record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
5,314 | ornl_15 | Fe-35Ni-15Cr | ferritic_model_alloy | irradiated | null | 500 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,315 | ornl_15 | Fe-35Ni-22Cr | ferritic_model_alloy | irradiated | null | 500 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,317 | ornl_15 | Fe-35Ni-15Cr | ferritic_model_alloy | irradiated | null | 600 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,318 | ornl_15 | Fe-35Ni-22Cr | ferritic_model_alloy | irradiated | null | 600 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,319 | ornl_15 | Fe-15Cr-xNi | austenitic_steel | irradiated | null | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,320 | ornl_15 | Fe-Cr | ferritic_model_alloy | irradiated | null | 400 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | 500,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,321 | ornl_15 | Fe-Cr | ferritic_model_alloy | irradiated | null | 500 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | 20,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,323 | ornl_15 | Fe-Cr | ferritic_model_alloy | irradiated | null | 330 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,324 | ornl_15 | Fe-Cr | ferritic_model_alloy | irradiated | null | 400 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,325 | ornl_15 | Fe-Cr | ferritic_model_alloy | irradiated | null | 500 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,326 | ornl_15 | Fe-Cr | ferritic_model_alloy | irradiated | null | 500 | ORR | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,327 | ornl_15 | V-5Al | vanadium_alloy | irradiated | 15 | 425 | EBR II | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,328 | ornl_15 | V-5Al | vanadium_alloy | irradiated | 31 | 600 | EBR II | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,329 | ornl_15 | V-5Fe | vanadium_alloy | irradiated | 52 | 520 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 100 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,330 | ornl_15 | V-5Fe | vanadium_alloy | irradiated | 34.2 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 93.2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,331 | ornl_15 | V-Cr alloys (10-15% Cr) + Al | vanadium_alloy | irradiated | 80 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 40 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,332 | ornl_15 | V-5Cr | vanadium_alloy | irradiated | 34.2 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 24.6 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,333 | ornl_15 | V-5Cr | vanadium_alloy | irradiated | 45 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 27 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,334 | ornl_15 | V-2Si | vanadium_alloy | irradiated | 45 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 35 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,335 | ornl_15 | V-2Si | vanadium_alloy | irradiated | 45 | 520 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 35 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,341 | ornl_15 | V-5Cr | vanadium_alloy | irradiated | 34.2 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 24.6 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,343 | ornl_15 | V-2Si | vanadium_alloy | irradiated | 45 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 35 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,345 | ornl_15 | V-1Si | vanadium_alloy | irradiated | 34.2 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 18.7 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,346 | ornl_15 | V-12Ni | vanadium_alloy | irradiated | 80 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 15 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,348 | ornl_15 | V-2Ti-Ni | vanadium_alloy | irradiated | 15 | 500 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,349 | ornl_15 | V-2Ti-Ni | vanadium_alloy | irradiated | 31 | 500 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,350 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 14 | 365 | Fast Flux Test Facility | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,352 | ornl_15 | 2.25% Cr steel with 2% W, 0.25% V, and 0.1% C | RAFM_steel | irradiated | 14 | 365 | Fast Flux Test Facility | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,353 | ornl_15 | FIRD steels | RAFM_steel | irradiated | 7 | 365 | Fast Flux Test Facility | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,354 | ornl_15 | 2 1/4CrV | RAFM_steel | irradiated | 13.5 | 365 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,355 | ornl_15 | 2 1/4Cr-1WV | RAFM_steel | irradiated | 13.5 | 365 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,356 | ornl_15 | 2 1/4Cr-2W | RAFM_steel | irradiated | 13.5 | 365 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,357 | ornl_15 | 2 1/4Cr-2WV | RAFM_steel | irradiated | 13.5 | 365 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,359 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 13.5 | 365 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,360 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 13.5 | 365 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,361 | ornl_15 | 12Cr-2WV | RAFM_steel | irradiated | 13.5 | 365 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,363 | ornl_15 | 12Cr-1MoVW | RAFM_steel | irradiated | 13.5 | 365 | null | null | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,364 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 13 | 365 | FFTF | neutron | null | 365 | Mechanical Charpy | null | null | null | null | null | 15 | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,365 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 7 | 365 | FFTF | neutron | null | 365 | Mechanical Charpy | null | null | null | null | null | 4 | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,366 | ornl_15 | 2 1/4CrV | RAFM_steel | irradiated | 13 | 365 | null | null | null | null | Mechanical Charpy | 280 | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,367 | ornl_15 | 2 1/4Cr-1WV | RAFM_steel | irradiated | 13 | 365 | null | null | null | null | Mechanical Charpy | 330 | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,368 | ornl_15 | 2 1/4Cr-2W | RAFM_steel | irradiated | 13 | 365 | null | null | null | null | Mechanical Charpy | 250 | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,369 | ornl_15 | 2 1/4Cr-2WV | RAFM_steel | irradiated | 13 | 365 | null | null | null | null | Mechanical Charpy | 280 | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,370 | ornl_15 | 5Cr-2WV | RAFM_steel | irradiated | 13 | 365 | null | null | null | null | Mechanical Charpy | 210 | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,371 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 7 | 365 | null | null | null | null | Mechanical Charpy | 180 | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,372 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 7 | 365 | null | null | null | null | Mechanical Charpy | 150 | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,373 | ornl_15 | 12Cr-2WV | RAFM_steel | irradiated | 13 | 365 | null | null | null | null | Mechanical Charpy | 320 | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,374 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 7 | 365 | null | null | null | null | Mechanical Charpy | 160 | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,375 | ornl_15 | 12Cr-1MoVW | RAFM_steel | irradiated | 7 | 365 | null | null | null | null | Mechanical Charpy | 350 | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,376 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 200 | 420 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,378 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 200 | 420 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,379 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 200 | 420 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,382 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 200 | 420 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,383 | ornl_15 | L6 (12Cr-1W-6.5Mn) | RAFM_steel | irradiated | 200 | 420 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,384 | ornl_15 | L1 | RAFM_steel | irradiated | 203.2 | null | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,385 | ornl_15 | L2 | RAFM_steel | irradiated | 203.5 | null | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,386 | ornl_15 | L3-UC19 | RAFM_steel | irradiated | 204 | null | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,387 | ornl_15 | L4 | RAFM_steel | irradiated | 204.8 | null | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,388 | ornl_15 | L5 | RAFM_steel | irradiated | 205.7 | null | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,390 | ornl_15 | L7 | RAFM_steel | irradiated | 208.8 | null | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,391 | ornl_15 | L8 | RAFM_steel | irradiated | 204.4 | null | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,392 | ornl_15 | L9 | RAFM_steel | irradiated | 206.9 | null | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,393 | ornl_15 | ferritic alloy | RAFM_steel | irradiated | 200 | null | fusion device | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,395 | ornl_15 | HT-9 | RAFM_steel | irradiated | 110 | null | FFTF/MOTA | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,398 | ornl_15 | HT9 | RAFM_steel | irradiated | 11 | 407 | MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.1 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,399 | ornl_15 | HT9 | RAFM_steel | irradiated | 34 | 425 | MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,400 | ornl_15 | HT9 | RAFM_steel | irradiated | 26 | 406 | MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,401 | ornl_15 | HT9 | RAFM_steel | irradiated | 37 | 403 | MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,402 | ornl_15 | HT9 | RAFM_steel | irradiated | 40 | 406 | MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,403 | ornl_15 | HT9 | RAFM_steel | irradiated | 35 | 420 | MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,404 | ornl_15 | HT9 | RAFM_steel | irradiated | 24 | 433 | MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,405 | ornl_15 | HT9 | RAFM_steel | irradiated | 50 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,407 | ornl_15 | HT9 | RAFM_steel | irradiated | 150 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,408 | ornl_15 | HT9 | RAFM_steel | irradiated | 200 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,410 | ornl_15 | HT9 | RAFM_steel | irradiated | 200 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,411 | ornl_15 | HT9 | RAFM_steel | irradiated | 200 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,412 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 50 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,413 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 100 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,414 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 150 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,416 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 200 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,417 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 200 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,418 | ornl_15 | HT9 | RAFM_steel | irradiated | 208 | 400 | null | neutron | null | 400 | Swelling | null | null | null | null | null | null | null | null | null | 1.2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,419 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 208 | 400 | null | neutron | null | 400 | Swelling | null | null | null | null | null | null | null | null | null | -2.3 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,421 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 200 | null | null | null | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,422 | ornl_15 | HT9 | RAFM_steel | irradiated | 208 | 400 | null | neutron | null | 400 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,423 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | null | 400 | null | neutron | null | 400 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,425 | ornl_15 | 300 series austenitic stainless steel | austenitic_steel | irradiated | 3 | 125 | High Flux Isotope Reactor | neutron | 50 | 250 | Mechanical Fracture | null | null | null | null | 400 | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,426 | ornl_15 | austenitic stainless steels | austenitic_steel | irradiated | null | 200 | null | neutron | null | 200 | Mechanical Tensile | null | null | 1 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,427 | ornl_15 | EC316L | austenitic_steel | irradiated | 3.2 | 275 | HFIR | neutron | 50 | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,428 | ornl_15 | EC316L | austenitic_steel | irradiated | 3.2 | 92.5 | HFIR | neutron | 50 | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,429 | ornl_15 | 316L annealed | austenitic_steel | unirradiated | null | null | null | null | null | null | Mechanical Fracture | null | null | null | null | 385 | null | 275 | 580 | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,430 | ornl_15 | 316L annealed | austenitic_steel | unirradiated | null | null | null | null | null | null | Mechanical Fracture | null | null | null | null | 407 | null | 230 | 510 | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,431 | ornl_15 | 316L annealed | austenitic_steel | unirradiated | null | null | null | null | null | null | Mechanical Fracture | null | null | null | null | 353 | null | 190 | 480 | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,432 | ornl_15 | 316L annealed | austenitic_steel | unirradiated | null | null | null | null | null | null | Mechanical Fracture | null | null | null | null | 387 | null | 600 | 690 | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,434 | ornl_15 | 316L annealed | austenitic_steel | irradiated | 3 | 75 | null | neutron | null | 100 | Mechanical Fracture | 610 | 675 | null | null | 350 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,435 | ornl_15 | 316L annealed | austenitic_steel | irradiated | 3 | 75 | null | neutron | null | 200 | Mechanical Fracture | 600 | 675 | null | null | 299 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,436 | ornl_15 | 316L annealed | austenitic_steel | irradiated | 3 | 270 | null | neutron | null | 250 | Mechanical Fracture | 575 | 700 | null | null | 251 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,437 | ornl_15 | 316L annealed | austenitic_steel | irradiated | 3 | 90 | null | neutron | null | 90 | Mechanical Fracture | 610 | 675 | null | null | 393 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,438 | ornl_15 | 316L weld | austenitic_steel | unirradiated | null | null | null | null | null | 90 | Mechanical Fracture | null | null | null | null | 355 | null | 230 | 510 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
5,439 | ornl_15 | 316L weld | austenitic_steel | irradiated | 3 | 80 | null | neutron | null | 90 | Mechanical Fracture | 610 | 670 | null | null | 32 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.