record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
3,100 | ornl_11 | Fe-10Cr | RAFM_steel | irradiated | null | 510 | null | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,101 | ornl_11 | V alloy | vanadium_alloy | irradiated | 0 | 600 | HVEM | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,104 | ornl_11 | V alloy | vanadium_alloy | irradiated | 2.4 | 600 | HVEM | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,105 | ornl_11 | V-5Fe | vanadium_alloy | irradiated | 0 | 600 | HVEM | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,106 | ornl_11 | V-5Fe | vanadium_alloy | irradiated | 0.28 | 600 | HVEM | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,107 | ornl_11 | V-5Fe | vanadium_alloy | irradiated | 0.7 | 600 | HVEM | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,108 | ornl_11 | V-5Fe | vanadium_alloy | irradiated | 2.1 | 600 | HVEM | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,109 | ornl_11 | V-1Ni | vanadium_alloy | irradiated | 0 | 600 | HVEM | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,110 | ornl_11 | V-1Ni | vanadium_alloy | irradiated | 0.6 | 600 | HVEM | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,111 | ornl_11 | V-1Ni | vanadium_alloy | irradiated | 1.4 | 600 | HVEM | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,112 | ornl_11 | V-1Ni | vanadium_alloy | irradiated | 2.4 | 600 | HVEM | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,113 | ornl_11 | beryllium | beryllium | irradiated | null | 400 | HVEM | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,114 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 72 | 400 | HFIR | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,116 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 11 | 400 | HFIR | neutron | 110 | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,117 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 16 | 390 | EBR-II | neutron | 1 | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,118 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 50 | 400 | HFIR | neutron | null | 400 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,119 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 100 | 600 | HFIR | neutron | null | 600 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,120 | ornl_11 | 12Cr-1MoVW | RAFM_steel | irradiated | 50 | 400 | HFIR | neutron | null | 400 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,121 | ornl_11 | 9Cr steel | RAFM_steel | unirradiated | null | null | null | null | null | 400 | Mechanical Tensile | null | null | null | null | null | null | 754 | 848 | 8.1 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
3,122 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 43 | 400 | null | null | 36 | 400 | Mechanical Tensile | 881 | 916 | 5.8 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,123 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 60 | 400 | null | null | 49 | 400 | Mechanical Tensile | 865 | 898 | 5.6 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,124 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 37 | 400 | null | null | 30 | 400 | Mechanical Tensile | 998 | 1,018 | 4.7 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,125 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 38 | 400 | null | null | 32 | 400 | Mechanical Tensile | 1,004 | 1,027 | 4.9 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,127 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 43 | 600 | null | null | 36 | 600 | Mechanical Tensile | 385 | 405 | 10.7 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,128 | ornl_11 | 9Cr steel | RAFM_steel | unirradiated | null | null | null | null | null | 400 | Mechanical Tensile | null | null | null | null | null | null | 663 | 804 | 1.8 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
3,129 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 37 | 400 | null | null | 30 | 400 | Mechanical Tensile | 1,116 | 1,193 | 1.7 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,130 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 52 | 400 | null | null | 522 | 400 | Mechanical Tensile | 1,162 | 1,184 | 3.9 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,131 | ornl_11 | 12Cr-1MoVW | RAFM_steel | unirradiated | null | null | null | null | null | 400 | Mechanical Tensile | null | null | null | null | null | null | 786 | 954 | 5.6 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
3,132 | ornl_11 | 12Cr-1MoVW | RAFM_steel | irradiated | 52 | 400 | null | null | 121 | 400 | Mechanical Tensile | 1,101 | 1,166 | 2.3 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,133 | ornl_11 | 12Cr-1MoVW | RAFM_steel | irradiated | 72 | 400 | null | null | 161 | 400 | Mechanical Tensile | 1,083 | 1,110 | 2.3 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,134 | ornl_11 | 12Cr-1MoVW-2Ni | RAFM_steel | unirradiated | null | null | null | null | null | 400 | Mechanical Tensile | null | null | null | null | null | null | 755 | 883 | 8.1 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
3,135 | ornl_11 | 12Cr-1MoVW-2Ni | RAFM_steel | irradiated | 49 | 400 | null | null | 532 | 400 | Mechanical Tensile | 1,104 | 1,153 | 3.6 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,136 | ornl_11 | 12Cr-1MoVW-2Ni | RAFM_steel | irradiated | 70 | 400 | null | null | 719 | 400 | Mechanical Tensile | 1,013 | 1,052 | 2.9 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,138 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 54.5 | 400 | null | neutron | 73 | 400 | Mechanical Tensile | 1,250 | null | 4.5 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,139 | ornl_11 | 12Cr-1MoVW | RAFM_steel | irradiated | 54.5 | 400 | null | neutron | null | 400 | Mechanical Tensile | 1,200 | null | 3.5 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,140 | ornl_11 | 12Cr-1MoVW-2Ni | RAFM_steel | irradiated | 54.5 | 400 | null | neutron | null | 400 | Mechanical Tensile | 1,100 | null | 4 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,141 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 54.5 | 600 | null | neutron | null | 600 | Mechanical Tensile | 400 | null | 12 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,142 | ornl_11 | 12Cr-1MoVW | RAFM_steel | irradiated | 54.5 | 600 | null | neutron | null | 600 | Mechanical Tensile | 450 | null | 7 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,143 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 75 | 400 | null | neutron | 725 | 400 | Mechanical Tensile | 1,100 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,144 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 75 | 400 | null | neutron | 725 | 400 | Mechanical Tensile | 1,100 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,145 | ornl_11 | 12Cr-1MoVW | RAFM_steel | irradiated | 73 | 400 | null | neutron | 165 | 400 | Mechanical Tensile | 1,100 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,148 | ornl_11 | 12Cr-1MoVW | RAFM_steel | irradiated | 73 | 400 | null | neutron | 165 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,152 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 16 | 390 | EBR-II | neutron | 1 | 390 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,153 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 54.5 | 400 | HFIR | neutron | 525 | 400 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,154 | ornl_11 | 12Cr-1MoVW-2Ni | RAFM_steel | irradiated | 54.5 | 400 | HFIR | neutron | 525 | 400 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,155 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 54.5 | 400 | HFIR | neutron | 525 | 400 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,156 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 9.5 | 400 | HFIR | neutron | null | 400 | Mechanical Tensile | 881 | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,157 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 54.5 | 400 | HFIR | neutron | 525 | 400 | Mechanical Tensile | 937 | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,158 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 16 | 390 | EBR-II | neutron | 1 | 390 | Mechanical Tensile | 687 | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,159 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 9.5 | 400 | HFIR | neutron | null | 400 | Mechanical Tensile | 1,098 | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,160 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 54.5 | 400 | HFIR | neutron | 525 | 400 | Mechanical Tensile | 1,039 | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,162 | ornl_11 | 12Cr-1MoVW | RAFM_steel | irradiated | 54.5 | 400 | HFIR | neutron | 129 | 400 | Mechanical Tensile | 1,070 | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,163 | ornl_11 | 12Cr-1MoVW-2Ni | RAFM_steel | irradiated | 9.5 | 400 | HFIR | neutron | 80 | 400 | Mechanical Tensile | 1,056 | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,164 | ornl_11 | 12Cr-1MoVW-2Ni | RAFM_steel | irradiated | 54.5 | 400 | HFIR | neutron | 525 | 400 | Mechanical Tensile | 1,062 | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,165 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 72 | 400 | HFIR | neutron | null | 400 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,167 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 72 | 600 | HFIR | neutron | 700 | 600 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,168 | ornl_11 | solution-annealed (SA) PCA austenitic stainless steel | austenitic_steel | irradiated | 13 | 330 | ORR | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,171 | ornl_11 | 25%CW PCA | RAFM_steel | irradiated | 7.4 | 60 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,173 | ornl_11 | 25%CW PCA | RAFM_steel | irradiated | 7.4 | 330 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,174 | ornl_11 | 25%CW PCA | RAFM_steel | irradiated | 7.4 | 400 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,175 | ornl_11 | 25% CW PCA | RAFM_steel | irradiated | 7.4 | 330 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 62 | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,176 | ornl_11 | 25% CW PCA | RAFM_steel | irradiated | 13 | 400 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 37 | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,178 | ornl_11 | CW PCA | RAFM_steel | irradiated | 7.4 | 60 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,179 | ornl_11 | CW PCA | RAFM_steel | irradiated | 7.4 | 200 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,180 | ornl_11 | SA 316 | RAFM_steel | irradiated | 1.1 | 55 | HFIR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,181 | ornl_11 | CW 316+Ti | RAFM_steel | irradiated | 1.1 | 55 | HFIR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,183 | ornl_11 | CW 316 | RAFM_steel | irradiated | 5 | 450 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,184 | ornl_11 | type 316 | RAFM_steel | irradiated | 55 | 350 | fission_reactor | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,186 | ornl_11 | J316/SA | austenitic_steel | irradiated | 6.9175 | 60 | ORR | neutron | 703 | 60 | Mechanical Tensile | 690 | 745 | 32.5 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,187 | ornl_11 | J316/20CW | austenitic_steel | irradiated | 6.9175 | 60 | ORR | neutron | 834 | 60 | Mechanical Tensile | 834 | 855 | 8.5 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,189 | ornl_11 | J316/SA | austenitic_steel | irradiated | 6.9175 | 200 | ORR | neutron | 745 | 200 | Mechanical Tensile | 745 | 745 | 4 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,190 | ornl_11 | J316/SA | austenitic_steel | irradiated | 6.9175 | 200 | ORR | neutron | 745 | 200 | Mechanical Tensile | 758 | 765 | 5.9 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,191 | ornl_11 | J316/20CW | austenitic_steel | irradiated | 6.9175 | 200 | ORR | neutron | 793 | 200 | Mechanical Tensile | 793 | 821 | 4.4 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,194 | ornl_11 | J316/SA | austenitic_steel | irradiated | 7.41102 | 330 | ORR | neutron | 848 | 330 | Mechanical Tensile | 848 | 855 | 3.1 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,195 | ornl_11 | J316/SA | austenitic_steel | irradiated | 7.41102 | 330 | ORR | neutron | 848 | 330 | Mechanical Tensile | 869 | 869 | 2.9 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,196 | ornl_11 | J316/20CW | austenitic_steel | irradiated | 7.41102 | 330 | ORR | neutron | 862 | 330 | Mechanical Tensile | 862 | 876 | 2.3 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,197 | ornl_11 | J316/20CW | austenitic_steel | irradiated | 7.41102 | 330 | ORR | neutron | 862 | 330 | Mechanical Tensile | 993 | 1,007 | 2 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,198 | ornl_11 | J316/SA | austenitic_steel | irradiated | 7.41102 | 400 | ORR | neutron | 595 | 400 | Mechanical Tensile | 595 | 677 | 7 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,199 | ornl_11 | J316/SA | austenitic_steel | irradiated | 7.41102 | 400 | ORR | neutron | 595 | 400 | Mechanical Tensile | 650 | 717 | 6.8 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,200 | ornl_11 | J316/20CW | austenitic_steel | irradiated | 7.41102 | 400 | ORR | neutron | 415 | 400 | Mechanical Tensile | 415 | 457 | 2.8 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,201 | ornl_11 | J316/20CW | austenitic_steel | irradiated | 7.41102 | 400 | ORR | neutron | 415 | 400 | Mechanical Tensile | 800 | 848 | 3.4 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,202 | ornl_11 | JPCA/15 CW | austenitic_steel | irradiated | 6.9186 | 60 | ORR | neutron | 876 | 60 | Mechanical Tensile | 876 | 889 | 8.1 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,203 | ornl_11 | JPCA/15 CW | austenitic_steel | irradiated | 6.9186 | 60 | ORR | neutron | 876 | 60 | Mechanical Tensile | 862 | 869 | 7.3 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,204 | ornl_11 | JPCA/25 CW | austenitic_steel | irradiated | 6.9186 | 60 | ORR | neutron | 910 | 60 | Mechanical Tensile | 910 | 924 | 4.5 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,205 | ornl_11 | JPCA/25 CW | austenitic_steel | irradiated | 6.9186 | 60 | ORR | neutron | 910 | 60 | Mechanical Tensile | 917 | 931 | 4.5 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,206 | ornl_11 | JPCAISA | austenitic_steel | irradiated | 6.9186 | 200 | ORR | neutron | 714 | 200 | Mechanical Tensile | 714 | 717 | 11.3 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,207 | ornl_11 | JPCAISA | austenitic_steel | irradiated | 6.9186 | 200 | ORR | neutron | 714 | 200 | Mechanical Tensile | 696 | 703 | 11.1 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,209 | ornl_11 | JPCA/15 CW | austenitic_steel | irradiated | 6.9 | 200 | ORR | neutron | 807 | 200 | Mechanical Tensile | 807 | 814 | 3.4 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,210 | ornl_11 | JPCAISA | austenitic_steel | irradiated | 7.4 | 330 | ORR | neutron | 821 | 330 | Mechanical Tensile | 821 | 821 | 2.5 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,212 | ornl_11 | JPCA/15 CW | austenitic_steel | irradiated | 7.41118 | 330 | ORR | neutron | 876 | 330 | Mechanical Tensile | 876 | 889 | 2.3 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,213 | ornl_11 | JPCA/15 CW | austenitic_steel | irradiated | 7.41118 | 330 | ORR | neutron | 876 | 330 | Mechanical Tensile | 938 | 945 | 2.2 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,214 | ornl_11 | JPCA/15CW Rod | austenitic_steel | irradiated | 7.41118 | 330 | ORR | neutron | 931 | 330 | Mechanical Tensile | 931 | 945 | 5.3 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,215 | ornl_11 | JPCA/15CW Rod | austenitic_steel | irradiated | 7.41118 | 330 | ORR | neutron | 931 | 330 | Mechanical Tensile | 958 | 958 | 5.4 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,216 | ornl_11 | JPCAISA | austenitic_steel | irradiated | 7.41118 | 400 | ORR | neutron | 505 | 400 | Mechanical Tensile | 505 | 652 | 12.9 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,217 | ornl_11 | JPCAISA | austenitic_steel | irradiated | 7.41118 | 400 | ORR | neutron | 505 | 400 | Mechanical Tensile | 549 | 667 | 10.5 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,218 | ornl_11 | JPCA/15CW | austenitic_steel | irradiated | 7.41118 | 600 | ORR | neutron | 855 | 600 | Mechanical Tensile | 855 | 896 | 2.9 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,219 | ornl_11 | JPCA/15CW | austenitic_steel | irradiated | 7.41118 | 400 | ORR | neutron | 827 | 400 | Mechanical Tensile | 827 | 841 | 1.9 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,220 | ornl_11 | JPCA/SA | austenitic_steel | irradiated | 27 | 300 | HFIR | neutron | 770 | 300 | Mechanical Tensile | 770 | 789 | 9.93 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,222 | ornl_11 | JPCA/15 CW | austenitic_steel | irradiated | 27 | 300 | HFIR | neutron | 775 | 300 | Mechanical Tensile | 747 | 780 | 7.27 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,223 | ornl_11 | JPCAISA | austenitic_steel | irradiated | 22 | 400 | HFIR | neutron | 878 | 400 | Mechanical Tensile | 878 | 888 | 6.4 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.