record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
2,859 | ornl_10 | Al2O4 | ceramic_insulator | irradiated | 3 | 810 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,860 | ornl_10 | Al2O3 | ceramic_insulator | irradiated | 12 | 620 | ion_beam | ion | 100 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,861 | ornl_10 | MgAl2O4 | ceramic_insulator | irradiated | 30 | 630 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | 22 | null |
2,862 | ornl_10 | MgAl2O4 | ceramic_insulator | irradiated | 3 | 630 | ion_beam | ion | 100 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | 16 | null |
2,863 | ornl_10 | MgAl2O4 | ceramic_insulator | irradiated | 12 | 260 | ion_beam | ion | 100 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | 21 | null |
2,864 | ornl_10 | MgAl2O4 | ceramic_insulator | irradiated | 0.6 | 260 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | 2 | null |
2,866 | ornl_10 | MgAl2O4 | ceramic_insulator | irradiated | 3 | 630 | ion_beam | ion | 100 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,867 | ornl_10 | spinel | ceramic_insulator | irradiated | 12 | 630 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,869 | ornl_10 | Al2O3 | ceramic_insulator | irradiated | 0.3 | 230 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,870 | ornl_10 | Al2O3 | ceramic_insulator | irradiated | 0.3 | 750 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,871 | ornl_10 | MgAl2O4 | ceramic_insulator | irradiated | 0.1 | 600 | ion_beam | proton | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,872 | ornl_10 | spinel | ceramic_insulator | irradiated | null | 650 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,873 | ornl_10 | Al2O3 | ceramic_insulator | irradiated | 3 | 650 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,874 | ornl_10 | Al2O3 | ceramic_insulator | irradiated | 0.1 | null | ion_beam | proton | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,875 | ornl_10 | Al2O3 | ceramic_insulator | irradiated | null | 650 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,877 | ornl_10 | MgO | ceramic_insulator | irradiated | 3 | null | ion_beam | proton | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,878 | ornl_10 | MgO | ceramic_insulator | irradiated | 21 | null | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,879 | ornl_10 | Al2O3 | ceramic_insulator | irradiated | null | 100 | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,880 | ornl_10 | MgAl2O4 | ceramic_insulator | irradiated | null | 350 | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,881 | ornl_10 | SiC/SiC | SiC_composite | irradiated | null | 600 | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,882 | ornl_10 | Al2O3 | ceramic_insulator | irradiated | null | 100 | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,883 | ornl_10 | SiC/SiC | SiC_composite | irradiated | null | 350 | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,884 | ornl_10 | SiC | ceramic_insulator | irradiated | null | 100 | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,885 | ornl_10 | advanced structural ceramics | ceramic_insulator | irradiated | null | 420 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,886 | ornl_10 | advanced structural ceramics | ceramic_insulator | irradiated | null | 800 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,887 | ornl_10 | ceramic TEM disks | ceramic_insulator | irradiated | null | 600 | FFTF | neutron | null | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,888 | ornl_10 | Chemically Vapor Deposited (CVD) Silicon Carbide | SiC_composite | irradiated | 30 | 25 | ion_beam | ion | null | 25 | Mechanical Hardness | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,889 | ornl_10 | Nicalon silicon carbide fiber | SiC_composite | irradiated | 15 | 25 | ion_beam | ion | null | 25 | Mechanical Hardness | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,890 | ornl_10 | sapphire | ceramic_insulator | irradiated | null | 29 | ion_beam | proton | null | 29 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,891 | ornl_10 | sapphire | ceramic_insulator | irradiated | null | 29 | ion_beam | proton | null | 29 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,892 | ornl_10 | Y2O3 | ceramic_insulator | unirradiated | null | 400 | null | null | null | 400 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,893 | ornl_11 | MFE specimens | other | irradiated | 20 | 60 | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,894 | ornl_11 | MFE specimens | other | irradiated | 20 | 330 | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,895 | ornl_11 | stainless steel | other | irradiated | 3 | 60 | HFIR | neutron | null | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,896 | ornl_11 | Fe-15Cr-20Ni | austenitic_steel | irradiated | null | 399 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,897 | ornl_11 | Fe-15Cr-25Ni | austenitic_steel | irradiated | null | 649 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,899 | ornl_11 | 12Cr-1MoVW | RAFM_steel | irradiated | 72 | 600 | HFIR | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,900 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 11 | 400 | HFIR | neutron | 110 | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,901 | ornl_11 | solution-annealed (SA) PCA austenitic stainless steel | austenitic_steel | irradiated | 13 | 330 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,902 | ornl_11 | 25% cold-worked (CW) PCA austenitic stainless steel | austenitic_steel | irradiated | 7.4 | 400 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,903 | ornl_11 | Fe-15Cr-XNi alloys | austenitic_steel | irradiated | 1.2 | null | null | neutron | 58 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,904 | ornl_11 | titanium-modified austenitic stainless steel | austenitic_steel | irradiated | null | 550 | null | neutron | null | 550 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,906 | ornl_11 | V-Cr-Ti | vanadium_alloy | irradiated | 114 | 420 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,907 | ornl_11 | V-Cr-Ti | vanadium_alloy | irradiated | 114 | 600 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,908 | ornl_11 | Oxide dispersion strengthened copper alloys (GlidCop) | copper_alloy | irradiated | 150 | 415 | Fast Flux Test Facility | neutron | null | 415 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,909 | ornl_11 | Type 316 stainless steel (MFE-6J/7J) | austenitic_steel | irradiated | 7.4 | 400 | Oak Ridge Research (ORR) | neutron | null | 400 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,910 | ornl_11 | SiC | SiC_composite | irradiated | null | 300 | HFIR and FFTF | neutron | null | 25 | Mechanical Hardness | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,911 | ornl_11 | SiC | SiC_composite | irradiated | null | 435 | HFIR and FFTF | neutron | null | 25 | Mechanical Hardness | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,912 | ornl_11 | Nicalon fiber | SiC_composite | irradiated | null | 25 | ion_beam | ion | null | 25 | Mechanical Hardness | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,913 | ornl_11 | single crystal sapphire (alumina) | ceramic_insulator | irradiated | null | 300 | null | proton | null | 300 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,914 | ornl_11 | single crystal sapphire (alumina) | ceramic_insulator | irradiated | null | 373 | null | proton | null | 373 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,915 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 200 | null | FFTF/MOTA 2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,916 | ornl_11 | low activation alloy in the 11Cr range | RAFM_steel | irradiated | 200 | null | FFTF/MOTA 2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,917 | ornl_11 | MOTA-28 Matrix Ferritic | RAFM_steel | irradiated | null | 420 | MOTA | neutron | null | 420 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,919 | ornl_11 | MOTA-28 Matrix Ferritic | RAFM_steel | irradiated | null | 520 | MOTA | neutron | null | 520 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,921 | ornl_11 | Fe-15Cr-16Ni (Base) | RAFM_steel | irradiated | null | 600 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | 12.5 | null |
2,922 | ornl_11 | Fe-15Cr-16Ni (Base) | RAFM_steel | irradiated | null | 520 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | 7.5 | null |
2,924 | ornl_11 | Fe-15Cr-16Ni + 0.25Ti | RAFM_steel | irradiated | null | 520 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | 7 | null |
2,925 | ornl_11 | Fe-15Cr-16Ni + 0.25Ti + 0.05C | RAFM_steel | irradiated | null | 600 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | 13.5 | null |
2,926 | ornl_11 | Fe-15Cr-16Ni + 0.25Ti + 0.05C | RAFM_steel | irradiated | null | 520 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | 9 | null |
2,928 | ornl_11 | Fe-15Cr-25Ni-0.013P | austenitic_steel | irradiated | 31.8 | 600 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,929 | ornl_11 | Fe-15Cr-25Ni-0.10P | austenitic_steel | irradiated | 31.8 | 600 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,931 | ornl_11 | MOTA 1F CANISTER 2b | other | irradiated | null | 600 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,933 | ornl_11 | CANISTER 2a | other | irradiated | null | 520 | FFTF | neutron | null | null | Thermal | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,934 | ornl_11 | WEEPER 3a | other | irradiated | null | 430 | FFTF | neutron | null | null | Thermal | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,935 | ornl_11 | CANISTER 4a | other | irradiated | null | 600 | FFTF | neutron | null | null | Thermal | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,936 | ornl_11 | MOTA 2A Canister 3d | other | irradiated | null | 430 | MOTA 2A | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,937 | ornl_11 | MOTA 2A Canister 3e | other | irradiated | null | 520 | MOTA 2A | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,938 | ornl_11 | MOTA 2A Canister 3f | other | irradiated | null | 600 | MOTA 2A | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,939 | ornl_11 | Specimen holder in HFIR-MFE-330J-1 capsule | other | irradiated | null | 330 | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,941 | ornl_11 | HFIR-MFE-330J-1 capsule | other | irradiated | null | 340 | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,942 | ornl_11 | HFIR-MFE-330J-I capsule | other | irradiated | null | 180 | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,943 | ornl_11 | austenitic stainless steels | austenitic_steel | irradiated | 3 | 60 | HFIR | neutron | null | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,944 | ornl_11 | austenitic stainless steels | austenitic_steel | irradiated | 3 | 125 | HFIR | neutron | null | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,946 | ornl_11 | austenitic stainless steels | austenitic_steel | irradiated | 3 | 300 | HFIR | neutron | null | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,947 | ornl_11 | austenitic stainless steels | austenitic_steel | irradiated | 3 | null | HFIR | neutron | 42 | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,948 | ornl_11 | Fe-15Cr-25Ni | austenitic_steel | irradiated | 9.1 | 365 | FFTF/MOTA | neutron | 172 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,949 | ornl_11 | Fe-15Cr-25Ni-0.04P | austenitic_steel | irradiated | null | 365 | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,952 | ornl_11 | SiC | SiC_composite | irradiated | 3 | null | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,953 | ornl_11 | SiC | SiC_composite | irradiated | 15 | null | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,954 | ornl_11 | C/C(Pitch) | other | irradiated | 1.5 | null | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,955 | ornl_11 | C/C(PAN) | other | irradiated | 1.5 | null | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,956 | ornl_11 | Si3N4 | ceramic_insulator | irradiated | 7.5 | null | ORR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,957 | ornl_11 | Al2O3 | ceramic_insulator | irradiated | 7.5 | null | ORR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,958 | ornl_11 | MgAlO2 | ceramic_insulator | irradiated | 7.5 | null | ORR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,960 | ornl_11 | MgO-1%Li | ceramic_insulator | irradiated | 7.5 | null | ORR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
2,961 | ornl_11 | 25Ni | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 620 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
2,962 | ornl_11 | 25Ni+P | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 640 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
2,963 | ornl_11 | 45Ni | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 680 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
2,964 | ornl_11 | 25Ni (Annealed) | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 150 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
2,965 | ornl_11 | 25Ni+P (Annealed) | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 180 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
2,966 | ornl_11 | 45Ni (Annealed) | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 210 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
2,967 | ornl_11 | 59Ni isotopic tailoring experiment | other | irradiated | 6.1 | 365 | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,968 | ornl_11 | 59Ni isotopic tailoring experiment | other | irradiated | 13.9 | 495 | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,969 | ornl_11 | 59Ni isotopic tailoring experiment | other | irradiated | 8.7 | 600 | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,971 | ornl_11 | Fe-15Cr-25Ni | austenitic_steel | irradiated | null | 495 | MOTA 1E | neutron | null | 495 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
2,973 | ornl_11 | Fe-15Cr-25Ni | austenitic_steel | irradiated | null | 806 | MOTA 1E | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,974 | ornl_11 | Fe-15Cr-25Ni | austenitic_steel | irradiated | null | 629 | MOTA 1E | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,975 | ornl_11 | 25 Ni | other | irradiated | 10 | 365 | null | neutron | null | 365 | Mechanical Tensile | 700 | null | 5 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
2,976 | ornl_11 | 25 Ni + 0.04P | other | irradiated | 10 | 365 | null | neutron | null | 365 | Mechanical Tensile | 750 | null | 4 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.