record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
3,353 | ornl_11 | C38 (D9 B/P-1) | other | irradiated | 32.4 | 396 | MOTA-1C | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,355 | ornl_11 | C38 (D9 B/P-1) | other | irradiated | 76.5 | 384 | MOTA-1E | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,356 | ornl_11 | C38 (D9 B/P-1) | other | irradiated | 89.8 | 386 | MOTA-1F | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,358 | ornl_11 | C39 (D9 B/P-2) | other | irradiated | 35.5 | 396 | MOTA-1C | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,359 | ornl_11 | C39 (D9 B/P-2) | other | irradiated | 55.4 | 386 | MOTA-1D | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,360 | ornl_11 | C39 (D9 B/P-2) | other | irradiated | 79.6 | 384 | MOTA-1E | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,361 | ornl_11 | C39 (D9 B/P-2) | other | irradiated | 92.9 | 386 | MOTA-1F | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,362 | ornl_11 | C40 (D9 B/P-3) | other | irradiated | 10.6 | 401 | MOTA-1B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,363 | ornl_11 | C40 (D9 B/P-3) | other | irradiated | 35.5 | 396 | MOTA-1C | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,364 | ornl_11 | C40 (D9 B/P-3) | other | irradiated | 54.1 | 386 | MOTA-1D | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,365 | ornl_11 | C40 (D9 B/P-3) | other | irradiated | 75.7 | 384 | MOTA-1E | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,366 | ornl_11 | C40 (D9 B/P-3) | other | irradiated | 89 | 386 | MOTA-1F | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,367 | ornl_11 | C42 (D9 B/P-4) | other | irradiated | 14.1 | 431 | MOTA-1B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,368 | ornl_11 | C42 (D9 B/P-4) | other | irradiated | 47.2 | 420 | MOTA-1C | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,370 | ornl_11 | C42 (D9 B/P-4) | other | irradiated | 104.7 | 414 | MOTA-1E | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,371 | ornl_11 | C42 (D9 B/P-4) | other | irradiated | 138.5 | 405 | MOTA-1F | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,372 | ornl_11 | C44 (D9 B/P-5) | other | irradiated | 10.6 | 401 | MOTA-1B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,373 | ornl_11 | C44 (D9 B/P-5) | other | irradiated | 35.5 | 396 | MOTA-1C | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,375 | ornl_11 | C44 (D9 B/P-5) | other | irradiated | 79.6 | 384 | MOTA-1E | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,377 | ornl_11 | PCA alloy | RAFM_steel | irradiated | null | 400 | null | neutron | null | 400 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,379 | ornl_11 | AISI 316 | RAFM_steel | irradiated | null | 400 | null | neutron | null | 400 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,382 | ornl_11 | austenitic stainless steels | austenitic_steel | irradiated | null | 400 | EBR-II or FFTF | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,383 | ornl_11 | V-base alloys containing >5 wt.% Ti | vanadium_alloy | irradiated | null | 420 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,385 | ornl_11 | V-15Cr-1Ti | vanadium_alloy | irradiated | 114 | 420 | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,386 | ornl_11 | V-3Ti-1Si | vanadium_alloy | irradiated | 114 | 420 | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,387 | ornl_11 | V-13.5Cr-5Ti | vanadium_alloy | irradiated | null | 600 | FFTF/MOTA | neutron | null | 400 | Mechanical Tensile | null | null | null | null | null | 673.15 | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,388 | ornl_11 | V-3.1Ti-0.3Si (BL-27) | vanadium_alloy | irradiated | 114 | 420 | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,391 | ornl_11 | Ti(O,N,C) in BL-16 | other | irradiated | 114 | 420 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,392 | ornl_11 | V-Ti | vanadium_alloy | irradiated | null | 600 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | 200 | null |
3,393 | ornl_11 | V-15Cr-5Ti | vanadium_alloy | irradiated | null | 600 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | 200 | null |
3,394 | ornl_11 | V-17.7Ti (BL-15) | vanadium_alloy | irradiated | 84 | 600 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,396 | ornl_11 | V-3Ti-0.3Si (BL-27) | vanadium_alloy | irradiated | 114 | 420 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,397 | ornl_11 | V (BL-20) | vanadium_alloy | irradiated | 114 | 420 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,398 | ornl_11 | V-13.5Cr-5Ti | vanadium_alloy | irradiated | null | 420 | null | neutron | null | 420 | Mechanical Tensile | null | null | 5 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,400 | ornl_11 | Ti2O precipitates | other | irradiated | null | 420 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | 200 | null |
3,401 | ornl_11 | Ti5(Si,P)3 precipitates | other | irradiated | null | 420 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 15 | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,402 | ornl_11 | V-15Cr-5Ti | vanadium_alloy | irradiated | null | null | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 523.15 | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
3,403 | ornl_11 | V-5 at% Fe | vanadium_alloy | irradiated | null | 600 | FFTF or JOYO | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,404 | ornl_11 | V-Cr binaries (9-14 wt% Cr) | vanadium_alloy | irradiated | 77 | 600 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 63.6 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,405 | ornl_11 | V-Cr binaries (9-14 wt% Cr) | vanadium_alloy | irradiated | 77 | 600 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 73.6 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,406 | ornl_11 | V-5Cr, V-2Si, V-1Zr | vanadium_alloy | irradiated | 42 | 427 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,407 | ornl_11 | V-5Cr, V-2Si, V-1Zr | vanadium_alloy | irradiated | 42 | 433 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,408 | ornl_11 | V-5Cr, V-2Si, V-1Zr | vanadium_alloy | irradiated | 42 | 519 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,409 | ornl_11 | V-5Cr, V-2Si, V-1Zr | vanadium_alloy | irradiated | 42 | 600 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,412 | ornl_11 | V-Cr alloys | vanadium_alloy | irradiated | 45.3 | 519 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,414 | ornl_11 | V alloy | vanadium_alloy | irradiated | 77 | 600 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,415 | ornl_11 | V-9.5Cr | vanadium_alloy | irradiated | 77 | 600 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 75 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,416 | ornl_11 | V-10.0Cr | vanadium_alloy | irradiated | 77 | 600 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 70 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,418 | ornl_11 | V-Cr alloys | vanadium_alloy | irradiated | 77 | null | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 140 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,419 | ornl_11 | GlidCop | copper_alloy | irradiated | 34 | 415 | FFTF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,420 | ornl_11 | GlidCop | copper_alloy | irradiated | 50 | 415 | FFTF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,421 | ornl_11 | GlidCop | copper_alloy | irradiated | 104 | 415 | FFTF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,422 | ornl_11 | GlidCop | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,423 | ornl_11 | Cu-Cr2O3 | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,424 | ornl_11 | Cu-HfO2 | copper_alloy | irradiated | 50 | 415 | FFTF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,425 | ornl_11 | CuAl25 | copper_alloy | irradiated | 104 | null | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,426 | ornl_11 | CuAl25 | copper_alloy | irradiated | 150 | null | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 43 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,427 | ornl_11 | CuAl15 | copper_alloy | irradiated | 34.1 | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,428 | ornl_11 | ODS steel | ODS_steel | irradiated | 50 | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,430 | ornl_11 | CuAl20 20% CW | copper_alloy | irradiated | 0 | null | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,431 | ornl_11 | CuAl20 20% CW | copper_alloy | irradiated | 50 | null | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,432 | ornl_11 | CuAl20 20% CW | copper_alloy | irradiated | 100 | null | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,433 | ornl_11 | CuAl20 20% CW | copper_alloy | irradiated | 150 | null | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,434 | ornl_11 | CuAl25 50% CW | copper_alloy | irradiated | 50 | null | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,435 | ornl_11 | CuAl25 50% CW | copper_alloy | irradiated | 100 | null | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,437 | ornl_11 | Cu-HfO2 | copper_alloy | irradiated | 50 | null | null | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | 1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,438 | ornl_11 | Cu-Cr2O3 | copper_alloy | irradiated | 100 | null | null | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | 15 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,439 | ornl_11 | ODS steel | ODS_steel | irradiated | 150 | null | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 100 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,440 | ornl_11 | ODS steel | ODS_steel | irradiated | 150 | null | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 115 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,442 | ornl_11 | ODS steel | ODS_steel | irradiated | 150 | null | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 95 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,443 | ornl_11 | ODS steel | ODS_steel | irradiated | 150 | null | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 50 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,444 | ornl_11 | CuAl25 50% CW | copper_alloy | irradiated | 0 | null | null | neutron | null | null | Mechanical Tensile | 480 | 540 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,445 | ornl_11 | CuAl25 50% CW | copper_alloy | irradiated | 50 | null | null | neutron | null | null | Mechanical Tensile | 440 | 480 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,446 | ornl_11 | CuAl25 50% CW | copper_alloy | irradiated | 150 | null | null | neutron | null | null | Mechanical Tensile | 430 | 460 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,447 | ornl_11 | CuAl20 20% CW | copper_alloy | irradiated | 0 | null | null | neutron | null | null | Mechanical Tensile | 410 | 460 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,448 | ornl_11 | CuAl20 20% CW | copper_alloy | irradiated | 50 | null | null | neutron | null | null | Mechanical Tensile | 380 | 410 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,449 | ornl_11 | CuAl20 20% CW | copper_alloy | irradiated | 150 | null | null | neutron | null | null | Mechanical Tensile | 370 | 400 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,450 | ornl_11 | Cu - HfO2 | copper_alloy | irradiated | 0 | null | null | neutron | null | null | Mechanical Tensile | 350 | 400 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,451 | ornl_11 | Cu - Cr2O3 | copper_alloy | irradiated | 0 | null | null | neutron | null | null | Mechanical Tensile | 280 | 340 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,452 | ornl_11 | CuAl15 + B | copper_alloy | irradiated | 0 | null | null | neutron | null | null | Mechanical Tensile | 260 | 320 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,453 | ornl_11 | CuAl25 Weld | copper_alloy | irradiated | 0 | null | null | neutron | null | null | Mechanical Tensile | 180 | 240 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,454 | ornl_11 | ODS steel | ODS_steel | irradiated | 0 | null | null | neutron | null | null | Mechanical Tensile | 320 | 360 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,455 | ornl_11 | ODS steel | ODS_steel | irradiated | 50 | null | null | neutron | null | null | Mechanical Tensile | 160 | 180 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,456 | ornl_11 | ODS steel | ODS_steel | irradiated | 0 | null | null | neutron | null | null | Mechanical Tensile | 300 | 340 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,457 | ornl_11 | ODS steel | ODS_steel | irradiated | 0 | null | null | neutron | null | null | Mechanical Tensile | 180 | 240 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,458 | ornl_11 | Cu-HfO2 | copper_alloy | irradiated | 150 | 415 | null | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,459 | ornl_11 | Cu-HfO2 | copper_alloy | irradiated | 150 | null | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,460 | ornl_11 | Cu-Cr2O3 | copper_alloy | irradiated | 50 | null | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,461 | ornl_11 | GlidCop | copper_alloy | irradiated | 150 | 415 | null | neutron | null | 400 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,462 | ornl_11 | SUS316L | austenitic_steel | irradiated | null | 400 | null | neutron | null | 300 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,463 | ornl_11 | SUS316L | austenitic_steel | irradiated | null | 330 | null | neutron | null | 300 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,464 | ornl_11 | SUS316L | austenitic_steel | irradiated | null | 200 | null | neutron | null | 200 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,465 | ornl_11 | SUS316L | austenitic_steel | irradiated | null | 60 | null | neutron | null | 60 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,468 | ornl_11 | MFE-6J/7J | other | irradiated | 7.4 | 330 | null | neutron | null | 330 | Mechanical Tensile | null | 880 | 5 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,469 | ornl_11 | MFE-6J/7J | other | irradiated | 7.4 | 400 | null | neutron | null | 400 | Mechanical Tensile | null | 910 | 8 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,472 | ornl_11 | J316 | austenitic_steel | irradiated | null | 330 | MFE-6J/7J | neutron | null | 300 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,474 | ornl_11 | USPCA | austenitic_steel | irradiated | null | 60 | MFE-6J/7J | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,476 | ornl_11 | austenitic stainless steels | austenitic_steel | irradiated | null | 60 | fusion spectrally-tailored conditions | neutron | null | 60 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,480 | ornl_11 | MFE-6J/7J | other | irradiated | null | 400 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,481 | ornl_11 | arc cast beryllium | beryllium | irradiated | 8 | 400 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 5.75 | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.