record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
2,608 | ornl_10 | Marz Copper | copper_alloy | irradiated | 0.34 | 400 | DR-3 | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.3 | 2.4 | 180,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,610 | ornl_10 | Marz Copper | copper_alloy | irradiated | 34.1 | 414 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.09 | 2.1 | 53,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | 2.9 | null |
2,611 | ornl_10 | Cu-5Ni | copper_alloy | irradiated | 34.1 | 414 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.15 | 2.6 | 66,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | 2 | null | 4.3 | null |
2,612 | ornl_10 | Marz Copper | copper_alloy | irradiated | 31.6 | 529 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.31 | 2.5 | 140,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | 3.4 | null |
2,613 | ornl_10 | Cu-5Ni | copper_alloy | irradiated | 31.6 | 529 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.4 | 2.5 | 210,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | 2 | null | 3.6 | null |
2,615 | ornl_10 | Pure Copper | copper_alloy | irradiated | 1 | 420 | LAMPF | proton | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,616 | ornl_10 | Cu-5Ni | copper_alloy | irradiated | 0.25 | 335 | LAMPF | proton | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | 2 | null | null | null |
2,618 | ornl_10 | Pure Copper | copper_alloy | irradiated | 0.3 | 400 | OR-3 | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,620 | ornl_10 | Pure Copper | copper_alloy | irradiated | 0.8 | 400 | OR-3 | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,621 | ornl_10 | Pure Copper | copper_alloy | irradiated | 34 | 414 | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,622 | ornl_10 | Cu-5Ni | copper_alloy | irradiated | 34 | 414 | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | 2 | null | null | null |
2,623 | ornl_10 | Pure Copper | copper_alloy | irradiated | 32 | 529 | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,624 | ornl_10 | Cu-5Ni | copper_alloy | irradiated | 32 | 529 | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | 2 | null | null | null |
2,625 | ornl_10 | Pure Copper | copper_alloy | irradiated | 1.3 | 400 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.25 | null | 7,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,626 | ornl_10 | pure copper | copper_alloy | irradiated | null | 250 | DR-3 | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | 100,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,628 | ornl_10 | pure copper | copper_alloy | irradiated | null | 335 | LAMPF | proton | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | 10,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,629 | ornl_10 | Copper Alloys | copper_alloy | irradiated | null | 411 | FFTF-MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,630 | ornl_10 | Copper Alloys | copper_alloy | irradiated | null | 414 | FFTF-MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,631 | ornl_10 | Copper Alloys | copper_alloy | irradiated | null | 529 | FFTF-MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,633 | ornl_10 | high purity copper | copper_alloy | irradiated | 30 | 385 | MOTA-IF | neutron | 100 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,634 | ornl_10 | high purity copper | copper_alloy | irradiated | 30 | 410 | MOTA-IF | neutron | 100 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,635 | ornl_10 | Cu-5Ni | copper_alloy | irradiated | 30 | 410 | MOTA-IF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | 2 | null | null | null |
2,636 | ornl_10 | 99.999% copper | copper_alloy | irradiated | 10 | 250 | ion_beam | ion | null | 250 | Swelling | null | null | null | null | null | null | null | null | null | 0.5 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,639 | ornl_10 | 99.999% copper | copper_alloy | irradiated | 30 | 350 | ion_beam | ion | null | 350 | Swelling | null | null | null | null | null | null | null | null | null | 4.8 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,640 | ornl_10 | Glidcop A125 with CuAg, CuAu, CuTiNi, and CuTiAg brazes | copper_alloy | irradiated | 30 | 600 | MOTA 2B | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,641 | ornl_10 | Glidcop A115 induction brazes | copper_alloy | irradiated | 30 | 400 | MOTA 2B | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,642 | ornl_10 | ZrO2 | copper_alloy | irradiated | 30 | 600 | MOTA 2B | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,643 | ornl_10 | Pure Cu, Cu binary alloys | copper_alloy | irradiated | 30 | 500 | MOTA 2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,644 | ornl_10 | tu-graphite composite and Cu-Al O,-W fiber composite | carbon_graphite | irradiated | 20 | 400 | MOTA 2B | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,645 | ornl_10 | Pure Cu and various Cu alloys | copper_alloy | irradiated | 10 | 418 | MOTA 2A | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,647 | ornl_10 | Generation 1.5 and 2.0 Copper Alloys | copper_alloy | irradiated | null | 411 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,648 | ornl_10 | Generation 1.5 and 2.0 Copper Alloys | copper_alloy | irradiated | null | 414 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,649 | ornl_10 | Generation 1.5 and 2.0 Copper Alloys | copper_alloy | irradiated | null | 529 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,650 | ornl_10 | Dispersion Strengthened Copper Alloys | copper_alloy | irradiated | null | 411 | FFTF/MOTA | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,651 | ornl_10 | Dispersion Strengthened Copper Alloys | copper_alloy | irradiated | null | 414 | FFTF/MOTA | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,652 | ornl_10 | Dispersion Strengthened Copper Alloys | copper_alloy | irradiated | null | 529 | FFTF/MOTA | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,653 | ornl_10 | Glidcop CuAl25 | copper_alloy | irradiated | 100 | 411 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,654 | ornl_10 | Cu-2.0Be | copper_alloy | irradiated | 100 | 411 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,656 | ornl_10 | pure copper | copper_alloy | irradiated | 100 | 400 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 50 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,657 | ornl_10 | Cu-5Ni | copper_alloy | irradiated | null | 400 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | 2 | null | null | null |
2,658 | ornl_10 | Marz Copper | copper_alloy | irradiated | 34 | 414 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 18 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,660 | ornl_10 | Marz Copper | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 48 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,661 | ornl_10 | Marz Copper | copper_alloy | irradiated | 32 | 529 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,664 | ornl_10 | CuBeNi (CWA, U3) | copper_alloy | irradiated | 34 | 414 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,665 | ornl_10 | CuBeNi (CWA, U3) | copper_alloy | irradiated | 32 | 529 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,667 | ornl_10 | CuBeNi (CWA, U4) | copper_alloy | irradiated | 32 | 529 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,668 | ornl_10 | CuBe (CWA) | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.3 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,669 | ornl_10 | CuBe (CWA) | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.4 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,670 | ornl_10 | CuBe (SAA) | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.6 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,671 | ornl_10 | CuBe (SAA) | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.4 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,672 | ornl_10 | MZC (CWA, U6) | copper_alloy | irradiated | 34 | 414 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,673 | ornl_10 | MZC (CWA, U6) | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.4 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,674 | ornl_10 | MZC (CWA, U6) | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 8.3 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,675 | ornl_10 | MZC (CWA, U6) | copper_alloy | irradiated | 32 | 529 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,676 | ornl_10 | MZC (CWA, U7) | copper_alloy | irradiated | 34 | 414 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.3 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,677 | ornl_10 | MZC (CWA, U7) | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,678 | ornl_10 | MZC (CWA, U7) | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 8.4 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,679 | ornl_10 | CuCrZr | copper_alloy | irradiated | 34 | 414 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,680 | ornl_10 | CuCrZr | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,681 | ornl_10 | MZC (MIT #2) | copper_alloy | irradiated | 34 | 414 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,682 | ornl_10 | MZC (MIT #2) | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,683 | ornl_10 | MZC (MIT #2) | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.6 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,684 | ornl_10 | MZC (MIT #3) | copper_alloy | irradiated | 34 | 414 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.9 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,685 | ornl_10 | MZC (MIT #3) | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,686 | ornl_10 | MZC (MIT #3) | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,688 | ornl_10 | Marz Cu | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 31 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,690 | ornl_10 | CuAl15+B | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 11 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,691 | ornl_10 | CuAl25 | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,692 | ornl_10 | CuAl25 + Weld | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 10 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,693 | ornl_10 | CuAl25 + Weld | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 43 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,696 | ornl_10 | ODE1 | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 28 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,697 | ornl_10 | ODE1 | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 53 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,698 | ornl_10 | ODS steel | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 37 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,699 | ornl_10 | ODS steel | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 67 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,700 | ornl_10 | ODE2 | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 18 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,701 | ornl_10 | ODE2 | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 39 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,702 | ornl_10 | ODE3 | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 31 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,704 | ornl_10 | ODS steel | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 10 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,705 | ornl_10 | ODS steel | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 24 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,706 | ornl_10 | CuNiTi(VK) | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,707 | ornl_10 | CuNiTi(VL) | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,708 | ornl_10 | Pure Copper | copper_alloy | irradiated | 25 | 412.5 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 20 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,709 | ornl_10 | Pure Copper | copper_alloy | irradiated | 50 | 412.5 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 45 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,710 | ornl_10 | Cu-5Ni | copper_alloy | irradiated | 50 | 412.5 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 25 | null | null | null | 0.85 | false | ornl_extraction | 2 | null | null | null |
2,711 | ornl_10 | CuAl15 Annealed | copper_alloy | irradiated | 100 | 412.5 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 11 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,712 | ornl_10 | CuAl20 20% Cold-Worked | copper_alloy | irradiated | 100 | 412.5 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,713 | ornl_10 | CuAl25 Cold-Worked | copper_alloy | irradiated | 100 | 412.5 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -1 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,714 | ornl_10 | CuAl25 | copper_alloy | irradiated | 100 | 400 | MOTA-IE | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 19 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,716 | ornl_10 | CuAl25 (Generation 1.0) | copper_alloy | irradiated | 100 | 400 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,718 | ornl_10 | CuCr | copper_alloy | irradiated | 115 | 450 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 13 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,719 | ornl_10 | CuHf | copper_alloy | irradiated | 50 | 450 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,720 | ornl_10 | CuHf | copper_alloy | irradiated | 100 | 450 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,721 | ornl_10 | MZC 90% CWA | copper_alloy | irradiated | 100 | 450 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 6.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,722 | ornl_10 | CuCrZr | copper_alloy | irradiated | 100 | 450 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,723 | ornl_10 | MIT #3 | copper_alloy | irradiated | 100 | 450 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,724 | ornl_10 | MIT #2 | copper_alloy | irradiated | 100 | 450 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,726 | ornl_10 | Cu-2.0 Be (Solutionized and Aged) | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.4 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,727 | ornl_10 | Cu-2.0 Be (20% Cold-Worked and Aged) | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.3 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,728 | ornl_10 | Cu-2.0 Be (20% Cold-Worked and Aged) | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,729 | ornl_10 | Cu-0.3 Be-1.8 Ni (20% Cold-Worked and Aged) | copper_alloy | irradiated | 50 | 414 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.6 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.