record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
4,326 | ornl_13 | V-5 Cr | vanadium_alloy | irradiated | null | 520 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.4 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,327 | ornl_13 | V-5 Cr | vanadium_alloy | irradiated | null | 427 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.97 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,328 | ornl_13 | V-5 Cr | vanadium_alloy | irradiated | null | 411 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.11 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,329 | ornl_13 | V-5Cr | vanadium_alloy | irradiated | null | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,330 | ornl_13 | V-5Cr | vanadium_alloy | irradiated | null | 427 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,331 | ornl_13 | V-5Cr | vanadium_alloy | irradiated | null | 520 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,332 | ornl_13 | V-5Cr | vanadium_alloy | irradiated | null | 600 | null | neutron | 100 | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,333 | ornl_13 | V alloy | vanadium_alloy | irradiated | null | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,335 | ornl_13 | V alloy | vanadium_alloy | irradiated | null | 520 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,336 | ornl_13 | V alloy | vanadium_alloy | irradiated | null | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,337 | ornl_13 | V-5Cr | vanadium_alloy | irradiated | 44 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 14.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,338 | ornl_13 | V-5Cr | vanadium_alloy | irradiated | 44 | 427 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 8.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,339 | ornl_13 | V-5Cr | vanadium_alloy | irradiated | 44 | 520 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,340 | ornl_13 | V alloy | vanadium_alloy | irradiated | 44 | 427 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,341 | ornl_13 | V alloy | vanadium_alloy | irradiated | 44 | 520 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,342 | ornl_13 | V alloy | vanadium_alloy | irradiated | 44 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,343 | ornl_13 | V alloy | vanadium_alloy | irradiated | 15 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.6 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,346 | ornl_13 | V-5Cr-5Ti | vanadium_alloy | irradiated | null | 550 | null | null | null | 25 | Mechanical Tensile | null | null | 5 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,347 | ornl_13 | V-5Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 430 | 514 | 34.1 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,348 | ornl_13 | V-5Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 441 | 544 | 35 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,350 | ornl_13 | V-10Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 594 | 645 | 39.1 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,351 | ornl_13 | V-12.5Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 591 | 679 | 35.8 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,352 | ornl_13 | V-12.5Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 560 | 656 | 34.1 | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,353 | ornl_13 | V-5Cr-5Ti | vanadium_alloy | irradiated | null | 700 | null | null | null | null | Mechanical Tensile | 499 | 603 | 27.5 | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,354 | ornl_13 | V-10Cr-5Ti | vanadium_alloy | irradiated | null | 700 | null | null | null | null | Mechanical Tensile | 503 | 599 | 27.5 | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,355 | ornl_13 | V-12.5Cr-5Ti | vanadium_alloy | irradiated | null | 700 | null | null | null | null | Mechanical Tensile | 606 | 702 | 20.8 | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,356 | ornl_13 | V-5Cr-5Ti | vanadium_alloy | irradiated | null | 500 | null | null | null | null | Mechanical Tensile | 507 | 583 | 19.8 | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,357 | ornl_13 | V-10Cr-5Ti | vanadium_alloy | irradiated | null | 500 | null | null | null | null | Mechanical Tensile | 583 | 660 | 21.5 | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,358 | ornl_13 | V-12.5Cr-5Ti | vanadium_alloy | irradiated | null | 550 | null | null | null | null | Mechanical Tensile | 591 | 699 | 21.4 | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,359 | ornl_13 | V-10Cr-5Ti | vanadium_alloy | irradiated | null | 600 | null | null | null | null | Mechanical Tensile | 537 | 629 | 17.8 | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,360 | ornl_13 | V-12.5Cr-5Ti | vanadium_alloy | irradiated | null | 600 | null | null | null | null | Mechanical Tensile | 580 | 672 | 20.8 | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,363 | ornl_13 | V-12.5Cr-5Ti | vanadium_alloy | irradiated | null | 700 | null | null | null | null | Mechanical Tensile | 637 | null | 9.6 | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,364 | ornl_13 | V-5Cr-5Ti | vanadium_alloy | irradiated | null | 700 | null | null | null | 700 | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,365 | ornl_13 | V-5Cr-5Ti | vanadium_alloy | irradiated | null | 500 | null | null | null | 500 | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,366 | ornl_13 | V-5Cr-5Ti | vanadium_alloy | irradiated | null | 500 | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,367 | ornl_13 | V-10Cr-5Ti | vanadium_alloy | irradiated | null | 500 | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,368 | ornl_13 | V-12.5Cr-5Ti | vanadium_alloy | unirradiated | null | 500 | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,369 | ornl_13 | Cu-5Ni | copper_alloy | irradiated | null | 400 | MOTA 2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.91 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,370 | ornl_13 | Cu-5Ni (40% cold worked) | copper_alloy | irradiated | null | 400 | MOTA 2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.37 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,371 | ornl_13 | Cu-5Ni (high dose) | copper_alloy | irradiated | null | 400 | MOTA 2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 30.1 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,372 | ornl_13 | pure copper | copper_alloy | irradiated | null | 400 | MOTA 2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 24.4 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,374 | ornl_13 | Cu-5Mn | copper_alloy | irradiated | null | 400 | MOTA 2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,375 | ornl_13 | MARZ copper | copper_alloy | irradiated | 34 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,376 | ornl_13 | MARZ copper | copper_alloy | irradiated | 151 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,377 | ornl_13 | GlidCop CuA120 | copper_alloy | irradiated | 34 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,378 | ornl_13 | GlidCop CuA125 | copper_alloy | irradiated | 151 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,379 | ornl_13 | CuAl20 | copper_alloy | irradiated | 150 | null | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,380 | ornl_13 | CuAl20 | copper_alloy | unirradiated | 0 | null | null | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,381 | ornl_13 | CuAl20 | copper_alloy | irradiated | 50 | null | null | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | 2.8 |
4,382 | ornl_13 | CuAl20 | copper_alloy | irradiated | 100 | null | null | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | 3.2 |
4,383 | ornl_13 | CuAl20 | copper_alloy | irradiated | 150 | null | null | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | 3.5 |
4,385 | ornl_13 | CuAl25 | copper_alloy | irradiated | 50 | null | null | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | 3.2 |
4,386 | ornl_13 | CuAl25 | copper_alloy | irradiated | 100 | null | null | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | 3.8 |
4,387 | ornl_13 | CuAl25 | copper_alloy | irradiated | 150 | null | null | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | 4.2 |
4,388 | ornl_13 | MARZ Copper | copper_alloy | irradiated | 0 | null | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,389 | ornl_13 | MARZ Copper | copper_alloy | irradiated | 100 | null | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | 4.5 |
4,390 | ornl_13 | CuAl25 | copper_alloy | irradiated | 63 | 400 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,391 | ornl_13 | Pure Cu | copper_alloy | irradiated | 100 | 411 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 90 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,393 | ornl_13 | OFHC copper | copper_alloy | irradiated | 0.5 | 100 | DR-3 | neutron | null | null | Mechanical Fatigue | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,394 | ornl_13 | CuAl25 | copper_alloy | irradiated | 0.5 | 100 | DR-3 | neutron | null | null | Mechanical Fatigue | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,395 | ornl_13 | Copper alloys | copper_alloy | irradiated | 0.55 | null | PIREX | proton | 100 | null | Mechanical Fatigue | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,396 | ornl_13 | alloy/Y2O3 interface | ceramic_insulator | unirradiated | null | 927 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,397 | ornl_13 | Type 316NG SS | austenitic_steel | unirradiated | null | null | null | null | null | 60 | Mechanical Tensile | null | null | null | null | null | null | 197 | 532 | 31 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,398 | ornl_13 | Type 316NG SS | austenitic_steel | unirradiated | null | null | null | null | null | 95 | Mechanical Tensile | null | null | null | null | null | null | 194 | 514 | 29 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,399 | ornl_13 | Type 316NG SS | austenitic_steel | unirradiated | null | null | null | null | null | 105 | Mechanical Tensile | null | null | null | null | null | null | 181 | 505 | 29 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,400 | ornl_13 | Type 316NG SS | austenitic_steel | unirradiated | null | null | null | null | null | 150 | Mechanical Tensile | null | null | null | null | null | null | 192 | 478 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,401 | ornl_13 | Type 316NG SS | austenitic_steel | unirradiated | null | null | null | null | null | 190 | Mechanical Tensile | null | null | null | null | null | null | 162 | 467 | 27 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,402 | ornl_13 | Type 316NG SS | austenitic_steel | unirradiated | null | null | null | null | null | 225 | Mechanical Tensile | null | null | null | null | null | null | 170 | 466 | 26 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,403 | ornl_13 | Type 316NG SS | austenitic_steel | unirradiated | null | null | null | null | null | 240 | Mechanical Tensile | null | null | null | null | null | null | 156 | 453 | 26 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,405 | ornl_13 | Ceramic Insulators | ceramic_insulator | irradiated | null | 400 | null | null | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,406 | ornl_13 | reactor grade beryllium | beryllium | irradiated | null | 500 | null | neutron | null | 20 | Mechanical Tensile | null | null | null | null | null | null | 800 | 1,100 | 15 | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,408 | ornl_13 | single crystal beryllium | beryllium | irradiated | null | 500 | SM-2 | neutron | null | 20 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,409 | ornl_13 | thermally extruded beryllium | beryllium | irradiated | null | 500 | SM-2 | neutron | null | 20 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | 400 | null | null | null |
4,410 | ornl_13 | hot pressed beryllium | beryllium | irradiated | null | 500 | SM-2 | neutron | null | 20 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | 56 | null | null | null |
4,411 | ornl_13 | beryllium | beryllium | irradiated | null | 650 | null | neutron | null | 20 | Mechanical Tensile | 480 | 1,250 | 18 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,412 | ornl_13 | beryllium | beryllium | irradiated | null | 650 | null | neutron | null | 650 | Mechanical Tensile | 320 | 600 | 14 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,413 | ornl_13 | beryllium (single crystal) | beryllium | irradiated | null | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,414 | ornl_13 | beryllium (hot pressed) | beryllium | irradiated | null | 700 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 9 | null | null | null | 0.8 | false | ornl_extraction | 56 | null | null | null |
4,415 | ornl_13 | beryllium (hot pressed) | beryllium | irradiated | null | 750 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 13 | null | null | null | 0.8 | false | ornl_extraction | 56 | null | null | null |
4,416 | ornl_13 | beryllium (thermally extruded) | beryllium | irradiated | null | 800 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4 | null | null | null | 0.8 | false | ornl_extraction | 400 | null | null | null |
4,417 | ornl_13 | beryllium | beryllium | irradiated | null | 40 | MIR | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.3 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,418 | ornl_13 | beryllium | beryllium | irradiated | null | 700 | SM-2 | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 15 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,419 | ornl_13 | un-doped sapphire single crystal | ceramic_insulator | irradiated | null | 400 | LAMPF | proton | null | 400 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,420 | ornl_13 | 99.5-grade Sumitomo alumina | ceramic_insulator | irradiated | null | 500 | LAMPF | proton | null | 500 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,421 | ornl_13 | high purity copper TEM disks | copper_alloy | irradiated | null | 640 | LAMPF | proton | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,422 | ornl_13 | Dielectric-coated silica mirrors | ceramic_insulator | irradiated | null | 100 | EBRII | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,424 | ornl_14 | Pure Copper | copper_alloy | irradiated | 35.9 | 520 | FFTF-MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,425 | ornl_14 | Pure Copper | copper_alloy | irradiated | 13.6 | 600 | FFTF-MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,427 | ornl_14 | Pure Nickel | nickel_alloy | irradiated | 31.8 | 600 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,429 | ornl_14 | Pure molybdenum | refractory_metal | irradiated | 111 | null | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,431 | ornl_14 | type 316 stainless steel | austenitic_steel | irradiated | 4.2 | 402.5 | fast reactor | neutron | 3 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,432 | ornl_14 | austenitic stainless steel | austenitic_steel | irradiated | 10 | 500 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,433 | ornl_14 | ITER first wall/blanket candidate materials | other | irradiated | 3 | 60 | null | neutron | null | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,434 | ornl_14 | W | tungsten | irradiated | 34 | 423 | FFTF/MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,435 | ornl_14 | W | tungsten | irradiated | 34 | 600 | FFTF/MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,437 | ornl_14 | DHCE capsules | vanadium_alloy | irradiated | 29 | null | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,439 | ornl_14 | HfO2-strengthened alloy | copper_alloy | irradiated | 150 | 415 | Fast Flux Test Facility (FFTF) | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,440 | ornl_14 | copper alloys | copper_alloy | irradiated | 12.7 | 375 | MOTA 2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,441 | ornl_14 | copper alloys | copper_alloy | irradiated | 21.2 | 375 | MOTA 2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,442 | ornl_14 | copper alloys | copper_alloy | irradiated | 48 | 423 | MOTA 2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.