record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
2,482 | ornl_10 | V-Ti alloys (9-20 wt.% Ti) | vanadium_alloy | irradiated | 114 | null | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1 | 42.5 | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,483 | ornl_10 | V-3Ti-1Si (BL-27) | vanadium_alloy | irradiated | 114 | null | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,484 | ornl_10 | V-15Cr-5Ti (BL-24) | vanadium_alloy | irradiated | 114 | null | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,485 | ornl_10 | V-15Cr-1Ti (BL-26) | vanadium_alloy | irradiated | 114 | null | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,487 | ornl_10 | V-18Ti | vanadium_alloy | irradiated | 114 | 420 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,488 | ornl_10 | V-20Ti | vanadium_alloy | irradiated | 114 | 420 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,489 | ornl_10 | V-15Cr-5Ti (BL 41) | vanadium_alloy | unirradiated | null | null | null | null | null | 400 | Mechanical Tensile | null | null | null | null | null | null | 450 | 520 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,490 | ornl_10 | V-7.5Cr-15Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 680 | 750 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,491 | ornl_10 | Vanstar-7 | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 530 | 620 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,492 | ornl_10 | V-Ti Alloys | vanadium_alloy | unirradiated | null | null | null | null | null | 420 | Mechanical Tensile | null | null | null | null | null | null | 380 | 540 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,493 | ornl_10 | V-Cr-5Ti Alloys | vanadium_alloy | unirradiated | null | null | null | null | null | 420 | Mechanical Tensile | null | null | null | null | null | null | 210 | 360 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | 10 | null | null |
2,494 | ornl_10 | V-3Ti-Si Alloys | vanadium_alloy | unirradiated | null | null | null | null | null | 420 | Mechanical Tensile | null | null | null | null | null | null | 180 | 400 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | 15 | null | null |
2,495 | ornl_10 | V-1Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 268 | 343 | 34 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,497 | ornl_10 | V-3Ti-0.25Si | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 367 | 465 | 33 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,498 | ornl_10 | V-3Ti-0.54Si | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 473 | 545 | 26 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,499 | ornl_10 | V alloy | vanadium_alloy | irradiated | 40 | null | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,500 | ornl_10 | V-10Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 700 | Mechanical Tensile | null | null | null | null | null | null | 277 | 488 | 27 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,501 | ornl_10 | V-12Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 491 | 573 | 23 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,502 | ornl_10 | V-12Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 100 | Mechanical Tensile | null | null | null | null | null | null | 402 | 500 | 27 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,503 | ornl_10 | V-12Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 225 | Mechanical Tensile | null | null | null | null | null | null | 347 | 464 | 26 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,505 | ornl_10 | V-12Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 433 | Mechanical Tensile | null | null | null | null | null | null | 321 | 501 | 24 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,506 | ornl_10 | V-12Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 520 | Mechanical Tensile | null | null | null | null | null | null | 303 | 488 | 22 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,508 | ornl_10 | V-12Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 650 | Mechanical Tensile | null | null | null | null | null | null | 310 | 529 | 25 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,509 | ornl_10 | V-12Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 700 | Mechanical Tensile | null | null | null | null | null | null | 299 | 513 | 26 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,510 | ornl_10 | V-15Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 533 | 627 | 37 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,511 | ornl_10 | V-15Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 100 | Mechanical Tensile | null | null | null | null | null | null | 483 | 589 | 37 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,513 | ornl_10 | V-15Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 325 | Mechanical Tensile | null | null | null | null | null | null | 368 | 522 | 30 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,514 | ornl_10 | V-15Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 420 | Mechanical Tensile | null | null | null | null | null | null | 379 | 571 | 27 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,515 | ornl_10 | V-15Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 520 | Mechanical Tensile | null | null | null | null | null | null | 360 | 567 | 27 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,516 | ornl_10 | V-15Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 600 | Mechanical Tensile | null | null | null | null | null | null | 384 | 610 | 31 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,517 | ornl_10 | V-15Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 650 | Mechanical Tensile | null | null | null | null | null | null | 373 | 573 | 30 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,518 | ornl_10 | V-15Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 700 | Mechanical Tensile | null | null | null | null | null | null | 355 | 519 | 32 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,519 | ornl_10 | V-10Cr-10Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 534 | 628 | 34 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,522 | ornl_10 | V-10Cr-10Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 325 | Mechanical Tensile | null | null | null | null | null | null | 367 | 532 | 30 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,523 | ornl_10 | V-10Cr-10Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 420 | Mechanical Tensile | null | null | null | null | null | null | 364 | 570 | 30 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,524 | ornl_10 | V-10Cr-10Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 520 | Mechanical Tensile | null | null | null | null | null | null | 349 | 560 | 29 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,525 | ornl_10 | V-10Cr-10Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 600 | Mechanical Tensile | null | null | null | null | null | null | 352 | 565 | 30 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,526 | ornl_10 | V-10Cr-10Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 700 | Mechanical Tensile | null | null | null | null | null | null | 328 | 492 | 28 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,527 | ornl_10 | V-7.5Cr-15Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 636 | 717 | 28 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,528 | ornl_10 | V-7.5Cr-15Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 100 | Mechanical Tensile | null | null | null | null | null | null | 556 | 647 | 28 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,530 | ornl_10 | V-7.5Cr-15Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 325 | Mechanical Tensile | null | null | null | null | null | null | 487 | 682 | 25 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,531 | ornl_10 | V-7.5Cr-15Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 420 | Mechanical Tensile | null | null | null | null | null | null | 471 | 695 | 29 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,532 | ornl_10 | V-7.5Cr-15Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 520 | Mechanical Tensile | null | null | null | null | null | null | 468 | 730 | 28 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,533 | ornl_10 | V-7.5Cr-15Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 600 | Mechanical Tensile | null | null | null | null | null | null | 469 | 738 | 27 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,534 | ornl_10 | V-7.5Cr-15Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 650 | Mechanical Tensile | null | null | null | null | null | null | 441 | 661 | 28 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,535 | ornl_10 | V-7.5Cr-15Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 700 | Mechanical Tensile | null | null | null | null | null | null | 404 | 584 | 30 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,536 | ornl_10 | Vanstar-7 | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 411 | 571 | 37 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,537 | ornl_10 | Vanstar-7 | vanadium_alloy | unirradiated | null | null | null | null | null | 105 | Mechanical Tensile | null | null | null | null | null | null | 337 | 501 | 35 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,538 | ornl_10 | Vanstar-7 | vanadium_alloy | unirradiated | null | null | null | null | null | 225 | Mechanical Tensile | null | null | null | null | null | null | 279 | 462 | 31 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,539 | ornl_10 | V-10Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 459.3969 | 572.442 | 24.399 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
2,541 | ornl_10 | V-15Cr-5Ti (BL 23) | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 558.1555 | 642.1572 | 26.1669 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
2,542 | ornl_10 | V-15Cr-5Ti (BL 24) | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 577.7104 | 663.0236 | 23.3113 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
2,543 | ornl_10 | V-15Cr-5Ti (BL 41) | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 601.3434 | 711.0014 | 27.0546 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
2,545 | ornl_10 | V-3Ti-0.54Si | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 519.2681 | 602.8017 | 22.1016 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
2,546 | ornl_10 | V-3Ti-0.99Si | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 428.719 | 513.4361 | 23.903 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
2,547 | ornl_10 | Vanstar-7 | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 452.7675 | 603.5484 | 24.594 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
2,549 | ornl_10 | V-3Ti-Si Alloys (0-1.3% Si) | vanadium_alloy | unirradiated | null | null | null | null | null | 700 | Mechanical Tensile | null | null | null | null | null | null | 295 | 468 | 21.4 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
2,550 | ornl_10 | V alloy | vanadium_alloy | irradiated | 1 | null | FFTF | neutron | 0.02 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,551 | ornl_10 | V alloy | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,553 | ornl_10 | V-5at.%Ti | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,554 | ornl_10 | V-5at.%Cr | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,555 | ornl_10 | V-5at.%Fe | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,556 | ornl_10 | V-5at.%Nb | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,557 | ornl_10 | V-5at.%Mo | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,558 | ornl_10 | V-3Ti-1Si | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,559 | ornl_10 | V-5Cr-5Ti | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,560 | ornl_10 | V-15Cr-25Ti | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,561 | ornl_10 | V alloy | vanadium_alloy | irradiated | null | 500 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,562 | ornl_10 | V alloy | vanadium_alloy | irradiated | null | 600 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,563 | ornl_10 | V-100 appm B | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | 100 | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,564 | ornl_10 | V-500 appm B | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | 500 | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,565 | ornl_10 | V-2500 appm B | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | 2,500 | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,566 | ornl_10 | Ti-6Al-4V | titanium_alloy | irradiated | null | 425 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,567 | ornl_10 | Ti-6Al-4V | titanium_alloy | irradiated | null | 600 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,568 | ornl_10 | V-5Ti | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,569 | ornl_10 | V-20Ti | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,571 | ornl_10 | V-10Cr-5Ti | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,572 | ornl_10 | V-3Ti-0.1C | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,573 | ornl_10 | V-10Ti | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,574 | ornl_10 | V-3Ti-0.2Zr-0.1C | vanadium_alloy | irradiated | null | 425 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,575 | ornl_10 | copper | copper_alloy | irradiated | 0.25 | 400 | LASREF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | 2 | null | 1 | null |
2,576 | ornl_10 | Cu-5Ni | copper_alloy | irradiated | 30 | 420 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | 2 | null | 1 | null |
2,579 | ornl_10 | Marz Copper | copper_alloy | irradiated | 0.25 | 220 | LAMPF | proton | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,580 | ornl_10 | Marz Copper | copper_alloy | irradiated | 0.34 | 300 | DR-3 | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,581 | ornl_10 | Marz Copper | copper_alloy | irradiated | 0.34 | 420 | DR-3 | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,584 | ornl_10 | Marz Copper | copper_alloy | irradiated | 34.1 | 414 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 15.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,585 | ornl_10 | Cu-5Ni | copper_alloy | irradiated | 34.1 | 414 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 22 | null | null | null | 0.85 | false | ornl_extraction | 2 | null | null | null |
2,587 | ornl_10 | Marz Copper | copper_alloy | irradiated | 31.6 | 529 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.76 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,588 | ornl_10 | Cu-5Ni | copper_alloy | irradiated | 31.6 | 529 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.56 | null | null | null | 0.85 | false | ornl_extraction | 2 | null | null | null |
2,589 | ornl_10 | pure copper | copper_alloy | irradiated | 0.25 | 335 | LAMPF | proton | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,590 | ornl_10 | Cu-5Ni | copper_alloy | irradiated | 0.25 | 335 | LAMPF | proton | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | 2 | null | null | null |
2,592 | ornl_10 | pure copper | copper_alloy | irradiated | 0.15 | 220 | LAMPF | proton | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,594 | ornl_10 | pure copper | copper_alloy | irradiated | 34.1 | 414 | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 1,000 | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,596 | ornl_10 | pure copper | copper_alloy | irradiated | 34.1 | 414 | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,597 | ornl_10 | Cu-5Ni | copper_alloy | irradiated | 34.1 | 414 | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | 2 | null | null | null |
2,598 | ornl_10 | pure copper | copper_alloy | irradiated | 31.6 | 529 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,601 | ornl_10 | Cu-5Ni | copper_alloy | irradiated | 31.6 | 529 | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | 2 | null | null | null |
2,602 | ornl_10 | Marz copper | copper_alloy | irradiated | null | 800 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.015 | 4.8 | 1,700,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,603 | ornl_10 | Marz Copper | copper_alloy | irradiated | 0.25 | 335 | LAMPF | proton | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.19 | 2.6 | 74,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | 3 | null |
2,606 | ornl_10 | Cu-5Ni | copper_alloy | irradiated | 0.25 | 220 | LAMPF | proton | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.21 | 2.5 | 100,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | 2 | null | 3 | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.