record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
3,224 | ornl_11 | JPCAISA | austenitic_steel | irradiated | 22 | 400 | HFIR | neutron | 878 | 400 | Mechanical Tensile | 896 | 910 | 6 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,225 | ornl_11 | JPCAICW | austenitic_steel | irradiated | 22 | 400 | HFIR | neutron | 952 | 400 | Mechanical Tensile | 952 | 972 | 5.5 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,226 | ornl_11 | JPCAICW | austenitic_steel | irradiated | 22 | 400 | HFIR | neutron | 952 | 400 | Mechanical Tensile | 859 | 974 | 6.3 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,227 | ornl_11 | JPCAISA | austenitic_steel | irradiated | 27 | 500 | HFIR | neutron | 650 | 500 | Mechanical Tensile | 650 | 732 | 8.2 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,228 | ornl_11 | JPCAISA | austenitic_steel | irradiated | 27 | 500 | HFIR | neutron | 650 | 500 | Mechanical Tensile | 631 | 724 | 11.7 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,231 | ornl_11 | type 316 stainless steel (cold-worked) | austenitic_steel | irradiated | null | 500 | HFIR | neutron | null | 200 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,232 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 9.5 | 400 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.8 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,233 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 11.3 | 480 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,234 | ornl_11 | 9Cr steel | RAFM_steel | irradiated | 11.3 | 510 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,237 | ornl_11 | Fe-15Cr-25Ni | austenitic_steel | irradiated | null | 330 | MFE-4 | neutron | null | null | Mechanical Tensile | 700 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,238 | ornl_11 | Fe-15Cr-25Ni | austenitic_steel | irradiated | null | 400 | MFE-4 | neutron | null | null | Mechanical Tensile | 680 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,240 | ornl_11 | Fe-15Cr-25Ni | austenitic_steel | irradiated | null | 600 | MFE-4 | neutron | null | null | Mechanical Tensile | 150 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,243 | ornl_11 | Fe-15Cr-xNi | austenitic_steel | irradiated | 12.5 | 500 | ORR | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,244 | ornl_11 | Fe-15Cr-25Ni | austenitic_steel | irradiated | null | 400 | MFE-4 | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 1.9 | 150,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,245 | ornl_11 | Fe-15Cr-35Ni | austenitic_steel | irradiated | null | 400 | MFE-4 | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 2.3 | 250,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,246 | ornl_11 | Fe-15Cr-45Ni | austenitic_steel | irradiated | null | 400 | MFE-4 | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 2.9 | 350,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,248 | ornl_11 | Fe-15Cr-35Ni | austenitic_steel | irradiated | null | 500 | MFE-4 | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 5.5 | 60,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,249 | ornl_11 | Fe-15Cr-45Ni | austenitic_steel | irradiated | null | 500 | MFE-4 | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 1.9 | 100,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,250 | ornl_11 | Fe-15Cr-25Ni | austenitic_steel | irradiated | null | 395 | AD-1 | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 35 | 1,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,251 | ornl_11 | Fe-15Cr-35Ni | austenitic_steel | irradiated | null | 395 | AD-1 | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 23 | 300,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,252 | ornl_11 | Fe-15Cr-45Ni | austenitic_steel | irradiated | null | 395 | AD-1 | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 25 | 100,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,253 | ornl_11 | Fe-Cr | ferritic_model_alloy | irradiated | 0.01 | 150 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,257 | ornl_11 | Fe-14.8Cr-13.8Ni-2.5Mo-2.0Mn-1.55Si-0.2Ti-0.04C | ferritic_model_alloy | irradiated | 10 | 540 | MV-III | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 10.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,258 | ornl_11 | Fe-14.8Cr-13.8Ni-2.5Mo-2.0Mn-1.55Si-0.2Ti-0.04C | ferritic_model_alloy | irradiated | 6.3 | 540 | MV-III | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,259 | ornl_11 | Fe-10.5Cr-13.8Ni-2.4Mo-2.0Mn-0.7Si-0.2Ti-0.04C | ferritic_model_alloy | irradiated | 14.9 | 540 | MV-III | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 6.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,260 | ornl_11 | Fe-16.3Cr-13.7Ni-2.4Mo-2.0Mn-0.8Si-0.2Ti-0.04C | ferritic_model_alloy | irradiated | 6.3 | 540 | MV-III | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,261 | ornl_11 | Fe-16.2Cr-13.8Ni-2.5Mo-2.0Mn-1.5Si-0.2Ti-0.4C | ferritic_model_alloy | irradiated | 10 | 540 | MV-III | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 15.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,262 | ornl_11 | Fe-16.2Cr-13.7Ni-2.5Mo-2.0Mn-0.7Si-0.1Ti-0.04C | ferritic_model_alloy | irradiated | 10 | 540 | MV-III | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 13 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,263 | ornl_11 | Fe-16.2Cr-13.7Ni-2.5Mo-2.0Mn-0.7Si-0.1Ti-0.04C | ferritic_model_alloy | irradiated | 17 | 600 | MV-III | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 10.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,265 | ornl_11 | 20% cold worked M316 | austenitic_steel | irradiated | 70 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 10 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,266 | ornl_11 | 20% cold worked M316 | austenitic_steel | irradiated | 70 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 11 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,267 | ornl_11 | 20% cold worked M316 | austenitic_steel | irradiated | 70 | 400 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,268 | ornl_11 | 20% cold worked M316 (V1257) | austenitic_steel | irradiated | 67 | 400 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,269 | ornl_11 | 20% cold worked M316 (V1257) | austenitic_steel | irradiated | 67 | 400 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 60 | 2,000,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,271 | ornl_11 | 20% cold worked M316 (V1254/V1256) | austenitic_steel | irradiated | 38 | 400 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 50 | 20,000,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,272 | ornl_11 | 20% cold worked AISI 316 stainless steel | austenitic_steel | irradiated | null | 400 | RS-1 experiment | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.2 | null | 123,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,273 | ornl_11 | 20% cold worked AISI 316 stainless steel | austenitic_steel | irradiated | null | 433 | RS-1 experiment | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.3 | null | 123,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,274 | ornl_11 | 20% cold worked AISI 316 stainless steel | austenitic_steel | irradiated | null | 467 | RS-1 experiment | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 9.5 | null | 123,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,275 | ornl_11 | 20% cold worked AISI 316 stainless steel | austenitic_steel | irradiated | null | 533 | RS-1 experiment | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 14 | null | 123,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,276 | ornl_11 | AISI 316 stainless steel (Core 1) | austenitic_steel | irradiated | null | 540 | MV-III | neutron | null | 540 | Swelling | null | null | null | null | null | null | null | null | null | 14 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,277 | ornl_11 | AISI 316 stainless steel (Core 4) | austenitic_steel | irradiated | null | 540 | MV-III | neutron | null | 540 | Swelling | null | null | null | null | null | null | null | null | null | 18 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,278 | ornl_11 | AISI 316 stainless steel (Core 1) | austenitic_steel | irradiated | null | 540 | MV-III | neutron | null | 540 | Swelling | null | null | null | null | null | null | null | null | null | 6 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,279 | ornl_11 | AISI 316 stainless steel (Core 4) | austenitic_steel | irradiated | null | 540 | MV-III | neutron | null | 540 | Swelling | null | null | null | null | null | null | null | null | null | 11 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,281 | ornl_11 | AISI 316 stainless steel (Core 4) | austenitic_steel | irradiated | null | 540 | MV-III | neutron | null | 540 | Swelling | null | null | null | null | null | null | null | null | null | 2 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,282 | ornl_11 | AISI 316 stainless steel (Core 1, 20% Cold Work) | austenitic_steel | irradiated | 15 | 540 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 16 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,283 | ornl_11 | AISI 316 stainless steel (Core 1, 1150C Anneal) | austenitic_steel | irradiated | 15 | 540 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 14 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,284 | ornl_11 | AISI 316 stainless steel (Core 1, 1150C Anneal + 650C Age) | austenitic_steel | irradiated | 15 | 540 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,285 | ornl_11 | AISI 316 stainless steel (Core 1, 1300C Anneal) | austenitic_steel | irradiated | 15 | 540 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 6 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,287 | ornl_11 | AISI 316 stainless steel (Core 4, 1150C Anneal) | austenitic_steel | irradiated | 15 | 540 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 14 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,289 | ornl_11 | AISI 316 stainless steel (Core 4, 1300C Anneal) | austenitic_steel | irradiated | 15 | 540 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,290 | ornl_11 | D9 | RAFM_steel | irradiated | null | 575 | FFTF | neutron | null | 575 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,291 | ornl_11 | D9 | RAFM_steel | irradiated | null | 605 | FFTF | neutron | null | 605 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,292 | ornl_11 | D9 | RAFM_steel | irradiated | null | 670 | FFTF | neutron | null | 670 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,293 | ornl_11 | D9 | RAFM_steel | irradiated | null | 750 | FFTF | neutron | null | 750 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,294 | ornl_11 | cold worked material | other | irradiated | null | 400 | null | neutron | null | 400 | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,295 | ornl_11 | Cold worked tube | other | irradiated | 60 | 495 | null | neutron | null | 495 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,297 | ornl_11 | Cold worked tube | other | irradiated | 60 | 495 | null | neutron | null | 495 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,298 | ornl_11 | Cold worked tube | other | irradiated | 75 | 550 | null | neutron | null | 550 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,300 | ornl_11 | Cold worked tube | other | irradiated | 45 | 600 | null | neutron | null | 600 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,301 | ornl_11 | Cold worked tube | other | irradiated | 75 | 600 | null | neutron | null | 600 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,302 | ornl_11 | Cold worked tube | other | irradiated | 50 | 600 | null | neutron | null | 600 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,303 | ornl_11 | Cold Worked Tube | other | irradiated | 20 | 667 | null | neutron | null | 667 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,304 | ornl_11 | 10% Cold Work Tube | other | irradiated | 60 | 495 | null | null | null | 495 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,305 | ornl_11 | 20% Cold Work Tube | other | irradiated | 60 | 495 | null | null | null | 495 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,306 | ornl_11 | 30% Cold Work Tube | other | irradiated | 40 | 495 | null | null | null | 495 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,307 | ornl_11 | Cold Worked Tube (15.4 MPa) | other | irradiated | 60 | 667 | null | null | null | 667 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,308 | ornl_11 | Cold Worked Tube (5.2 MPa) | other | irradiated | 60 | 667 | null | null | null | 667 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,309 | ornl_11 | AISI 316 stainless steel | austenitic_steel | irradiated | 80 | 550 | null | neutron | null | 550 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,310 | ornl_11 | AISI 316 stainless steel (10% Cold Work) | austenitic_steel | irradiated | 60 | 550 | null | null | null | 550 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,313 | ornl_11 | Pressurized tubes (10% Cold Work) | other | irradiated | 20 | 667 | null | neutron | null | 667 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,314 | ornl_11 | Pressurized tubes (10% Cold Work) | other | irradiated | 40 | 667 | null | neutron | null | 667 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,315 | ornl_11 | Pressurized tubes (20% Cold Work) | other | irradiated | 60 | 667 | null | neutron | null | 667 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,316 | ornl_11 | Pressurized tubes (30% Cold Work) | other | irradiated | 40 | 667 | null | neutron | null | 667 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,317 | ornl_11 | Cold worked material | other | unirradiated | null | null | null | null | null | 650 | Mechanical Hardness | null | null | null | 265 | null | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
3,319 | ornl_11 | Cold worked material (30% CW) | other | unirradiated | null | null | null | null | null | 760 | Mechanical Hardness | null | null | null | 260 | null | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
3,320 | ornl_11 | Cold worked material (20% CW) | other | unirradiated | null | null | null | null | null | 650 | Mechanical Hardness | null | null | null | 245 | null | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
3,323 | ornl_11 | K280 | other | irradiated | null | 400 | FFTF | neutron | null | 400 | Mechanical Creer | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,324 | ornl_11 | 83508' | other | irradiated | null | 400 | FFTF | neutron | null | 400 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,325 | ornl_11 | A094* | other | irradiated | null | 400 | FFTF | neutron | null | 400 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,326 | ornl_11 | A095* | other | irradiated | null | 400 | FFTF | neutron | null | 400 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,327 | ornl_11 | C38 | other | irradiated | null | 400 | FFTF | neutron | null | 400 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,329 | ornl_11 | C40 | other | irradiated | null | 400 | FFTF | neutron | null | 400 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,331 | ornl_11 | C44 | other | irradiated | null | 400 | FFTF | neutron | null | 400 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,332 | ornl_11 | K280 (PCA) | austenitic_steel | irradiated | 20.4 | 405 | MOTA-1A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,334 | ornl_11 | K280 (PCA) | austenitic_steel | irradiated | 50.2 | 396 | MOTA-1C | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,335 | ornl_11 | K280 (PCA) | austenitic_steel | irradiated | 65.3 | 386 | MOTA-1D | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,336 | ornl_11 | K280 (PCA) | austenitic_steel | irradiated | 81.1 | 384 | MOTA-1E | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,337 | ornl_11 | K280 (PCA) | austenitic_steel | irradiated | 106.8 | 386 | MOTA-1F | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,340 | ornl_11 | 83508 (D9 Reference) | other | irradiated | 77.2 | 420 | MOTA-1C | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,341 | ornl_11 | 83508 (D9 Reference) | other | irradiated | 101.2 | 404 | MOTA-1D | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,342 | ornl_11 | A094 (D9I-2) | other | irradiated | 14.1 | 431 | MOTA-1B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,344 | ornl_11 | A094 (D9I-2) | other | irradiated | 72.2 | 410 | MOTA-1D | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,345 | ornl_11 | A094 (D9I-2) | other | irradiated | 109.2 | 410 | MOTA-1E | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,346 | ornl_11 | A094 (D9I-2) | other | irradiated | 141.2 | 410 | MOTA-1F | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,347 | ornl_11 | A095 (D9I-1) | other | irradiated | 14.5 | 431 | MOTA-1B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,348 | ornl_11 | A095 (D9I-1) | other | irradiated | 48.4 | 420 | MOTA-1C | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,349 | ornl_11 | A095 (D9I-1) | other | irradiated | 73.9 | 410 | MOTA-1D | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,350 | ornl_11 | A095 (D9I-1) | other | irradiated | 108.1 | 410 | MOTA-1E | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,351 | ornl_11 | A095 (D9I-1) | other | irradiated | 140.1 | 410 | MOTA-1F | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,352 | ornl_11 | C38 (D9 B/P-1) | other | irradiated | 11.5 | 401 | MOTA-1B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.