 230 | null | Swelling | null | null | null | null | null | null | null | null | null | 0.2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,438 | ornl_10 | SA PCA | RAFM_steel | irradiated | 7.4 | 330 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,439 | ornl_10 | SA PCA | RAFM_steel | irradiated | 7.4 | 400 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,440 | ornl_10 | 25% CW PCA | austenitic_steel | irradiated | 7.4 | 60 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,441 | ornl_10 | 25% CW PCA | austenitic_steel | irradiated | 7.4 | 200 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,443 | ornl_10 | Austenitic Stainless Steels | austenitic_steel | irradiated | null | 600 | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,445 | ornl_10 | Austenitic Stainless Steels | austenitic_steel | irradiated | null | 55 | null | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,446 | ornl_10 | 10Kh12G20V | RAFM_steel | irradiated | null | 365 | MOTA 2B | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,447 | ornl_10 | Fe-19.0Mn-13.0Cr-1.0W-0.32Si 0.09C | RAFM_steel | irradiated | null | 420 | MOTA 2B | neutron | null | 600 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,448 | ornl_10 | Fe-15Cr-15Mn | ferritic_model_alloy | unirradiated | null | 300 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,449 | ornl_10 | Fe-15Cr-15Mn | ferritic_model_alloy | unirradiated | null | 400 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,450 | ornl_10 | Fe-15Cr-15Mn | ferritic_model_alloy | unirradiated | null | 500 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,451 | ornl_10 | Fe-15Cr-15Mn | ferritic_model_alloy | unirradiated | null | 600 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,452 | ornl_10 | Fe-15Cr-15Mn | ferritic_model_alloy | unirradiated | null | 700 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,454 | ornl_10 | Fe-15Cr-15Mn | ferritic_model_alloy | unirradiated | null | 500 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,455 | ornl_10 | Fe-15Cr-15Mn | ferritic_model_alloy | unirradiated | null | 600 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,456 | ornl_10 | Fe-15Cr-15Mn | ferritic_model_alloy | unirradiated | null | 700 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,457 | ornl_10 | Fe-15Cr-15Mn | ferritic_model_alloy | unirradiated | null | 300 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,458 | ornl_10 | Fe-10Cr-30Mn | ferritic_model_alloy | unirradiated | null | 300 | null | null | null | null | Mechanical Hardness | null | null | null | 250 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,459 | ornl_10 | Fe-10Cr-30Mn | ferritic_model_alloy | unirradiated | null | 300 | null | null | null | null | Mechanical Hardness | null | null | null | 193 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,462 | ornl_10 | Fe-10Cr-30Mn | ferritic_model_alloy | unirradiated | null | 500 | null | null | null | null | Mechanical Hardness | null | null | null | 244 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,463 | ornl_10 | Fe-10Cr-30Mn | ferritic_model_alloy | unirradiated | null | 500 | null | null | null | null | Mechanical Hardness | null | null | null | 209 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,464 | ornl_10 | Fe-10Cr-30Mn | ferritic_model_alloy | unirradiated | null | 500 | null | null | null | null | Mechanical Hardness | null | null | null | 286 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,465 | ornl_10 | Fe-10Cr-30Mn | ferritic_model_alloy | unirradiated | null | 600 | null | null | null | null | Mechanical Hardness | null | null | null | 173 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,466 | ornl_10 | Fe-10Cr-30Mn | ferritic_model_alloy | unirradiated | null | 600 | null | null | null | null | Mechanical Hardness | null | null | null | 206 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,467 | ornl_10 | Fe-10Cr-30Mn | ferritic_model_alloy | unirradiated | null | 600 | null | null | null | null | Mechanical Hardness | null | null | null | 263 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,468 | ornl_10 | Fe-10Cr-30Mn | ferritic_model_alloy | unirradiated | null | 700 | null | null | null | null | Mechanical Hardness | null | null | null | 169 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,469 | ornl_10 | Fe-10Cr-30Mn | ferritic_model_alloy | unirradiated | null | 600 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 15.88 | 6,270.2 | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,470 | ornl_10 | Fe-30Mn | ferritic_model_alloy | unirradiated | null | 300 | null | null | null | null | Mechanical Hardness | null | null | null | 226 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,471 | ornl_10 | Fe-30Mn | ferritic_model_alloy | unirradiated | null | 300 | null | null | null | null | Mechanical Hardness | null | null | null | 212 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,472 | ornl_10 | Fe-30Mn | ferritic_model_alloy | unirradiated | null | 400 | null | null | null | null | Mechanical Hardness | null | null | null | 255 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,473 | ornl_10 | Fe-30Mn | ferritic_model_alloy | unirradiated | null | 400 | null | null | null | null | Mechanical Hardness | null | null | null | 293 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,474 | ornl_10 | Fe-30Mn | ferritic_model_alloy | unirradiated | null | 500 | null | null | null | null | Mechanical Hardness | null | null | null | 271 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,479 | ornl_10 | Fe-30Mn | ferritic_model_alloy | unirradiated | null | 600 | null | null | null | null | Mechanical Hardness | null | null | null | 163 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,480 | ornl_10 | Fe-30Mn | ferritic_model_alloy | unirradiated | null | 700 | null | null | null | null | Mechanical Hardness | null | null | null | 114 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,481 | ornl_10 | V-10Cr | vanadium_alloy | irradiated | 114 | null | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 5.5 | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.