record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
4,201 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 5 | 365 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | 236.15 | null | null | null | null | null | null | 8.2 | 0.8 | false | ornl_extraction | null | null | null | null |
4,202 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 5 | 365 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | 309.15 | null | null | null | null | null | null | 7.3 | 0.8 | false | ornl_extraction | null | null | null | null |
4,203 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 5 | 365 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | 267.15 | null | null | null | null | null | null | 8.9 | 0.8 | false | ornl_extraction | null | null | null | null |
4,205 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 36 | 420 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | 238.15 | null | null | null | null | null | null | 7.8 | 0.8 | false | ornl_extraction | null | null | null | null |
4,206 | ornl_13 | 12Cr-1MoVW Steel | RAFM_steel | irradiated | 4 | 365 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | 370.15 | null | null | null | null | null | null | 3.6 | 0.8 | false | ornl_extraction | null | null | null | null |
4,207 | ornl_13 | 12Cr-1MoVW Steel | RAFM_steel | irradiated | 4 | 365 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | 368.15 | null | null | null | null | null | null | 3.4 | 0.8 | false | ornl_extraction | null | null | null | null |
4,208 | ornl_13 | 12Cr-1MoVW Steel | RAFM_steel | irradiated | 4 | 365 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | 373.15 | null | null | null | null | null | null | 2.5 | 0.8 | false | ornl_extraction | null | null | null | null |
4,209 | ornl_13 | 12Cr-1MoVW Steel | RAFM_steel | irradiated | 4 | 365 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | 380.15 | null | null | null | null | null | null | 3.9 | 0.8 | false | ornl_extraction | null | null | null | null |
4,210 | ornl_13 | 12Cr-1MoVW Steel | RAFM_steel | irradiated | 35 | 420 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | 328.15 | null | null | null | null | null | null | 4.1 | 0.8 | false | ornl_extraction | null | null | null | null |
4,211 | ornl_13 | 12Cr-1MoVW Steel | RAFM_steel | irradiated | 35 | 420 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | 345.15 | null | null | null | null | null | null | 4.1 | 0.8 | false | ornl_extraction | null | null | null | null |
4,212 | ornl_13 | reduced activation ferritic steels (2 1/4-3)Cr-(1-2)W | RAFM_steel | irradiated | 48.5 | 410 | FFTF/MOTA | neutron | null | 410 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,213 | ornl_13 | reduced activation ferritic steels | RAFM_steel | irradiated | 0.1 | 300 | JMTR | neutron | null | 600 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,215 | ornl_13 | reduced activation steels | RAFM_steel | irradiated | 7 | 365 | FFTF | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,218 | ornl_13 | 2Cr-0.5V | RAFM_steel | irradiated | 44 | 420 | null | neutron | null | 420 | Mechanical Tensile | 992 | 1,014 | 7.6 | null | null | null | 785 | 901 | 13.9 | null | null | null | null | 0.95 | false | ornl_extraction | null | null | null | null |
4,219 | ornl_13 | 2Cr-0.5V | RAFM_steel | irradiated | 39 | 585 | null | neutron | null | 585 | Mechanical Tensile | 204 | 319 | 32.5 | null | null | null | 785 | 901 | 13.9 | null | null | null | null | 0.95 | false | ornl_extraction | null | null | null | null |
4,220 | ornl_13 | 2Cr-1.0V | RAFM_steel | irradiated | 12 | 420 | null | neutron | null | 420 | Mechanical Tensile | 1,055 | 1,086 | 8.1 | null | null | null | 312 | 555 | 26.7 | null | null | null | null | 0.95 | false | ornl_extraction | null | null | null | null |
4,221 | ornl_13 | 2Cr-1.0V | RAFM_steel | irradiated | 43 | 420 | null | neutron | null | 420 | Mechanical Tensile | 1,110 | 1,121 | 8 | null | null | null | 312 | 555 | 26.7 | null | null | null | null | 0.95 | false | ornl_extraction | null | null | null | null |
4,222 | ornl_13 | 2Cr-1.5V | RAFM_steel | irradiated | 8 | 420 | null | neutron | null | 420 | Mechanical Tensile | 706 | 755 | 6.1 | null | null | null | 297 | 477 | 24.4 | null | null | null | null | 0.95 | false | ornl_extraction | null | null | null | null |
4,223 | ornl_13 | 5Cr-2WV | RAFM_steel | irradiated | 13 | 365 | null | neutron | null | 365 | Mechanical Tensile | 730 | 771 | 9.1 | null | null | null | 537 | 645 | 13 | null | null | null | null | 0.95 | false | ornl_extraction | null | null | null | null |
4,224 | ornl_13 | 8Cr-2WVTaB | RAFM_steel | irradiated | 7 | 365 | null | neutron | null | 365 | Mechanical Tensile | 697 | 780 | 6.9 | null | null | null | 679 | 811 | 5 | null | null | null | null | 0.95 | false | ornl_extraction | null | null | null | null |
4,225 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 12 | 420 | null | neutron | null | 420 | Mechanical Tensile | 660 | 698 | 12 | null | null | null | 566 | 665 | 15.7 | null | null | null | null | 0.95 | false | ornl_extraction | null | null | null | null |
4,226 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 10 | 420 | null | neutron | null | 420 | Mechanical Tensile | 599 | 677 | 16.9 | null | null | null | 582 | 675 | 15.8 | null | null | null | null | 0.95 | false | ornl_extraction | null | null | null | null |
4,228 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 10 | 420 | null | neutron | null | 420 | Mechanical Tensile | 608 | 714 | 15.8 | null | null | null | 716 | 587 | 15.8 | null | null | null | null | 0.95 | false | ornl_extraction | null | null | null | null |
4,229 | ornl_13 | 12Cr-6Mn-1W | RAFM_steel | irradiated | 8 | 420 | null | neutron | null | 420 | Mechanical Tensile | 848 | 942 | 14.7 | null | null | null | 1,002 | 10.1 | 822 | null | null | null | null | 0.95 | false | ornl_extraction | null | null | null | null |
4,230 | ornl_13 | 12Cr-2WV | RAFM_steel | irradiated | 7 | 365 | null | neutron | null | 365 | Mechanical Tensile | 857 | 885 | 8 | null | null | null | 657 | 13 | 522 | null | null | null | null | 0.95 | false | ornl_extraction | null | null | null | null |
4,231 | ornl_13 | 2 Cr | RAFM_steel | irradiated | 0 | 365 | null | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | 500 | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,233 | ornl_13 | 2 Cr | RAFM_steel | irradiated | 40 | 420 | null | neutron | null | null | Mechanical Tensile | null | 1,150 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,234 | ornl_13 | 5-9 Cr | RAFM_steel | irradiated | 40 | 420 | null | neutron | null | null | Mechanical Tensile | null | 800 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,235 | ornl_13 | 12 Cr | RAFM_steel | irradiated | 40 | 420 | null | neutron | null | null | Mechanical Tensile | null | 850 | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,237 | ornl_13 | GA3X | RAFM_steel | irradiated | 34 | 365 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,238 | ornl_13 | F82H | RAFM_steel | irradiated | 6.7 | 365 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,239 | ornl_13 | 2Cr-1.5V | RAFM_steel | irradiated | 11.3 | 365 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 523.15 | null | null | null | null | null | null | 308 | 0.8 | false | ornl_extraction | null | null | null | null |
4,240 | ornl_13 | 2 1/4CrV | RAFM_steel | irradiated | 7 | 365 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 523.15 | null | null | null | null | null | null | 10 | 0.8 | false | ornl_extraction | null | null | null | null |
4,241 | ornl_13 | 2 1/4Cr-1WV | RAFM_steel | irradiated | 7 | 365 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 465.15 | null | null | null | null | null | null | 11.8 | 0.8 | false | ornl_extraction | null | null | null | null |
4,243 | ornl_13 | 2 1/4Cr-2WV | RAFM_steel | irradiated | 7 | 365 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 384.15 | null | null | null | null | null | null | 9.1 | 0.8 | false | ornl_extraction | null | null | null | null |
4,244 | ornl_13 | 2 1/4Cr-2WV (JLF-4) | RAFM_steel | irradiated | 0.01 | 300 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 221.15 | null | null | null | null | null | null | 0.93 | 0.8 | false | ornl_extraction | null | null | null | null |
4,246 | ornl_13 | 7Cr-2WV (JLF-3) | RAFM_steel | irradiated | 0.01 | 300 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 212.15 | null | null | null | null | null | null | 0.92 | 0.8 | false | ornl_extraction | null | null | null | null |
4,247 | ornl_13 | 7.5Cr-2W (GA3X) | RAFM_steel | irradiated | 10.5 | 365 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 273.15 | null | null | null | null | null | null | 405 | 0.8 | false | ornl_extraction | null | null | null | null |
4,249 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 12 | 365 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 317.15 | null | null | null | null | null | null | 370 | 0.8 | false | ornl_extraction | null | null | null | null |
4,250 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 7 | 365 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 281.15 | null | null | null | null | null | null | 8.4 | 0.8 | false | ornl_extraction | null | null | null | null |
4,252 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 0.01 | 300 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 189.15 | null | null | null | null | null | null | 0.97 | 0.8 | false | ornl_extraction | null | null | null | null |
4,253 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 0.01 | 300 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 236.15 | null | null | null | null | null | null | 0.93 | 0.8 | false | ornl_extraction | null | null | null | null |
4,254 | ornl_13 | 12Cr-6Mn-1V (L8) | RAFM_steel | irradiated | 12 | 365 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 473.15 | null | null | null | null | null | null | 201 | 0.8 | false | ornl_extraction | null | null | null | null |
4,255 | ornl_13 | 12Cr-6Mn-1W (L9) | RAFM_steel | irradiated | 12 | 365 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 438.15 | null | null | null | null | null | null | 219 | 0.8 | false | ornl_extraction | null | null | null | null |
4,256 | ornl_13 | 12Cr-2WV | RAFM_steel | irradiated | 7 | 367 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 429.15 | null | null | null | null | null | null | 8.3 | 0.8 | false | ornl_extraction | null | null | null | null |
4,257 | ornl_13 | 12Cr-2WVTa (JLF-5) | RAFM_steel | irradiated | 0.01 | 300 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 235.15 | null | null | null | null | null | null | 0.85 | 0.8 | false | ornl_extraction | null | null | null | null |
4,258 | ornl_13 | 12Cr-2WVTaTi (JLF-6) | RAFM_steel | irradiated | 0.01 | 300 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 277.15 | null | null | null | null | null | null | 0.79 | 0.8 | false | ornl_extraction | null | null | null | null |
4,260 | ornl_13 | 2 Cr | RAFM_steel | irradiated | 0 | null | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,262 | ornl_13 | 5-9 Cr | RAFM_steel | irradiated | 0 | null | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,263 | ornl_13 | 5-9 Cr | RAFM_steel | irradiated | 15 | null | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 323.15 | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,264 | ornl_13 | 12 Cr | RAFM_steel | irradiated | 0 | null | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,265 | ornl_13 | 12 Cr | RAFM_steel | irradiated | 15 | null | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 473.15 | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,266 | ornl_13 | 12Cr-1V (alloy L8) | RAFM_steel | irradiated | 115 | null | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,267 | ornl_13 | 12Cr-1WV (alloy L9) | RAFM_steel | irradiated | 15 | null | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 10 | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,268 | ornl_13 | 2Cr-0.5V | RAFM_steel | irradiated | null | 520 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,270 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 43.3 | 420 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,271 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 114.2 | 420 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,272 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 9.8 | 420 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,274 | ornl_13 | 9Cr steel | RAFM_steel | irradiated | 114.2 | 420 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,275 | ornl_13 | GA3X | RAFM_steel | irradiated | 33.5 | 420 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,276 | ornl_13 | GA3X | RAFM_steel | irradiated | 103 | 420 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,277 | ornl_13 | F82H | RAFM_steel | irradiated | 7 | 365 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,278 | ornl_13 | F82H | RAFM_steel | irradiated | 35.8 | 405 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,279 | ornl_13 | 12 Cr alloys with Mn | RAFM_steel | unirradiated | null | 600 | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.75 | false | ornl_extraction | null | null | null | null |
4,280 | ornl_13 | AISI 422 | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 700 | 920 | 17 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,281 | ornl_13 | HT9 | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 650 | 800 | 12 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,284 | ornl_13 | AISI 422 | RAFM_steel | irradiated | null | 400 | null | neutron | null | 100 | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | 5 | 0.85 | false | ornl_extraction | null | null | null | null |
4,285 | ornl_13 | HT9 | RAFM_steel | irradiated | null | 400 | null | neutron | null | 200 | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | 25 | 0.85 | false | ornl_extraction | null | null | null | null |
4,286 | ornl_13 | V-Ti Alloys | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 280 | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,287 | ornl_13 | V-Ti Alloys | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 340 | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,288 | ornl_13 | V-Ti Alloys | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 410 | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,290 | ornl_13 | V-Cr-5Ti Alloys | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 480 | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,291 | ornl_13 | V alloy | vanadium_alloy | irradiated | null | 420 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,292 | ornl_13 | V-5Cr-5Ti (BL 47E) | vanadium_alloy | unirradiated | null | null | null | null | null | 600 | Mechanical Creep | null | null | null | 75 | null | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,293 | ornl_13 | V-5Cr-5Ti (BL 47C) | vanadium_alloy | unirradiated | null | null | null | null | null | 600 | Mechanical Creep | null | null | null | 15 | null | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,294 | ornl_13 | V-10Cr-5Ti (BL 43B) | vanadium_alloy | unirradiated | null | null | null | null | null | 600 | Mechanical Creep | null | null | null | 82 | null | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,296 | ornl_13 | V-1Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | 125 | null | null | 260 | 290 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,297 | ornl_13 | V-3Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | 140 | null | null | 295 | 375 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,298 | ornl_13 | V-3Ti-0.3Si | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | 170 | null | null | 393 | 450 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,300 | ornl_13 | V-3Ti-1Si | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | 168 | null | null | 421 | 480 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,301 | ornl_13 | V-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | 147 | null | null | 336 | 412 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,303 | ornl_13 | V-20Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | 274 | null | null | 599 | 655 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,304 | ornl_13 | V-5Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | 171 | null | null | 387 | 454 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,306 | ornl_13 | V-10Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | 192 | null | null | 440 | 541 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,307 | ornl_13 | V-12Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | 201 | null | null | 471 | 573 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,308 | ornl_13 | V-15Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | 234 | null | null | 533 | 555 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,309 | ornl_13 | V-15Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | 216 | null | null | 545 | 634 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,310 | ornl_13 | V-15Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | 221 | null | null | 570 | 674 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,311 | ornl_13 | V alloy | vanadium_alloy | irradiated | 114 | 600 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,312 | ornl_13 | V-3Ti-1Si | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | 170 | null | null | 380 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,314 | ornl_13 | V-5Cr-5Ti | vanadium_alloy | irradiated | 31 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,315 | ornl_13 | V-5Cr-5Ti | vanadium_alloy | irradiated | 51 | 406 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,317 | ornl_13 | V alloy | vanadium_alloy | irradiated | 42.1 | 600 | FFTF MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,319 | ornl_13 | V-5Cr | vanadium_alloy | irradiated | 46.4 | 427 | FFTF MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,320 | ornl_13 | V-5Cr | vanadium_alloy | irradiated | 15.1 | 411 | FFTF MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,321 | ornl_13 | V pure | vanadium_alloy | irradiated | null | 600 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,322 | ornl_13 | V pure | vanadium_alloy | irradiated | null | 520 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.85 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,323 | ornl_13 | V pure | vanadium_alloy | irradiated | null | 427 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.33 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,324 | ornl_13 | V pure | vanadium_alloy | irradiated | null | 411 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.44 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,325 | ornl_13 | V-5 Cr | vanadium_alloy | irradiated | null | 600 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 15.4 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.