record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
3,831 | ornl_12 | TZM | other | irradiated | null | 600 | null | neutron | null | null | Mechanical Hardness | null | null | null | 740 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,832 | ornl_12 | TZM | other | irradiated | null | 600 | null | neutron | null | null | Mechanical Hardness | null | null | null | 650 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,833 | ornl_12 | High purity copper | copper_alloy | irradiated | 48 | 413 | FFTF | neutron | 100 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,834 | ornl_12 | OFHC copper | copper_alloy | irradiated | 48 | 413 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,835 | ornl_12 | 99.999% Cu | copper_alloy | irradiated | null | 50 | LAMPF | proton | 90 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,836 | ornl_12 | Cu | copper_alloy | irradiated | 49 | 413 | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,837 | ornl_12 | Cu containing 100 appm of implanted helium | copper_alloy | irradiated | 49 | 413 | FFTF/MOTA | neutron | 100 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,839 | ornl_12 | copper | copper_alloy | irradiated | null | 400 | null | proton | 100 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,840 | ornl_12 | pure Cu | copper_alloy | irradiated | 48 | 413 | null | neutron | 15 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,841 | ornl_12 | Cu-base alloys | copper_alloy | irradiated | 34 | 415 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,842 | ornl_12 | Cu-base alloys | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,843 | ornl_12 | Cu-base alloys | copper_alloy | irradiated | 32 | 529 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,844 | ornl_12 | pure copper | copper_alloy | irradiated | 96 | null | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,845 | ornl_12 | MARZ Cu | copper_alloy | irradiated | null | 411 | null | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,846 | ornl_12 | MARZ Cu | copper_alloy | irradiated | null | 414 | null | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,848 | ornl_12 | MARL copper | copper_alloy | irradiated | 150 | 411 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,849 | ornl_12 | MARL copper | copper_alloy | irradiated | 150 | 430 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,850 | ornl_12 | pure copper | copper_alloy | irradiated | 150 | null | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,851 | ornl_12 | pure copper | copper_alloy | irradiated | 32 | 529 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,852 | ornl_12 | CuNiBe | copper_alloy | irradiated | 34 | 414 | null | null | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,853 | ornl_12 | CuNiBe | copper_alloy | irradiated | 32 | 539 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,854 | ornl_12 | AMAX MZC | copper_alloy | irradiated | 16 | 430 | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,855 | ornl_12 | CuNiTi | copper_alloy | irradiated | 34 | 411 | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,856 | ornl_12 | CuNiTi | copper_alloy | irradiated | 32 | 539 | null | null | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,857 | ornl_12 | Pure Cu | copper_alloy | irradiated | 150 | 420 | FFTF-MOTA | neutron | null | 420 | Swelling | null | null | null | null | null | null | null | null | null | 80 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,858 | ornl_12 | Cu-5Ni | copper_alloy | irradiated | 150 | 420 | FFTF-MOTA | neutron | null | 420 | Swelling | null | null | null | null | null | null | null | null | null | 75 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,860 | ornl_12 | MZC (HTB) | copper_alloy | irradiated | 150 | 420 | FFTF-MOTA | neutron | null | 420 | Swelling | null | null | null | null | null | null | null | null | null | 8 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,861 | ornl_12 | MIT #3 | beryllium | irradiated | 150 | 420 | FFTF-MOTA | neutron | null | 420 | Mechanical Tensile | 250 | 420 | null | null | null | null | null | null | null | 4 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,862 | ornl_12 | MIT #2 | beryllium | irradiated | 150 | 420 | FFTF-MOTA | neutron | null | 420 | Mechanical Tensile | 180 | 320 | null | null | null | null | null | null | null | 2.5 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,863 | ornl_12 | CuCrZr | copper_alloy | irradiated | 150 | 420 | FFTF-MOTA | neutron | null | 420 | Swelling | null | null | null | null | null | null | null | null | null | 1.5 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,864 | ornl_12 | CuNiBe (HTA) | copper_alloy | irradiated | 10 | 411 | null | null | null | 411 | Swelling | null | null | null | null | null | null | null | null | null | 2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,867 | ornl_12 | CuNiBe (HTB) | copper_alloy | irradiated | 100 | 411 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 14 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,868 | ornl_12 | Cu-2Be (Gen. 1) | copper_alloy | irradiated | 100 | 411 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,869 | ornl_12 | Cu-2Be (Gen. 2) | copper_alloy | irradiated | 150 | 411 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,870 | ornl_12 | Cu-2.0Be (HTB) | copper_alloy | unirradiated | 0 | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 800 | 1,000 | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,871 | ornl_12 | Cu-2.0Be (HTB) | copper_alloy | irradiated | 150 | 411 | null | null | null | null | Mechanical Tensile | 450 | 600 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,872 | ornl_12 | CuNiBe (U4) | copper_alloy | unirradiated | 0 | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 450 | 600 | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,874 | ornl_12 | CuNiTi without TiO2 and Zr | copper_alloy | irradiated | 150 | 411 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 11 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,875 | ornl_12 | CuNiTi with additives | copper_alloy | irradiated | 150 | 411 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,876 | ornl_12 | pure copper | copper_alloy | irradiated | 1 | 500 | ORR | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.8 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,877 | ornl_12 | pure copper | copper_alloy | irradiated | 32 | 529 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,878 | ornl_12 | copper alloy | copper_alloy | irradiated | 100 | 400 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,879 | ornl_12 | MARZ | copper_alloy | irradiated | 34 | 411 | FFTF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,880 | ornl_12 | 5Ni-Cu | copper_alloy | irradiated | 50 | 527 | FFTF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,881 | ornl_12 | CuBe | copper_alloy | irradiated | 50 | 411 | FFTF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,882 | ornl_12 | CuBe | copper_alloy | unirradiated | 0 | null | null | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | 807 | 1,040 | 7 | 0 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,883 | ornl_12 | CuBe | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Mechanical Tensile | 331 | 541 | 12.1 | null | null | null | null | null | null | 0.68 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,884 | ornl_12 | CuNiBe-aa | copper_alloy | unirradiated | 0 | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 575 | 770 | 9.5 | 0 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,885 | ornl_12 | CuNiBe-aa | copper_alloy | irradiated | 34 | 411 | null | neutron | null | null | Mechanical Tensile | 508 | 531 | 1.1 | null | null | null | null | null | null | -0.04 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,886 | ornl_12 | CuNiBe-ca | copper_alloy | unirradiated | 0 | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 501 | 553 | 2.5 | 0 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,888 | ornl_12 | CuNiBe-ca | copper_alloy | irradiated | 30 | 527 | null | neutron | null | null | Mechanical Tensile | 111 | 248 | 19.8 | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,889 | ornl_12 | MZC (AMAX) | copper_alloy | unirradiated | 0 | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 520 | 542 | 3.7 | 0 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,891 | ornl_12 | MZC (AMAX) | copper_alloy | irradiated | 30 | 527 | null | neutron | null | null | Mechanical Tensile | 124 | 256 | 23 | null | null | null | null | null | null | 0.42 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,894 | ornl_12 | MZC (MIT#2) | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Mechanical Tensile | 169 | 295 | 14.1 | null | null | null | null | null | null | 0.19 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,895 | ornl_12 | MZC (MIT#2) | copper_alloy | irradiated | 30 | 527 | null | neutron | null | null | Mechanical Tensile | 93 | 221 | 28.9 | null | null | null | null | null | null | 0.53 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,897 | ornl_12 | YZC (MIT#3) | copper_alloy | irradiated | 34 | 411 | null | neutron | null | null | Mechanical Tensile | 264 | 403 | 13.2 | null | null | null | null | null | null | 0.26 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,898 | ornl_12 | YZC (MIT#3) | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Mechanical Tensile | 248 | 388 | 15.1 | null | null | null | null | null | null | 0.66 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,899 | ornl_12 | YZC (MIT#3) | copper_alloy | irradiated | 30 | 527 | null | neutron | null | null | Mechanical Tensile | 166 | 314 | 18.9 | null | null | null | null | null | null | 0.21 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,901 | ornl_12 | MZC alloy (annealed and aged [MIT#2]) | copper_alloy | unirradiated | 0 | null | null | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | 210 | 230 | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,902 | ornl_12 | MZC alloy (annealed and aged [MIT#3]) | copper_alloy | unirradiated | 0 | null | null | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | 310 | 330 | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,903 | ornl_12 | MZC alloy | copper_alloy | irradiated | 34 | 411 | null | neutron | null | null | Mechanical Tensile | 220 | 250 | null | null | null | null | null | null | null | 2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,904 | ornl_12 | MZC alloy | copper_alloy | irradiated | 50 | 411 | null | neutron | null | null | Mechanical Tensile | 180 | 210 | null | null | null | null | null | null | null | 2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,905 | ornl_12 | MZC alloy | copper_alloy | irradiated | 30 | 527 | null | neutron | null | null | Mechanical Tensile | 120 | 150 | null | null | null | null | null | null | null | 2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,906 | ornl_12 | Type 316 SS | austenitic_steel | irradiated | 10 | 100 | null | neutron | null | 100 | Mechanical Fracture | null | null | null | null | 28 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,910 | ornl_12 | Type 304 SS | austenitic_steel | unirradiated | 9 | null | null | null | null | null | Mechanical Fracture | null | null | null | null | 115 | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,911 | ornl_12 | Type 316 SS | austenitic_steel | irradiated | 10 | null | null | null | null | 100 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,912 | ornl_12 | Type 316 SS | austenitic_steel | irradiated | 45 | null | null | null | null | 100 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,913 | ornl_12 | Type 304 SS | austenitic_steel | irradiated | 10 | null | null | null | null | null | Mechanical Fracture | null | null | null | null | 113 | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,914 | ornl_12 | Type 301 SS | other | irradiated | 10 | null | null | null | null | 100 | Mechanical Fracture | null | null | null | null | 68 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,915 | ornl_12 | Type 316 SS | austenitic_steel | irradiated | 10 | null | null | null | null | 250 | Mechanical Fracture | null | null | null | null | 55 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,916 | ornl_12 | Type 316 SS | austenitic_steel | irradiated | 10 | null | null | null | null | 100 | Mechanical Fracture | null | null | null | null | 29.5 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,917 | ornl_12 | Type 316 SS | austenitic_steel | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 300 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
3,919 | ornl_12 | Type 310 SS | other | irradiated | null | null | null | null | null | null | Mechanical Fracture | null | null | null | null | 85 | null | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
3,921 | ornl_12 | Type 304 SS | austenitic_steel | irradiated | 9 | null | null | neutron | null | null | Mechanical Fracture | null | null | null | null | 115 | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,923 | ornl_12 | Type 316 SS + Ti | austenitic_steel | irradiated | 10 | null | null | neutron | 550 | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,924 | ornl_12 | Austenitic Steels (316, 316L, 316NG, 304) | austenitic_steel | irradiated | null | 60 | null | neutron | 250 | null | Mechanical Fatigue | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,925 | ornl_12 | CP type 304 SS | austenitic_steel | irradiated | null | 288 | fission power reactor | neutron | null | 288 | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,926 | ornl_12 | HP type 304 SS | austenitic_steel | irradiated | null | 288 | fission power reactor | neutron | null | 288 | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,927 | ornl_12 | LS1A | other | unirradiated | 0 | null | ion_beam | ion | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,928 | ornl_12 | LS1A | other | irradiated | 1 | 675 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,929 | ornl_12 | LS1A | other | irradiated | 10 | null | ion_beam | ion | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,930 | ornl_12 | LS1A | other | irradiated | 75 | null | ion_beam | ion | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,932 | ornl_12 | LS1A | other | irradiated | 10 | 600 | ion_beam | ion | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,933 | ornl_12 | LS1A | other | irradiated | 70 | 600 | ion_beam | ion | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,934 | ornl_12 | Al2O3 | copper_alloy | irradiated | 0.00001 | 450 | ion_beam | proton | null | 450 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,935 | ornl_12 | Al2O3 | copper_alloy | irradiated | 0.00004 | 450 | ion_beam | ion | null | 450 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,936 | ornl_12 | MgAl2O4 | ceramic_insulator | irradiated | 0.001 | 400 | ion_beam | proton | null | 400 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,938 | ornl_12 | Al2O3 | copper_alloy | irradiated | 0.00004 | 450 | ion_beam | ion | null | 450 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,939 | ornl_12 | Al2O3 | copper_alloy | irradiated | 0.00006 | null | ion_beam | ion | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,940 | ornl_12 | Al2O3 | copper_alloy | irradiated | 0.1 | 70 | null | neutron | null | 200 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,941 | ornl_12 | ceramic | ceramic_insulator | irradiated | 0.00001 | null | null | neutron | null | null | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,942 | ornl_12 | Al2O3 | copper_alloy | irradiated | 0.001 | 300 | null | proton | null | 300 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,943 | ornl_12 | AlN | ceramic_insulator | irradiated | null | 25 | pulsed fission reactor | neutron | null | 25 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,944 | ornl_12 | sapphire | ceramic_insulator | irradiated | null | 25 | pulsed fission reactor | neutron | null | 25 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,947 | ornl_12 | Al2O3 | copper_alloy | irradiated | 0.1 | null | fission reactor | neutron | null | 25 | Thermal | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,948 | ornl_12 | Al2O3 | copper_alloy | irradiated | null | 26.85 | fission reactor | neutron | null | -233.15 | Thermal | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,949 | ornl_12 | BeO | beryllium | irradiated | 0.0005 | -50 | null | neutron | null | null | Thermal | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
3,950 | ornl_12 | BeO | beryllium | irradiated | null | 100 | fission | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
3,951 | ornl_12 | Sapphire | ceramic_insulator | unirradiated | 0 | null | TRIGA | neutron | null | 25 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
3,952 | ornl_12 | Sapphire | ceramic_insulator | irradiated | 0 | null | TRIGA | neutron | null | null | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.