record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
4,570 | ornl_14 | annealed Fe-17Cr-16Ni | RAFM_steel | irradiated | 36 | 600 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 20 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,571 | ornl_14 | Fe-15Cr-25Ni | austenitic_steel | irradiated | 3.5 | 400 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 1.9 | 100,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,573 | ornl_14 | Fe-15Cr-45Ni | austenitic_steel | irradiated | 3.5 | 400 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 2.3 | 200,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,574 | ornl_14 | Fe-15Cr-50Ni | austenitic_steel | irradiated | 3.5 | 400 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 2.4 | 400,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,575 | ornl_14 | Fe-15Cr-25Ni | austenitic_steel | irradiated | 3.5 | 500 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 9.4 | 4,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,576 | ornl_14 | Fe-15Cr-35Ni | austenitic_steel | irradiated | 3.5 | 500 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 5.6 | 10,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,578 | ornl_14 | Fe-15Cr-50Ni | austenitic_steel | irradiated | 3.5 | 500 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 3.4 | 15,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,580 | ornl_14 | Fe-15Cr-35Ni | austenitic_steel | irradiated | 10.4 | 395 | EBR-II | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 35 | 200,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,581 | ornl_14 | Fe-15Cr-45Ni | austenitic_steel | irradiated | 10.4 | 395 | EBR-II | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 23 | 1,500,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,582 | ornl_14 | Fe-15Cr-50Ni | austenitic_steel | irradiated | 10.4 | 395 | EBR-II | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 25 | 500,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,583 | ornl_14 | Fe-15Cr-Ni alloys | austenitic_steel | irradiated | null | 330 | ORR | neutron | null | null | Mechanical Tensile | 750 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,584 | ornl_14 | Fe-15Cr-Ni alloys | austenitic_steel | irradiated | null | 400 | ORR | neutron | null | null | Mechanical Tensile | 650 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,585 | ornl_14 | Fe-15Cr-Ni alloys | austenitic_steel | irradiated | null | 500 | ORR | neutron | null | null | Mechanical Tensile | 550 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,586 | ornl_14 | Fe-15Cr-Ni alloys | austenitic_steel | irradiated | null | 600 | ORR | neutron | null | null | Mechanical Tensile | 450 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,587 | ornl_14 | Fe-15Cr-Ni alloys | austenitic_steel | irradiated | null | 330 | EBR-II | neutron | null | null | Mechanical Tensile | 650 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,589 | ornl_14 | Fe-15Cr-Ni alloys | austenitic_steel | irradiated | null | 500 | EBR-II | neutron | null | null | Mechanical Tensile | 350 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,590 | ornl_14 | Fe-15Cr-Ni alloys | austenitic_steel | irradiated | null | 600 | EBR-II | neutron | null | null | Mechanical Tensile | 150 | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,592 | ornl_14 | 99.995% Nickel | nickel_alloy | irradiated | 31.1 | 425 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.1 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,593 | ornl_14 | 99.995% Nickel (30% Cold-Worked) | nickel_alloy | irradiated | 12 | 425 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.8 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,594 | ornl_14 | 99.995% Nickel (30% Cold-Worked) | nickel_alloy | irradiated | 31.1 | 425 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.1 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,597 | ornl_14 | Ni-Si alloy | other | irradiated | 14 | 425 | sodium coolant reactor | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 6.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,598 | ornl_14 | Ni-Si alloy | other | irradiated | 14 | 500 | sodium coolant reactor | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,601 | ornl_14 | Ni-Al alloy | other | irradiated | 14 | 500 | sodium coolant reactor | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.8 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,603 | ornl_14 | Ni | nickel_alloy | irradiated | 14 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.7 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,604 | ornl_14 | Ni | nickel_alloy | irradiated | 14 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 6.01 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,605 | ornl_14 | Ni | nickel_alloy | irradiated | 14 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 6.2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,606 | ornl_14 | Ni | nickel_alloy | irradiated | 31.1 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 7.48 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,607 | ornl_14 | Ni | nickel_alloy | irradiated | 31.1 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 9.14 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,608 | ornl_14 | Ni | nickel_alloy | irradiated | 14 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.73 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,609 | ornl_14 | Ni | nickel_alloy | irradiated | 14 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.58 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,610 | ornl_14 | Ni | nickel_alloy | irradiated | 14 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.83 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,611 | ornl_14 | Ni | nickel_alloy | irradiated | 31.8 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 6.3 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,612 | ornl_14 | Ni | nickel_alloy | irradiated | 12 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.39 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,613 | ornl_14 | Ni | nickel_alloy | irradiated | 12 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.76 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,614 | ornl_14 | Ni | nickel_alloy | irradiated | 12 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,616 | ornl_14 | Ni | nickel_alloy | irradiated | 31.8 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 7.43 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,618 | ornl_14 | Ni-5Al | other | irradiated | 14 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.21 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,619 | ornl_14 | Ni-5Al | other | irradiated | 31.1 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 6.92 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,620 | ornl_14 | Ni-5Al | other | irradiated | 31.1 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.63 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,621 | ornl_14 | Ni-5Al | other | irradiated | 14 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.46 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,622 | ornl_14 | Ni-5Al | other | irradiated | 14 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.36 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,623 | ornl_14 | Ni-5Al | other | irradiated | 31.8 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.19 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,624 | ornl_14 | Ni-5Al | other | irradiated | 31.8 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.05 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,625 | ornl_14 | Ni-5Al | other | irradiated | 14 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.39 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,628 | ornl_14 | Ni-5Si | other | irradiated | 14 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.48 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,629 | ornl_14 | Ni-5Si | other | irradiated | 14 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.11 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,630 | ornl_14 | Ni-5Si | other | irradiated | 14 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.06 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,632 | ornl_14 | Ni-5Si | other | irradiated | 31.1 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.28 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,634 | ornl_14 | Ni-5Si | other | irradiated | 14 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.12 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,635 | ornl_14 | Ni-5Si | other | irradiated | 14 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,636 | ornl_14 | Ni-5Si | other | irradiated | 31.8 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.21 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,637 | ornl_14 | Ni-5Si | other | irradiated | 31.8 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.42 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,638 | ornl_14 | Ni-5Si | other | irradiated | 12 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.22 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,640 | ornl_14 | Ni-5Si | other | irradiated | 31 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.06 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,641 | ornl_14 | Ni-5Si | other | irradiated | 31 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.15 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,642 | ornl_14 | Ni-8Si | other | irradiated | 14 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.87 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,644 | ornl_14 | Ni-8Si | other | irradiated | 14 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.06 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,645 | ornl_14 | Ni-8Si | other | irradiated | 31.1 | 425 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.17 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,648 | ornl_14 | Ni-8Si | other | irradiated | 14 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.12 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,649 | ornl_14 | Ni-8Si | other | irradiated | 31.8 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.52 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,650 | ornl_14 | Ni-8Si | other | irradiated | 12 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.13 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,651 | ornl_14 | Ni-8Si | other | irradiated | 12 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.9 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,652 | ornl_14 | Ni-8Si | other | irradiated | 12 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.37 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,653 | ornl_14 | pure nickel | nickel_alloy | irradiated | 10 | 425 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,655 | ornl_14 | pure nickel | nickel_alloy | irradiated | 30 | 425 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 9 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,656 | ornl_14 | pure nickel | nickel_alloy | irradiated | 40 | 425 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 10 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,657 | ornl_14 | pure nickel | nickel_alloy | irradiated | 40 | 550 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 9.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,658 | ornl_14 | pure nickel | nickel_alloy | irradiated | 40 | 500 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 8 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,659 | ornl_14 | pure nickel | nickel_alloy | irradiated | 40 | 600 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 6.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,660 | ornl_14 | pure nickel | nickel_alloy | irradiated | 40 | 425 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,661 | ornl_14 | pure nickel | nickel_alloy | irradiated | 40 | 600 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,663 | ornl_14 | Ni-5Al | other | irradiated | 35 | 500 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,664 | ornl_14 | Ni-5Al | other | irradiated | 35 | 600 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,665 | ornl_14 | HT9 | RAFM_steel | irradiated | 208 | 400 | FFTF | neutron | null | 400 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,666 | ornl_14 | 9Cr steel | RAFM_steel | irradiated | 208 | 400 | FFTF | neutron | null | 400 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,667 | ornl_14 | HT9 | RAFM_steel | irradiated | 208 | 407 | FFTF | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,669 | ornl_14 | HT9 | RAFM_steel | irradiated | 208 | 406 | FFTF | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,670 | ornl_14 | HT9 | RAFM_steel | irradiated | 208 | 403 | FFTF | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,671 | ornl_14 | HT9 | RAFM_steel | irradiated | 208 | 420 | FFTF | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,673 | ornl_14 | HT9 | RAFM_steel | irradiated | 50 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,674 | ornl_14 | HT9 | RAFM_steel | irradiated | 200 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,675 | ornl_14 | 9Cr steel | RAFM_steel | irradiated | 100 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,676 | ornl_14 | 9Cr steel | RAFM_steel | irradiated | 200 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,677 | ornl_14 | HT9 | RAFM_steel | irradiated | 250 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,678 | ornl_14 | HT9 | RAFM_steel | irradiated | 50 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,679 | ornl_14 | HT9 | RAFM_steel | irradiated | 100 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,680 | ornl_14 | HT9 | RAFM_steel | irradiated | 150 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,681 | ornl_14 | HT9 | RAFM_steel | irradiated | 200 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,682 | ornl_14 | HT9 | RAFM_steel | irradiated | 230 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,683 | ornl_14 | 9Cr steel | RAFM_steel | irradiated | 50 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,684 | ornl_14 | 9Cr steel | RAFM_steel | irradiated | 100 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,685 | ornl_14 | 9Cr steel | RAFM_steel | irradiated | 150 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,686 | ornl_14 | 9Cr steel | RAFM_steel | irradiated | 200 | null | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,687 | ornl_14 | 2 1/4Cr-2WV steel | RAFM_steel | unirradiated | null | 1,050 | null | null | null | null | Mechanical Hardness | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,689 | ornl_14 | Steel with 0.25% V, Tempered 700°C | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 830 | 910 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,690 | ornl_14 | Steel with 0.50% V, Tempered 700°C | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 860 | 930 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,692 | ornl_14 | Steel with 0.25% V, Tempered 750°C | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 610 | 700 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,693 | ornl_14 | Steel with 0.50% V, Tempered 750°C | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 630 | 730 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,694 | ornl_14 | 2 1/4CrV | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 680 | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,697 | ornl_14 | 2 1/4CrVTi | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 580 | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.