record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
5,573 | ornl_15 | ISPRA-E | RAFM_steel | irradiated | 36.1 | 423 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.52 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,574 | ornl_15 | ISPRA-E | RAFM_steel | irradiated | 60.3 | 427 | MOTA-2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.91 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,575 | ornl_15 | ISPRA-E | RAFM_steel | irradiated | 36.3 | 520 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.08 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,576 | ornl_15 | ISPRA-E | RAFM_steel | irradiated | 60.8 | 520 | MOTA-2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 8.4 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,577 | ornl_15 | ISPRA-E | RAFM_steel | irradiated | 32.3 | 600 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.58 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,578 | ornl_15 | ISPRA-E | RAFM_steel | irradiated | 54.2 | 600 | MOTA-2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.66 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,579 | ornl_15 | AMCR | RAFM_steel | irradiated | 36.1 | 423 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.96 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,580 | ornl_15 | AMCR | RAFM_steel | irradiated | 60.3 | 427 | MOTA-2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.16 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,581 | ornl_15 | AMCR | RAFM_steel | irradiated | 36.3 | 520 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.71 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,583 | ornl_15 | AMCR | RAFM_steel | irradiated | 32.3 | 600 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.19 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,584 | ornl_15 | AMCR | RAFM_steel | irradiated | 54.2 | 600 | MOTA-2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.49 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,585 | ornl_15 | AMCR | RAFM_steel | irradiated | 60 | 425 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,586 | ornl_15 | Ispra variant C | RAFM_steel | irradiated | 60 | 425 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,587 | ornl_15 | AMCR | RAFM_steel | irradiated | 60 | 600 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,588 | ornl_15 | Ispra variant C | RAFM_steel | irradiated | 60 | 520 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 11.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,589 | ornl_15 | Ispra variant E | RAFM_steel | irradiated | 60 | 520 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 8.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,590 | ornl_15 | W | tungsten | irradiated | 34 | 423 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -2.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,592 | ornl_15 | PCA (titanium-modified austenitic stainless steel) | RAFM_steel | irradiated | 15 | 472.5 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,593 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | irradiated | 37 | 420 | FFTF | neutron | null | 25 | Mechanical Tensile | null | null | 7 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | 30 | null | null | null |
5,594 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 37 | 420 | FFTF | neutron | null | 25 | Mechanical Tensile | null | null | 5 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,595 | ornl_15 | V-14Cr-5Ti | vanadium_alloy | irradiated | 37 | 420 | FFTF | neutron | null | 25 | Mechanical Tensile | null | null | 3 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | 30 | null | null | null |
5,596 | ornl_15 | V-18Ti | vanadium_alloy | irradiated | 37 | 420 | FFTF | neutron | null | 25 | Mechanical Tensile | null | null | 11 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | 30 | null | null | null |
5,597 | ornl_15 | V-14Cr-5Ti | vanadium_alloy | irradiated | 37 | 420 | null | neutron | null | 420 | Mechanical Tensile | null | null | 3 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | 30 | null | null | null |
5,598 | ornl_15 | V-18Ti | vanadium_alloy | irradiated | 37 | 600 | null | neutron | null | 600 | Mechanical Tensile | null | null | 17 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | 30 | null | null | null |
5,599 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | irradiated | 34 | 420 | null | neutron | null | 25 | Mechanical Tensile | null | null | 8 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | 30 | null | null | null |
5,600 | ornl_15 | V-3Ti-1Si | vanadium_alloy | irradiated | 37 | 420 | null | neutron | null | 420 | Mechanical Tensile | null | null | 11 | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,601 | ornl_15 | V-18Ti | vanadium_alloy | irradiated | 43.5 | 420 | FFTF-MOTA | neutron | null | 420 | Mechanical Tensile | null | null | 18 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | 30 | null | null | null |
5,602 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | irradiated | 31 | 420 | FFTF-MOTA | neutron | null | 420 | Mechanical Tensile | null | null | 10 | null | null | 373.15 | null | null | null | 0.3 | null | null | null | 0.9 | false | ornl_extraction | 30 | null | null | null |
5,605 | ornl_15 | V-20Ti (BL-15) | vanadium_alloy | irradiated | 60 | 420 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,606 | ornl_15 | V-20Ti (BL-15) | vanadium_alloy | irradiated | 60 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,608 | ornl_15 | V-15Cr-5Ti (BL-24) | vanadium_alloy | irradiated | 80 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.4 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,609 | ornl_15 | V-10Cr-5Ti | vanadium_alloy | irradiated | 60 | 420 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,610 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | irradiated | 60 | 420 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.3 | null | null | null | 0.8 | false | ornl_extraction | 30 | null | null | null |
5,612 | ornl_15 | V-3Ti-0.25Si | vanadium_alloy | irradiated | 34 | 600 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,613 | ornl_15 | V-5Ti | vanadium_alloy | irradiated | 34 | 420 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,615 | ornl_15 | V-5Ti | vanadium_alloy | irradiated | 34 | 600 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.7 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,616 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | irradiated | 34 | 420 | null | null | null | 25 | Mechanical Tensile | null | null | 8.1 | null | null | 77.15 | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | 30 | null | null | null |
5,617 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | irradiated | 34 | 520 | null | null | null | 25 | Mechanical Tensile | null | null | 10.2 | null | null | 77.15 | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | 30 | null | null | null |
5,618 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | irradiated | 34 | 600 | null | null | null | null | Mechanical Tensile | null | null | null | null | null | 77.15 | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | 30 | null | null | null |
5,619 | ornl_15 | V-3Ti-0.25Si | vanadium_alloy | irradiated | 60 | 420 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,620 | ornl_15 | V-3Ti-0.5Si | vanadium_alloy | irradiated | 60 | 420 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,621 | ornl_15 | V-3Ti-0.25Si | vanadium_alloy | irradiated | 60 | 600 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.6 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,622 | ornl_15 | V-3Ti-0.5Si | vanadium_alloy | irradiated | 60 | 600 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,623 | ornl_15 | V-5Cr-5Ti | vanadium_alloy | irradiated | 120 | 420 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,624 | ornl_15 | V-10Cr-5Ti | vanadium_alloy | irradiated | 120 | 420 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,625 | ornl_15 | V-20Cr-5Ti | vanadium_alloy | irradiated | 120 | 420 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,626 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | irradiated | 120 | 420 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.5 | null | null | null | 0.8 | false | ornl_extraction | 30 | null | null | null |
5,627 | ornl_15 | V-15Cr-5Ti | vanadium_alloy | irradiated | 120 | 420 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,628 | ornl_15 | V-15Cr-5Ti | vanadium_alloy | irradiated | 120 | 600 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.7 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,629 | ornl_15 | V-10Cr-5Ti | vanadium_alloy | irradiated | 120 | 600 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,630 | ornl_15 | V-3Ti-0.25Si | vanadium_alloy | irradiated | 120 | 420 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.6 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,631 | ornl_15 | V-3Ti-0.25Si | vanadium_alloy | irradiated | 120 | 600 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.9 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,632 | ornl_15 | V-3Ti-0.5Si | vanadium_alloy | irradiated | 120 | 420 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.4 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,633 | ornl_15 | 14Cr-16Ni-2.5Mo-2Mn austenitic stainless steel | RAFM_steel | irradiated | 34 | 500 | HFIR | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,634 | ornl_15 | 14Cr-16Ni-2.5Mo-2Mn austenitic stainless steel | RAFM_steel | irradiated | 57 | 500 | HFIR | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.85 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,635 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | irradiated | 34 | 420 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | 30 | null | null | null |
5,636 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | irradiated | 34 | 600 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | 30 | null | null | null |
5,637 | ornl_15 | V-20Ti (without B, BL-16) | vanadium_alloy | irradiated | 114 | 420 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,638 | ornl_15 | V-20Ti (containing B, BL-15) | vanadium_alloy | irradiated | 46 | 420 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,639 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | irradiated | 34 | 420 | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.75 | false | ornl_extraction | 30 | null | 2 | null |
5,640 | ornl_15 | V-5Cr-5Ti-1Al-1Si-0.8Y | vanadium_alloy | irradiated | 51 | 406 | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.27 | null | null | null | 0.75 | false | ornl_extraction | null | null | null | null |
5,641 | ornl_15 | V alloy | vanadium_alloy | irradiated | 60 | 600 | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 45 | null | null | null | 0.75 | false | ornl_extraction | null | null | null | null |
5,642 | ornl_15 | V alloy | vanadium_alloy | irradiated | 45 | 600 | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 25 | null | null | null | 0.75 | false | ornl_extraction | null | null | null | null |
5,643 | ornl_15 | V-20Ti (BL-16) | vanadium_alloy | irradiated | 114 | 420 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.4 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,644 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | irradiated | 34 | 420 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.3 | null | null | null | 0.8 | false | ornl_extraction | 30 | null | null | null |
5,645 | ornl_15 | V-20Ti (BL-15) boron-doped | vanadium_alloy | irradiated | 46 | 420 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,646 | ornl_15 | V-20Ti (BL-16) without boron | vanadium_alloy | irradiated | 80 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.3 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,647 | ornl_15 | V on addition of Ti and Cr | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 40 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | 10 | null | null |
5,648 | ornl_15 | V-1Ti | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 357.52 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,649 | ornl_15 | V-3Ti | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 378.65 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,650 | ornl_15 | V-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 382.05 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,653 | ornl_15 | V-14Cr | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 559.82 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,654 | ornl_15 | V-14Cr-1Ti | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 674.01 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,655 | ornl_15 | V-5Cr-3Ti | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 431.31 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,656 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 443.47 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | 30 | null | null | null |
5,657 | ornl_15 | 9Cr steel | RAFM_steel | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 548.53 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,658 | ornl_15 | V-14Cr-5Ti | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 633.38 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | 30 | null | null | null |
5,659 | ornl_15 | V-10Cr-9Ti | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 656.63 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,660 | ornl_15 | V-7Cr-15Ti | vanadium_alloy | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 727.07 | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,661 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | irradiated | 34 | 600 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 73.15 | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | 30 | null | null | null |
5,662 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | irradiated | 28 | 600 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 130 | null | null | 0.8 | false | ornl_extraction | 30 | null | null | null |
5,663 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | irradiated | 34 | 420 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | 30 | null | null | null |
5,664 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | irradiated | 34 | 600 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | 30 | null | null | null |
5,665 | ornl_15 | V-20Ti | vanadium_alloy | irradiated | null | 420 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,666 | ornl_15 | V alloy | vanadium_alloy | irradiated | 24 | null | FFTF/MOTA | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,667 | ornl_15 | V alloy | vanadium_alloy | irradiated | 13 | null | FFTF/MOTA | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,668 | ornl_15 | V alloy | vanadium_alloy | irradiated | 23 | null | FFTF | neutron | 0.02 | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,669 | ornl_15 | V-(3-5)Ti | vanadium_alloy | irradiated | 34 | 513.33 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 73.15 | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | 30 | null | null | null |
5,670 | ornl_15 | V-4Cr-4Ti | vanadium_alloy | irradiated | 34 | 513.33 | null | neutron | null | null | Microstructure | null | null | null | null | null | 73.15 | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | 30 | null | null | null |
5,672 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 45.5 | 510 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 423.15 | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,673 | ornl_15 | V-14Cr-5Ti | vanadium_alloy | irradiated | 41 | 420 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | 30 | null | null | null |
5,674 | ornl_15 | V-14Cr-5Ti | vanadium_alloy | irradiated | 21 | 520 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | 30 | null | null | null |
5,675 | ornl_15 | V-14Cr-5Ti | vanadium_alloy | irradiated | 44 | 600 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | 30 | null | null | null |
5,676 | ornl_15 | V-14Cr-5Ti | vanadium_alloy | irradiated | 114 | 600 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | 30 | null | null | null |
5,677 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 41 | 420 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,678 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 50 | 520 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,679 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 44 | 600 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,680 | ornl_15 | V-5Ti | vanadium_alloy | irradiated | 34 | 427 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,681 | ornl_15 | V-5Ti | vanadium_alloy | irradiated | 24 | 519 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,682 | ornl_15 | V-5Ti | vanadium_alloy | irradiated | 28 | 599 | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.