record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
5,440 | ornl_15 | 316 annealed | austenitic_steel | irradiated | 3 | null | null | neutron | null | 22 | Mechanical Fracture | 275 | 575 | null | null | 393 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,441 | ornl_15 | 316 annealed | austenitic_steel | irradiated | 3 | null | null | neutron | null | 90 | Mechanical Fracture | 230 | 500 | null | null | 422 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,442 | ornl_15 | 316 annealed | austenitic_steel | irradiated | 3 | 85 | null | neutron | null | 90 | Mechanical Fracture | 690 | 695 | null | null | 369 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,443 | ornl_15 | 316 cold-worked | austenitic_steel | irradiated | 3 | null | null | neutron | null | 90 | Mechanical Fracture | 675 | 110 | null | null | 317 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,446 | ornl_15 | PCA annealed | austenitic_steel | irradiated | 3 | null | null | neutron | null | 25 | Mechanical Fracture | 255 | 580 | null | null | 360 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,448 | ornl_15 | PCA annealed | austenitic_steel | irradiated | 3 | null | null | neutron | null | 200 | Mechanical Fracture | 215 | 490 | null | null | 299 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,450 | ornl_15 | PCA annealed | austenitic_steel | irradiated | 3 | 70 | null | neutron | null | 100 | Mechanical Fracture | 715 | 740 | null | null | 239 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,452 | ornl_15 | PCA annealed | austenitic_steel | irradiated | 3 | 270 | null | neutron | null | 250 | Mechanical Fracture | 600 | 670 | null | null | 148 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,453 | ornl_15 | PCA old-worked | austenitic_steel | irradiated | 3 | null | null | neutron | null | 22 | Mechanical Fracture | 675 | 725 | null | null | 262 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,454 | ornl_15 | PCA old-worked | austenitic_steel | irradiated | 3 | null | null | neutron | null | 90 | Mechanical Fracture | 655 | 705 | null | null | 234 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,455 | ornl_15 | PCA old-worked | austenitic_steel | irradiated | 3 | 90 | null | neutron | null | 90 | Mechanical Fracture | 925 | 950 | null | null | 177 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,456 | ornl_15 | PCA weld | austenitic_steel | irradiated | 3 | null | null | neutron | null | 90 | Mechanical Fracture | 240 | 525 | null | null | 431 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,457 | ornl_15 | PCA weld | austenitic_steel | irradiated | 3 | 90 | null | neutron | null | 90 | Mechanical Fracture | 715 | 740 | null | null | 242 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,458 | ornl_15 | PCA weld | austenitic_steel | irradiated | 3 | 270 | null | neutron | null | 250 | Mechanical Fracture | 600 | 670 | null | null | 206 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,459 | ornl_15 | PCA EB weld | austenitic_steel | irradiated | 3 | 85 | null | neutron | null | 90 | Mechanical Fracture | 715 | 140 | null | null | 405 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,461 | ornl_15 | JS316 annealed | austenitic_steel | irradiated | 3 | 80 | null | neutron | null | 90 | Mechanical Fracture | 690 | 695 | null | null | 170 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,463 | ornl_15 | JS316 old-worked | austenitic_steel | irradiated | 3 | null | null | neutron | null | 90 | Mechanical Fracture | 715 | 770 | null | null | 85 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,464 | ornl_15 | JS316 old-worked | austenitic_steel | irradiated | 3 | 80 | null | neutron | null | 90 | Mechanical Fracture | 850 | 865 | null | null | 62 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,465 | ornl_15 | JS316 old-worked | austenitic_steel | irradiated | 3 | 270 | null | neutron | null | 250 | Mechanical Fracture | 825 | 860 | null | null | 60 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,468 | ornl_15 | cold-worked austenitic steels | other | irradiated | 10 | 60 | null | neutron | null | null | Mechanical Tensile | 850 | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,472 | ornl_15 | JPCA annealed material | austenitic_steel | irradiated | null | null | null | neutron | null | 250 | Mechanical Fracture | null | null | null | null | 100 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
5,474 | ornl_15 | US316 material | austenitic_steel | irradiated | null | null | null | neutron | null | 90 | Mechanical Fracture | null | null | null | null | 65 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
5,476 | ornl_15 | EC316L SA | austenitic_steel | unirradiated | 0 | 90 | null | null | null | 90 | Mechanical Tensile | null | null | null | null | null | null | 325 | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,477 | ornl_15 | EC316L SA | austenitic_steel | irradiated | 3 | 90 | null | neutron | null | 90 | Mechanical Tensile | 625 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,478 | ornl_15 | JPCA SA | austenitic_steel | unirradiated | 0 | 90 | null | null | null | 90 | Mechanical Tensile | null | null | null | null | null | null | 310 | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,481 | ornl_15 | JPCA CW | austenitic_steel | irradiated | 3 | 90 | null | neutron | null | 90 | Mechanical Tensile | 975 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,482 | ornl_15 | EC316L | austenitic_steel | unirradiated | 0 | null | null | null | null | 25 | Mechanical Fracture | null | null | null | null | 390 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,483 | ornl_15 | EC316L | austenitic_steel | unirradiated | 0 | null | null | null | null | 100 | Mechanical Fracture | null | null | null | null | 410 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,484 | ornl_15 | EC316L | austenitic_steel | unirradiated | 0 | null | null | null | null | 200 | Mechanical Fracture | null | null | null | null | 360 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,485 | ornl_15 | EC316L | austenitic_steel | irradiated | 3 | 90 | null | neutron | null | 25 | Mechanical Fracture | null | null | null | null | 385 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,486 | ornl_15 | EC316L | austenitic_steel | irradiated | 3 | 90 | null | neutron | null | 100 | Mechanical Fracture | null | null | null | null | 360 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,487 | ornl_15 | EC316L | austenitic_steel | irradiated | 3 | 90 | null | neutron | null | 200 | Mechanical Fracture | null | null | null | null | 300 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,488 | ornl_15 | EC316L | austenitic_steel | irradiated | 3 | 250 | null | neutron | null | 250 | Mechanical Fracture | null | null | null | null | 260 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,489 | ornl_15 | JPCA | austenitic_steel | unirradiated | 0 | null | null | null | null | 25 | Mechanical Fracture | null | null | null | null | 370 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,490 | ornl_15 | JPCA | austenitic_steel | unirradiated | 0 | null | null | null | null | 100 | Mechanical Fracture | null | null | null | null | 375 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,491 | ornl_15 | JPCA | austenitic_steel | unirradiated | 0 | null | null | null | null | 200 | Mechanical Fracture | null | null | null | null | 300 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,493 | ornl_15 | JPCA | austenitic_steel | irradiated | 3 | 90 | null | neutron | null | 100 | Mechanical Fracture | null | null | null | null | 250 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,494 | ornl_15 | JPCA | austenitic_steel | irradiated | 3 | 90 | null | neutron | null | 200 | Mechanical Fracture | null | null | null | null | 200 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,495 | ornl_15 | austenitic stainless steels | austenitic_steel | irradiated | 3 | 60 | HFIR | neutron | null | 20 | Mechanical Fracture | null | null | null | null | 150 | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,496 | ornl_15 | austenitic stainless steels | austenitic_steel | irradiated | 3 | 125 | HFIR | neutron | null | 250 | Mechanical Fracture | null | null | null | null | 400 | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,497 | ornl_15 | austenitic stainless steels | austenitic_steel | irradiated | 3 | 250 | HFIR | neutron | null | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,499 | ornl_15 | SA/BM | other | irradiated | 15 | 300 | HFIR | neutron | null | 300 | Mechanical Tensile | 809 | 845 | 12.3 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,501 | ornl_15 | SA/BM | other | irradiated | 8 | 400 | HFIR | neutron | null | 400 | Mechanical Tensile | 591 | 662 | 14.2 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,502 | ornl_15 | SA/BM | other | irradiated | 18 | 400 | HFIR | neutron | null | 400 | Mechanical Tensile | 785 | 789 | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,503 | ornl_15 | SA/BM | other | irradiated | 18 | 500 | HFIR | neutron | null | 500 | Mechanical Tensile | 470 | 562 | 16.5 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,504 | ornl_15 | SA/BM | other | irradiated | 10 | 500 | HFIR | neutron | null | 500 | Mechanical Tensile | 500 | 611 | 15.8 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,505 | ornl_15 | SA/BM | other | irradiated | 10 | 600 | HFIR | neutron | null | 600 | Mechanical Tensile | 363 | 467 | 19.7 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,508 | ornl_15 | SA/BM | other | unirradiated | 0 | null | null | null | null | 600 | Mechanical Tensile | null | null | null | null | null | null | 194 | 451 | 46.7 | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,509 | ornl_15 | CW/BM | other | irradiated | 18 | 500 | HFIR | neutron | null | 500 | Mechanical Tensile | 655 | 743 | 13.8 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,510 | ornl_15 | CW/BM | other | unirradiated | 0 | null | null | null | null | 500 | Mechanical Tensile | null | null | null | null | null | null | 547 | 612 | 15.7 | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,511 | ornl_15 | SA/EB/WM | other | irradiated | 15 | 300 | HFIR | neutron | null | 300 | Mechanical Tensile | 783 | 787 | 10.7 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,512 | ornl_15 | SA/EB/WM | other | irradiated | 18 | 400 | HFIR | neutron | null | 400 | Mechanical Tensile | 563 | 645 | 14.5 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,514 | ornl_15 | SA/EB/WM | other | irradiated | 10 | 400 | HFIR | neutron | null | 400 | Mechanical Tensile | 443 | 518 | 11.3 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,516 | ornl_15 | SA/EB/WM | other | irradiated | 10 | 600 | HFIR | neutron | null | 600 | Mechanical Tensile | 337 | 388 | 2.8 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,517 | ornl_15 | SA/EB/WM | other | unirradiated | 0 | null | null | null | null | 300 | Mechanical Tensile | null | null | null | null | null | null | 257 | 455 | 39.7 | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,518 | ornl_15 | SA/EB/WM | other | unirradiated | 0 | null | null | null | null | 400 | Mechanical Tensile | null | null | null | null | null | null | 251 | 464 | 42 | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,519 | ornl_15 | SA/EB/WM | other | unirradiated | 0 | null | null | null | null | 500 | Mechanical Tensile | null | null | null | null | null | null | 246 | 441 | 45.3 | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,520 | ornl_15 | SA/EB/WM | other | unirradiated | 0 | null | null | null | null | 600 | Mechanical Tensile | null | null | null | null | null | null | 230 | 428 | 39 | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,521 | ornl_15 | SA/EB/WJ | other | irradiated | 15 | 300 | HFIR | neutron | null | 300 | Mechanical Tensile | 728 | 746 | 12.3 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,522 | ornl_15 | SA/EB/WJ | other | irradiated | 17 | 400 | HFIR | neutron | null | 400 | Mechanical Tensile | 679 | 692 | 6.8 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,523 | ornl_15 | SA/EB/WJ | other | irradiated | 18 | 500 | HFIR | neutron | null | 500 | Mechanical Tensile | 427 | 498 | 14 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,524 | ornl_15 | SA/EB/WJ | other | irradiated | 10 | 600 | HFIR | neutron | null | 600 | Mechanical Tensile | 335 | 416 | 14.6 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,525 | ornl_15 | SA/EB/WJ | other | unirradiated | 0 | null | null | null | null | 300 | Mechanical Tensile | null | null | null | null | null | null | 275 | 440 | 16 | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,526 | ornl_15 | SA/EB/WJ | other | unirradiated | 0 | null | null | null | null | 400 | Mechanical Tensile | null | null | null | null | null | null | 271 | 435 | 17.3 | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,527 | ornl_15 | SA/EB/WJ | other | unirradiated | 0 | null | null | null | null | 500 | Mechanical Tensile | null | null | null | null | null | null | 250 | 408 | 17.3 | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,528 | ornl_15 | SA/EB/WJ | other | unirradiated | 0 | null | null | null | null | 600 | Mechanical Tensile | null | null | null | null | null | null | 247 | 401 | 17.3 | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,529 | ornl_15 | SA/TIG/WM | other | irradiated | 16 | 400 | HFIR | neutron | null | 400 | Mechanical Tensile | 680 | 689 | 8.7 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,530 | ornl_15 | SA/TIG/WM | other | irradiated | 16 | 500 | HFIR | neutron | null | 500 | Mechanical Tensile | 610 | 622 | 6.8 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,532 | ornl_15 | SA/TIG/WM | other | unirradiated | 0 | null | null | null | null | 500 | Mechanical Tensile | null | null | null | null | null | null | 311 | 288 | 17.7 | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,533 | ornl_15 | SA/TIG/WJ | other | irradiated | 16 | 400 | HFIR | neutron | null | 400 | Mechanical Tensile | 665 | 673 | 7 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,535 | ornl_15 | SA/TIG/WJ | other | unirradiated | 0 | null | null | null | null | 400 | Mechanical Tensile | null | null | null | null | null | null | 348 | 448 | 19.3 | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,536 | ornl_15 | SA/TIG/WJ | other | unirradiated | 0 | null | null | null | null | 500 | Mechanical Tensile | null | null | null | null | null | null | 332 | 423 | 16.7 | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,538 | ornl_15 | SA/Ti-insert EB/WM | other | unirradiated | 0 | null | null | null | null | 600 | Mechanical Tensile | null | null | null | null | null | null | 175 | 403 | 56 | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,539 | ornl_15 | JPCA SA base metal (BM) | RAFM_steel | irradiated | 18 | 300 | HFIR | neutron | 1,400 | 300 | Mechanical Tensile | 850 | 900 | 18 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,541 | ornl_15 | JPCA SA weld joint (WJ) | RAFM_steel | irradiated | 18 | 600 | HFIR | neutron | 1,400 | 600 | Mechanical Tensile | 450 | 500 | 15 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,542 | ornl_15 | Type 316L SS | RAFM_steel | unirradiated | null | null | null | null | null | 200 | Mechanical Tensile | null | null | null | null | null | null | 170 | 460 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
5,543 | ornl_15 | Type 316L SS | RAFM_steel | unirradiated | null | null | null | null | null | 200 | Mechanical Tensile | null | null | null | null | null | null | 106 | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
5,544 | ornl_15 | Type 316L SS | RAFM_steel | unirradiated | null | null | null | null | null | 20 | Mechanical Tensile | null | null | null | null | null | null | 200 | 500 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
5,545 | ornl_15 | Type 316L SS | RAFM_steel | unirradiated | null | null | null | null | null | 200 | Mechanical Fatigue | null | null | null | null | 16 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
5,546 | ornl_15 | Type 316L SS | RAFM_steel | unirradiated | null | null | null | null | null | 200 | Mechanical Fatigue | null | null | null | null | 16 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
5,547 | ornl_15 | Type 316L SS | RAFM_steel | unirradiated | null | null | null | null | null | 200 | Mechanical Fatigue | null | null | null | null | 16 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
5,548 | ornl_15 | Type 316L SS | RAFM_steel | unirradiated | null | null | null | null | null | 200 | Mechanical Fatigue | null | null | null | null | 16 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
5,552 | ornl_15 | ISPRA-A | RAFM_steel | irradiated | 60.8 | 520 | MOTA-2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.36 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,553 | ornl_15 | ISPRA-A | RAFM_steel | irradiated | 32.3 | 600 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.15 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,554 | ornl_15 | ISPRA-A | RAFM_steel | irradiated | 54.2 | 600 | MOTA-2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.86 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,556 | ornl_15 | ISPRA-B | RAFM_steel | irradiated | 60.3 | 427 | MOTA-2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.08 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,557 | ornl_15 | ISPRA-B | RAFM_steel | irradiated | 36.3 | 520 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.07 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,558 | ornl_15 | ISPRA-B | RAFM_steel | irradiated | 60.8 | 520 | MOTA-2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.04 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,559 | ornl_15 | ISPRA-B | RAFM_steel | irradiated | 32.3 | 600 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.99 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,560 | ornl_15 | ISPRA-B | RAFM_steel | irradiated | 54.2 | 600 | MOTA-2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.37 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,561 | ornl_15 | ISPRA-C | RAFM_steel | irradiated | 36.1 | 423 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.49 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,562 | ornl_15 | ISPRA-C | RAFM_steel | irradiated | 60.3 | 427 | MOTA-2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.71 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,563 | ornl_15 | ISPRA-C | RAFM_steel | irradiated | 36.3 | 520 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.91 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,564 | ornl_15 | ISPRA-C | RAFM_steel | irradiated | 60.8 | 520 | MOTA-2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 11.9 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,565 | ornl_15 | ISPRA-C | RAFM_steel | irradiated | 32.3 | 600 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.96 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,567 | ornl_15 | ISPRA-D | RAFM_steel | irradiated | 36.1 | 423 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.28 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,568 | ornl_15 | ISPRA-D | RAFM_steel | irradiated | 60.3 | 427 | MOTA-2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.55 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,569 | ornl_15 | ISPRA-D | RAFM_steel | irradiated | 36.3 | 520 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.58 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,571 | ornl_15 | ISPRA-D | RAFM_steel | irradiated | 32.3 | 600 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.72 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,572 | ornl_15 | ISPRA-D | RAFM_steel | irradiated | 54.2 | 600 | MOTA-2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.99 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.