record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
4,072 | ornl_13 | Fe-15Cr-30Ni | austenitic_steel | irradiated | 13.25 | 400 | null | null | 43 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 3 | 300,000,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,073 | ornl_13 | Fe-15Cr-45Ni | austenitic_steel | irradiated | 13.25 | 400 | null | null | 43 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 3.5 | 350,000,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,075 | ornl_13 | Fe-15Cr-45Ni CW | austenitic_steel | irradiated | 13.25 | 500 | null | null | 43 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 4 | 200,000,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,076 | ornl_13 | Fe-15Cr-20Ni CW | austenitic_steel | irradiated | 13.25 | 600 | null | null | 43 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 8 | 4,000,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,078 | ornl_13 | Fe-15Cr-25Ni (SA) | austenitic_steel | irradiated | null | 500 | null | null | null | 500 | Microstructure | null | null | null | null | null | null | null | null | null | null | 5 | 10,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,080 | ornl_13 | Fe-15Cr-35Ni (SA) | austenitic_steel | irradiated | null | 500 | null | null | null | 500 | Microstructure | null | null | null | null | null | null | null | null | null | null | 5 | 5,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,081 | ornl_13 | Fe-15Cr-35Ni (CW) | austenitic_steel | irradiated | null | 500 | null | null | null | 500 | Microstructure | null | null | null | null | null | null | null | null | null | null | 10 | 2,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,082 | ornl_13 | Fe-Cr | RAFM_steel | irradiated | null | 500 | null | null | null | 500 | Swelling | null | null | null | null | null | null | null | null | null | 3 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,084 | ornl_13 | Fe-15Cr-25Ni (SA) | austenitic_steel | irradiated | 12.7 | 500 | ORR | neutron | 45 | null | Swelling | null | null | null | null | null | null | null | null | null | 0.7 | 4.5 | 15,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,085 | ornl_13 | Fe-15Cr-25Ni (SA) | austenitic_steel | irradiated | 12.7 | 600 | ORR | neutron | 45 | null | Swelling | null | null | null | null | null | null | null | null | null | 0.5 | 12 | 500,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,086 | ornl_13 | Fe-20Cr-35Ni | ferritic_model_alloy | irradiated | 12.7 | 500 | ORR | neutron | 45 | null | Swelling | null | null | null | null | null | null | null | null | null | 0.8 | 4 | 120,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,087 | ornl_13 | Fe-20Cr-35Ni | ferritic_model_alloy | irradiated | 12.7 | 600 | ORR | neutron | 45 | null | Swelling | null | null | null | null | null | null | null | null | null | 0.6 | 8 | 6,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,088 | ornl_13 | Fe-25Cr-35Ni | ferritic_model_alloy | irradiated | 12.7 | 500 | ORR | neutron | 45 | null | Swelling | null | null | null | null | null | null | null | null | null | 1.1 | 4 | 180,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,089 | ornl_13 | Fe-25Cr-35Ni | ferritic_model_alloy | irradiated | 12.7 | 600 | ORR | neutron | 45 | null | Swelling | null | null | null | null | null | null | null | null | null | 0.9 | 9 | 5,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,090 | ornl_13 | Fe-7.5Cr-35Ni | ferritic_model_alloy | irradiated | null | 500 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,091 | ornl_13 | Fe-15Cr-35Ni | austenitic_steel | irradiated | null | 500 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,094 | ornl_13 | Fe-15Cr-35Ni | austenitic_steel | irradiated | null | 600 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,096 | ornl_13 | Fe-15Cr-25Ni | austenitic_steel | irradiated | 6 | 490 | MOTA | neutron | 0.3 | 25 | Mechanical Tensile | 580 | null | 12 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,097 | ornl_13 | Fe-15Cr-25Ni-0.04P | austenitic_steel | irradiated | 6 | 490 | MOTA | neutron | 0.3 | 25 | Mechanical Tensile | 520 | null | 15 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,098 | ornl_13 | Fe-15Cr-45Ni | austenitic_steel | irradiated | 6 | 490 | MOTA | neutron | 0.3 | 25 | Mechanical Tensile | 480 | null | 18 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,100 | ornl_13 | 25 Ni Cold Worked | other | irradiated | 0.4 | 465 | null | neutron | 62 | 465 | Mechanical Tensile | 450 | null | 25 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,102 | ornl_13 | 25 Ni Annealed | other | irradiated | 0.4 | 465 | null | neutron | 62 | 465 | Mechanical Tensile | 280 | null | 32 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,104 | ornl_13 | 25 Ni + P Annealed | other | irradiated | 0.4 | 465 | null | neutron | 62 | 465 | Mechanical Tensile | 300 | null | 35 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,105 | ornl_13 | 45 Ni Cold Worked | other | irradiated | 0.1 | 465 | null | neutron | 0.3 | 465 | Mechanical Tensile | 580 | null | 22 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,106 | ornl_13 | 45 Ni Annealed | other | irradiated | 0.4 | 465 | null | neutron | 62 | 465 | Mechanical Tensile | 320 | null | 35 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,107 | ornl_13 | Fe-10Cr-Si (0.1%) | RAFM_steel | irradiated | 30 | 365 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.44 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,109 | ornl_13 | Fe-10Cr ternary alloys (Si, V, Mn, W, Ta, Zr) | RAFM_steel | irradiated | 92.6 | 411 | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,111 | ornl_13 | Fe-10Cr-0.1Si | RAFM_steel | irradiated | 30 | 365 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.44 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,112 | ornl_13 | Fe-10Cr-0.1Si | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.88 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,113 | ornl_13 | Fe-10Cr-1Si | RAFM_steel | irradiated | 30 | 365 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.6 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,115 | ornl_13 | Fe-10Cr-0.1Mn | RAFM_steel | irradiated | 30 | 365 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.37 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,116 | ornl_13 | Fe-10Cr-0.1Mn | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.64 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,119 | ornl_13 | Fe-10Cr-0.1V | RAFM_steel | irradiated | 30 | 365 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.15 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,120 | ornl_13 | Fe-10Cr-0.1V | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.88 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,121 | ornl_13 | Fe-10Cr-1V | RAFM_steel | irradiated | 30 | 365 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.19 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,122 | ornl_13 | Fe-10Cr-1V | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.56 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,123 | ornl_13 | Fe-10Cr-0.1W | RAFM_steel | irradiated | 30 | 365 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.17 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,124 | ornl_13 | Fe-10Cr-0.1W | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.96 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,125 | ornl_13 | Fe-10Cr-1W | RAFM_steel | irradiated | 30 | 365 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.04 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,126 | ornl_13 | Fe-10Cr-1W | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.11 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,128 | ornl_13 | Fe-10Cr-0.1Ta | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.08 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,129 | ornl_13 | Fe-10Cr-1Ta | RAFM_steel | irradiated | 30 | 365 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.13 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,130 | ornl_13 | Fe-10Cr-1Ta | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.32 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,131 | ornl_13 | Fe-10Cr-0.1Zr | RAFM_steel | irradiated | 30 | 365 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.15 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,132 | ornl_13 | Fe-10Cr-0.1Zr | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.33 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,133 | ornl_13 | Fe-10Cr-1Zr | RAFM_steel | irradiated | 30 | 365 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.27 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,134 | ornl_13 | Fe-10Cr-1Zr | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.81 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,136 | ornl_13 | Fe-10Cr-0.1Mn | RAFM_steel | irradiated | 30 | 420 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,137 | ornl_13 | Fe-10Cr-1M (M=Si) | RAFM_steel | irradiated | 30 | 365 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,138 | ornl_13 | Fe-10Cr-1M (M=V, Mn, W, Ta, Zr) | RAFM_steel | irradiated | 30 | 365 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,140 | ornl_13 | Fe-10Cr-1Si | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,141 | ornl_13 | Fe-10Cr-1V | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,142 | ornl_13 | Fe-10Cr-1Mn | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,145 | ornl_13 | Fe-10Cr-1Zr | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,146 | ornl_13 | Fe-10Cr-1Mn | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,147 | ornl_13 | Fe-10Cr-0.1W | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,148 | ornl_13 | Fe-10Cr-1W | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,151 | ornl_13 | Fe-10Cr alloys | RAFM_steel | irradiated | 30 | 365 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,152 | ornl_13 | Fe-10Cr-1Ta | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,153 | ornl_13 | Fe-10Cr-0.1Zr | RAFM_steel | irradiated | 100 | 410 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,154 | ornl_13 | Fe-10Cr-1Si | RAFM_steel | irradiated | 30 | 365 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,155 | ornl_13 | Fe-10Cr-0.1V | RAFM_steel | irradiated | null | 365 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,156 | ornl_13 | Fe-10Cr-1Mn | RAFM_steel | irradiated | 95 | 365 | Experimental Breeder reactor | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.7 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,157 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 95 | 365 | Experimental Breeder reactor | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,158 | ornl_13 | Fe-10Cr-0.1Zr | RAFM_steel | irradiated | null | 365 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,160 | ornl_13 | Fe-10Cr-0.1W | RAFM_steel | irradiated | 100 | 410 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,162 | ornl_13 | Fe-10Cr-1Si | RAFM_steel | irradiated | 100 | 410 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,164 | ornl_13 | Fe-(3-18)Cr binary alloys | RAFM_steel | irradiated | 35 | 403 | FFTF | neutron | null | 25 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,165 | ornl_13 | Fe-(3-18)Cr binary alloys | RAFM_steel | irradiated | 35 | 574 | FFTF | neutron | null | 25 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,166 | ornl_13 | Fe-3Cr binary ferritic alloy | RAFM_steel | unirradiated | 0 | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 260 | null | 31 | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,167 | ornl_13 | Fe-3Cr binary ferritic alloy | RAFM_steel | irradiated | 7 | 365 | FFTF | neutron | null | 25 | Mechanical Tensile | 520 | null | 10 | null | null | null | 260 | null | 31 | null | null | null | null | 1 | false | ornl_extraction | null | null | null | null |
4,168 | ornl_13 | Fe-18Cr binary ferritic alloy | RAFM_steel | irradiated | 35 | 574 | FFTF | neutron | null | 25 | Mechanical Tensile | 580 | null | 5 | null | null | null | 250 | null | 32 | null | null | null | null | 1 | false | ornl_extraction | null | null | null | null |
4,169 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 35 | 403 | FFTF | neutron | null | 25 | Mechanical Tensile | 650 | null | 8 | null | null | null | 240 | null | 30 | null | null | null | null | 1 | false | ornl_extraction | null | null | null | null |
4,170 | ornl_13 | 3 Cr | other | irradiated | null | 25 | null | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,171 | ornl_13 | 3 Cr | other | irradiated | null | 365 | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,172 | ornl_13 | 3 Cr | other | irradiated | null | 400 | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,173 | ornl_13 | 3 Cr | other | irradiated | null | 585 | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,174 | ornl_13 | 6 Cr | other | irradiated | null | 25 | null | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,175 | ornl_13 | 6 Cr | other | irradiated | null | 365 | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,176 | ornl_13 | 6 Cr | other | irradiated | null | 400 | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,177 | ornl_13 | 6 Cr | other | irradiated | null | 585 | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,178 | ornl_13 | 9 Cr | RAFM_steel | irradiated | null | 400 | null | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,179 | ornl_13 | 9 Cr | RAFM_steel | irradiated | null | 600 | null | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,181 | ornl_13 | 12 Cr | RAFM_steel | irradiated | null | 600 | null | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,182 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 35 | 420 | FFTF | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,184 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 4.5 | 365 | MOTA | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,185 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 36 | 420 | null | neutron | 5 | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,186 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 37 | 420 | null | neutron | 5 | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,188 | ornl_13 | 12Cr-1MoVW | RAFM_steel | irradiated | 36 | 420 | null | neutron | 5 | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,189 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 5 | 365 | MOTA | neutron | 1 | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,190 | ornl_13 | 12Cr-1MoVW | RAFM_steel | unirradiated | 0 | null | null | neutron | null | 250 | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | 8.5 | 0.85 | false | ornl_extraction | null | null | null | null |
4,191 | ornl_13 | 12Cr-1MoVW | RAFM_steel | irradiated | 4 | 365 | null | neutron | null | 250 | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | 4.5 | 0.85 | false | ornl_extraction | null | null | null | null |
4,192 | ornl_13 | 9Cr steel | RAFM_steel | unirradiated | 0 | null | null | neutron | null | 100 | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | 10.5 | 0.85 | false | ornl_extraction | null | null | null | null |
4,193 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 36 | 420 | null | neutron | 5 | 100 | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | 7.8 | 0.85 | false | ornl_extraction | null | null | null | null |
4,195 | ornl_13 | 12Cr-1MoVW Steel | RAFM_steel | unirradiated | 0 | null | null | null | null | 200 | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | 8.5 | 0.85 | false | ornl_extraction | null | null | null | null |
4,196 | ornl_13 | 12Cr-1MoVW Steel | RAFM_steel | irradiated | 35 | 420 | null | null | null | 200 | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | 4.2 | 0.85 | false | ornl_extraction | null | null | null | null |
4,197 | ornl_13 | 12Cr-1MoVW Steel | RAFM_steel | irradiated | 35 | 420 | null | null | null | 200 | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | 5.2 | 0.85 | false | ornl_extraction | null | null | null | null |
4,198 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | null | 365 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,199 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | null | 420 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,200 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 5 | 365 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | 254.15 | null | null | null | null | null | null | 7.6 | 0.8 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.