record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
3,604 | ornl_12 | 316 SS | RAFM_steel | irradiated | 31.5 | 450 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.11 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,605 | ornl_12 | 316 SS | RAFM_steel | irradiated | 30 | 525 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.09 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,606 | ornl_12 | 316 SS | RAFM_steel | irradiated | 10 | 525 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.14 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,607 | ornl_12 | 316 SS | RAFM_steel | irradiated | 3 | 525 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,608 | ornl_12 | 316 SS | RAFM_steel | irradiated | 9.5 | 525 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,610 | ornl_12 | 316 SS | RAFM_steel | irradiated | 31.5 | 525 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,611 | ornl_12 | 316 SS | RAFM_steel | irradiated | 31.5 | 525 | null | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,612 | ornl_12 | 20% CW 316 SS | austenitic_steel | irradiated | null | 452 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 6.4 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,613 | ornl_12 | 20% CW 316 SS | austenitic_steel | irradiated | null | 452 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.7 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,614 | ornl_12 | 20% CW 316 SS | austenitic_steel | irradiated | 84 | 457 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,615 | ornl_12 | Beryllium | beryllium | irradiated | 84 | 457 | null | neutron | 6,405 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,616 | ornl_12 | 20% CW 316 SS | austenitic_steel | irradiated | null | 452 | null | neutron | null | null | Mechanical Fatigue | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,617 | ornl_12 | pure Cu | copper_alloy | irradiated | 0.04 | 45.5 | LASREF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,618 | ornl_12 | alumina-dispersion-strengthened Cu (CuAl25) | copper_alloy | irradiated | 0.04 | 45.5 | LASREF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,619 | ornl_12 | AISI 316 stainless steel | austenitic_steel | irradiated | 0.04 | 45.5 | LASREF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,620 | ornl_12 | pure Cu | copper_alloy | irradiated | null | 90 | RTNS-II | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,621 | ornl_12 | 316 SS | RAFM_steel | irradiated | 0.0001 | null | RTNS-II | neutron | null | null | Mechanical Tensile | 50 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | 2.5 | null | null |
3,622 | ornl_12 | 316 SS | RAFM_steel | irradiated | 0.0256 | null | OWR | neutron | null | null | Mechanical Tensile | 250 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | 12.5 | null | null |
3,623 | ornl_12 | pure Cu | copper_alloy | irradiated | null | null | LASREF | proton | null | null | Mechanical Tensile | 200 | null | null | null | null | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | 10 | null | null |
3,624 | ornl_12 | pure Cu | copper_alloy | irradiated | null | 290 | RTNS-II | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,625 | ornl_12 | pure Cu | copper_alloy | irradiated | null | 36 | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,626 | ornl_12 | alumina-dispersion-strengthened Cu | copper_alloy | irradiated | 0.0001 | null | RTNS-II | neutron | null | null | Mechanical Tensile | 35 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,627 | ornl_12 | alumina-dispersion-strengthened Cu | copper_alloy | irradiated | 0.0016 | null | RTNS-II | neutron | null | null | Mechanical Tensile | 50 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,628 | ornl_12 | alumina-dispersion-strengthened Cu | copper_alloy | irradiated | 0.005 | null | RTNS-II | neutron | null | null | Mechanical Tensile | 65 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,629 | ornl_12 | Pure Cu | copper_alloy | irradiated | 0.0001 | null | RTNS-II | neutron | null | null | Mechanical Tensile | 65 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,630 | ornl_12 | Pure Cu | copper_alloy | irradiated | 0.0016 | null | RTNS-II | neutron | null | null | Mechanical Tensile | 125 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,631 | ornl_12 | Pure Cu | copper_alloy | irradiated | 0.0081 | null | RTNS-II | neutron | null | null | Mechanical Tensile | 185 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,632 | ornl_12 | 316 SS | RAFM_steel | irradiated | null | 200 | LASREF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,633 | ornl_12 | Cu | copper_alloy | irradiated | null | 200 | LASREF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,634 | ornl_12 | Cu | copper_alloy | irradiated | null | 200 | RTNS-II | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,635 | ornl_12 | USPCA (titanium-modified stainless steel) | austenitic_steel | irradiated | 15 | 520 | Fast Flux Test Facility (FFTF) | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,637 | ornl_12 | irradiated stainless steels | other | irradiated | null | 300 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,639 | ornl_12 | CW/ Fe-15Cr-25Ni | austenitic_steel | irradiated | 10.3 | 365 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,640 | ornl_12 | CW/He Fe-15Cr-25Ni | austenitic_steel | irradiated | 10.3 | 365 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.2 | 8 | 4,500,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,642 | ornl_12 | SA/He Fe-15Cr-25Ni | austenitic_steel | irradiated | 10.3 | 365 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.161 | 6.9 | 3,280,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,643 | ornl_12 | CW/-/P Fe-15Cr-25Ni | austenitic_steel | irradiated | 10.3 | 365 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.303 | 10.2 | 3,830,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,645 | ornl_12 | SA/-/P Fe-15Cr-25Ni | austenitic_steel | irradiated | 10.3 | 365 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.116 | 8.3 | 2,640,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,646 | ornl_12 | SA/He/P Fe-15Cr-25Ni | austenitic_steel | irradiated | 10.3 | 365 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.302 | 6.9 | 12,400,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,647 | ornl_12 | CW/-/Ni Fe-15Cr-25Ni | austenitic_steel | irradiated | 10.3 | 365 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.043 | 10 | 570,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,648 | ornl_12 | CW/He/Ni Fe-15Cr-25Ni | austenitic_steel | irradiated | 10.3 | 365 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.04 | 7 | 3,800,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,649 | ornl_12 | SA/-/Ni Fe-15Cr-25Ni | austenitic_steel | irradiated | 10.3 | 365 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.456 | 13.6 | 1,400,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,650 | ornl_12 | SA/He/Ni Fe-15Cr-25Ni | austenitic_steel | irradiated | 10.3 | 365 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0.225 | 8.6 | 3,600,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,651 | ornl_12 | Fe-15Cr-25Ni-0.001P | austenitic_steel | irradiated | 10.3 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.25 | 10 | 4,500,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,652 | ornl_12 | Fe-15Cr-25Ni-0.001P (CW) | austenitic_steel | irradiated | 10.3 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.22 | 9 | 3,500,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,653 | ornl_12 | Fe-15Cr-25Ni-0.001P (SA) | austenitic_steel | irradiated | 10.3 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.28 | 16 | 2,500,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,655 | ornl_12 | Fe-15Cr-25Ni-0.04P (SA) | austenitic_steel | irradiated | 10.3 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.18 | 10 | 4,500,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,656 | ornl_12 | Fe-15Cr-45Ni (CW) | austenitic_steel | irradiated | 10.3 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.05 | 10 | 500,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,657 | ornl_12 | Fe-15Cr-45Ni (SA) | austenitic_steel | irradiated | 10.3 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.48 | 16 | 3,500,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,659 | ornl_12 | Fe-15Cr-25Ni SA | austenitic_steel | irradiated | 10.3 | 365 | null | neutron | null | null | Mechanical Tensile | 780 | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,660 | ornl_12 | Fe-15Cr-25Ni + 0.04P CW | austenitic_steel | irradiated | 10.3 | 365 | null | neutron | null | null | Mechanical Tensile | 850 | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,661 | ornl_12 | Fe-15Cr-45Ni CW | austenitic_steel | irradiated | 10.3 | 365 | null | neutron | null | null | Mechanical Tensile | 720 | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,663 | ornl_12 | Fe-12Cr | ferritic_model_alloy | irradiated | 20 | 370 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 15 | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,664 | ornl_12 | Fe-12Cr | ferritic_model_alloy | irradiated | 40 | 406 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,665 | ornl_12 | Fe-12Cr | ferritic_model_alloy | irradiated | null | 520 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,666 | ornl_12 | Fe-12Cr | ferritic_model_alloy | irradiated | null | 520 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,667 | ornl_12 | Fe-(10-15)Cr-(15-30)Mn steels | other | irradiated | null | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,668 | ornl_12 | 99.995% Nickel (Annealed at 975°C for 10 minutes) | nickel_alloy | irradiated | 13 | 425 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 6.1 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,669 | ornl_12 | 99.995% Nickel (Annealed at 975°C for 10 minutes) | nickel_alloy | irradiated | 13 | 500 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.3 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,670 | ornl_12 | 99.995% Nickel (Annealed at 975°C for 10 minutes) | nickel_alloy | irradiated | 13 | 600 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.4 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,671 | ornl_12 | 99.995% Nickel (30% Cold-Worked) | nickel_alloy | irradiated | 13 | 425 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 6.3 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,673 | ornl_12 | 99.995% Nickel (30% Cold-Worked) | nickel_alloy | irradiated | 13 | 600 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.7 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,675 | ornl_12 | 99.995% Nickel (30% cold-worked and aged 650°C for 10 hours) | nickel_alloy | irradiated | 13 | 500 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 6 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,676 | ornl_12 | 99.995% Nickel (30% cold-worked and aged 650°C for 10 hours) | nickel_alloy | irradiated | 13 | 600 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.4 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,677 | ornl_12 | Ni-5Si | other | irradiated | 13 | 425 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,678 | ornl_12 | Ni-8Si | other | irradiated | 13 | 425 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,679 | ornl_12 | Ni-5Al | other | irradiated | 13 | 425 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,680 | ornl_12 | Ni-Si alloy (Annealed) | other | irradiated | 14 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 6.2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,682 | ornl_12 | Ni-Si alloy (Cold Worked and Aged) | other | irradiated | 14 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,683 | ornl_12 | Ni-2Si alloy (Annealed) | other | irradiated | 14 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,684 | ornl_12 | Ni-5Si alloy (Annealed) | other | irradiated | 14 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,685 | ornl_12 | Ni-8Si alloy (Annealed) | other | irradiated | 14 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.4 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,686 | ornl_12 | Ni-Si alloy (Annealed) | other | irradiated | 14 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 6 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,687 | ornl_12 | Ni-5Si alloy (Annealed) | other | irradiated | 14 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,688 | ornl_12 | Ni-8Si alloy (Annealed) | other | irradiated | 14 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,689 | ornl_12 | Ni-Si alloy (Annealed) | other | irradiated | 14 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,690 | ornl_12 | Ni-Si alloy (Annealed) | other | irradiated | 12 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.4 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,691 | ornl_12 | Ni-5Si alloy (Annealed) | other | irradiated | 12 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,692 | ornl_12 | Ni-8Si alloy (Annealed) | other | irradiated | 14 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,693 | ornl_12 | Ni-5Si | other | irradiated | null | 425 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,694 | ornl_12 | Ni-5Si | other | irradiated | null | 500 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,695 | ornl_12 | Ni-5Si | other | irradiated | null | 600 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,696 | ornl_12 | Ni-2% Si | other | irradiated | null | 365 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,697 | ornl_12 | Ni-2% Si | other | irradiated | null | 406 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,698 | ornl_12 | Ni-2% Si | other | irradiated | null | 520 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,699 | ornl_12 | Ni-2% Si | other | irradiated | null | 600 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,700 | ornl_12 | Ni-8Si | other | irradiated | null | 425 | EBR-II | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,701 | ornl_12 | Ni-8Si | other | irradiated | null | 500 | EBR-II | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,702 | ornl_12 | Ni-8Si | other | irradiated | null | 600 | EBR-II | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,704 | ornl_12 | Ni-0Al (Annealed) | other | irradiated | 14 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 6.2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,705 | ornl_12 | Ni-5Al (Annealed) | other | irradiated | 14 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,706 | ornl_12 | Ni-0Al (Cold Worked) | other | irradiated | 14 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,709 | ornl_12 | Ni-5Al (Annealed) | other | irradiated | 14 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,710 | ornl_12 | Ni-0Al (Cold Worked) | other | irradiated | 14 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.3 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,711 | ornl_12 | Ni-0Al (Annealed) | other | irradiated | 12 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,712 | ornl_12 | Ni-0Al (Cold Worked) | other | irradiated | 12 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,713 | ornl_12 | Ni-0Al (Cold Worked and Aged) | other | irradiated | 14 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,714 | ornl_12 | Ni-5Al (Cold Worked) | other | irradiated | 14 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,715 | ornl_12 | Ni-5Al | other | irradiated | null | 425 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,716 | ornl_12 | Ni-5Al | other | irradiated | null | 500 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,717 | ornl_12 | Ni-5Al | other | irradiated | null | 600 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.