record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
4,819 | ornl_14 | austenitic stainless steels | austenitic_steel | irradiated | 1 | 300 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,820 | ornl_14 | austenitic stainless steels | austenitic_steel | irradiated | 10 | 500 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,821 | ornl_14 | 300-series stainless steels | other | irradiated | 50 | null | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,822 | ornl_14 | radiation-resistant developmental steels | other | irradiated | 100 | null | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,824 | ornl_14 | SA 316 stainless steel | austenitic_steel | irradiated | 10 | null | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,825 | ornl_14 | 20%CW PCA stainless steel | austenitic_steel | irradiated | 7.4 | 330 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,826 | ornl_14 | 20%CW PCA stainless steel | austenitic_steel | irradiated | 7.4 | 400 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,827 | ornl_14 | 316 austenitic steel | austenitic_steel | irradiated | 0 | 400 | fission | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,829 | ornl_14 | 316 austenitic steel | austenitic_steel | irradiated | 5 | 400 | fission | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,830 | ornl_14 | 25% CW PCA austenitic steel | austenitic_steel | irradiated | 0 | 400 | fission | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,831 | ornl_14 | 25% CW PCA austenitic steel | austenitic_steel | irradiated | 15 | 400 | fission | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,832 | ornl_14 | 25% CW PCA austenitic steel | austenitic_steel | irradiated | 7.4 | 300 | ORR (6J/7J) | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,833 | ornl_14 | 25% CW PCA austenitic steel | austenitic_steel | irradiated | 7.4 | 400 | ORR (6J/7J) | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,834 | ornl_14 | 25% CW PCA austenitic steel | austenitic_steel | irradiated | 7.4 | 500 | ORR (6J/7J) | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,835 | ornl_14 | stainless steel | other | irradiated | null | 525 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,836 | ornl_14 | austenitic steel | other | irradiated | null | 400 | mixed-spectrum | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | 100,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,837 | ornl_14 | SA type 316 | austenitic_steel | irradiated | 0.5 | 400 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,839 | ornl_14 | 304 SS | austenitic_steel | irradiated | 0.5 | 300 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | 150,000,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,841 | ornl_14 | Austenitic stainless steel (SA CW) | austenitic_steel | irradiated | null | 500 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | 1,000,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,842 | ornl_14 | Austenitic stainless steel (SA CW) | austenitic_steel | irradiated | null | 600 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | 100,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,843 | ornl_14 | Fe-13 Cr-14Ni | ferritic_model_alloy | irradiated | 5 | 400 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | 1,500,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,846 | ornl_14 | 20% CW 316 | austenitic_steel | irradiated | 50 | null | fast-breeder reactor | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,848 | ornl_14 | Pure Austenites (Annealed) | other | irradiated | 60 | 500 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 30 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,849 | ornl_14 | 316 SS (Annealed) | austenitic_steel | irradiated | 100 | 500 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 20 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,850 | ornl_14 | Advanced Ti-Modified Austenites | other | irradiated | 120 | 500 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,852 | ornl_14 | French 20-25% CW 15-15Ti steel modified with B+P | RAFM_steel | irradiated | 150 | null | Fast reactor | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,853 | ornl_14 | Japanese PNC316 steel modified with Ti+P+B | RAFM_steel | irradiated | 80 | null | Fast reactor | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,854 | ornl_14 | Fe-Cr | ferritic_model_alloy | irradiated | 50 | 500 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,855 | ornl_14 | type 316 austenitic stainless steel (US316) | austenitic_steel | irradiated | 3 | 60 | HFIR | neutron | null | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,856 | ornl_14 | type 316 austenitic stainless steel (J316) | austenitic_steel | irradiated | 3 | 250 | HFIR | neutron | null | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,857 | ornl_14 | 316L steel (EC316L) | austenitic_steel | irradiated | 3 | 60 | HFIR | neutron | null | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,858 | ornl_14 | EC316L steel | RAFM_steel | unirradiated | 0 | null | null | null | null | 22 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,861 | ornl_14 | EC316L steel | RAFM_steel | irradiated | 3 | 92.5 | null | neutron | null | 25 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,862 | ornl_14 | EC316L steel | RAFM_steel | irradiated | 3 | 92.5 | null | neutron | null | 100 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,863 | ornl_14 | EC316L steel | RAFM_steel | irradiated | 3 | 92.5 | null | neutron | null | 200 | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,864 | ornl_14 | EC316L ANNEALED | RAFM_steel | unirradiated | 0 | null | null | neutron | null | 25 | Mechanical Fracture | null | null | null | null | 385 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,867 | ornl_14 | EC316L ANNEALED | RAFM_steel | irradiated | 3 | null | null | neutron | null | 25 | Mechanical Fracture | null | null | null | null | 395 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,868 | ornl_14 | EC316L ANNEALED | RAFM_steel | irradiated | 3 | null | null | neutron | null | 100 | Mechanical Fracture | null | null | null | null | 370 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,870 | ornl_14 | JPCA ANNEALED | RAFM_steel | unirradiated | 0 | null | null | neutron | null | 25 | Mechanical Fracture | null | null | null | null | 365 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,871 | ornl_14 | JPCA ANNEALED | RAFM_steel | unirradiated | 0 | null | null | neutron | null | 100 | Mechanical Fracture | null | null | null | null | 370 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,872 | ornl_14 | JPCA ANNEALED | RAFM_steel | unirradiated | 0 | null | null | neutron | null | 200 | Mechanical Fracture | null | null | null | null | 315 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,873 | ornl_14 | JPCA ANNEALED | RAFM_steel | irradiated | 3 | null | null | neutron | null | 25 | Mechanical Fracture | null | null | null | null | 270 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,874 | ornl_14 | JPCA ANNEALED | RAFM_steel | irradiated | 3 | null | null | neutron | null | 100 | Mechanical Fracture | null | null | null | null | 250 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,875 | ornl_14 | JPCA ANNEALED | RAFM_steel | irradiated | 3 | null | null | neutron | null | 200 | Mechanical Fracture | null | null | null | null | 215 | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,876 | ornl_14 | EC316L annealed | austenitic_steel | unirradiated | null | null | null | null | null | 22 | Mechanical Fracture | null | null | null | null | 385 | null | null | null | null | null | null | null | 769 | 0.55 | false | ornl_extraction | null | null | null | null |
4,877 | ornl_14 | EC316L annealed | austenitic_steel | unirradiated | null | null | null | null | null | 100 | Mechanical Fracture | null | null | null | null | 407 | null | null | null | null | null | null | null | 889 | 0.55 | false | ornl_extraction | null | null | null | null |
4,878 | ornl_14 | EC316L annealed | austenitic_steel | unirradiated | null | null | null | null | null | 200 | Mechanical Fracture | null | null | null | null | 353 | null | null | null | null | null | null | null | 696 | 0.55 | false | ornl_extraction | null | null | null | null |
4,879 | ornl_14 | EC316L annealed | austenitic_steel | irradiated | 3 | 60 | HFIR | neutron | null | 25 | Mechanical Fracture | null | null | null | null | 387 | null | null | null | null | null | null | null | 775 | 0.9 | false | ornl_extraction | null | null | null | null |
4,880 | ornl_14 | EC316L annealed | austenitic_steel | irradiated | 3 | 60 | HFIR | neutron | null | 25 | Mechanical Fracture | null | null | null | null | 393 | null | null | null | null | null | null | null | 802 | 0.9 | false | ornl_extraction | null | null | null | null |
4,884 | ornl_14 | JPCA annealed | austenitic_steel | unirradiated | null | null | null | null | null | 100 | Mechanical Fracture | null | null | null | null | 362 | null | null | null | null | null | null | null | 705 | 0.55 | false | ornl_extraction | null | null | null | null |
4,885 | ornl_14 | JPCA annealed | austenitic_steel | unirradiated | null | null | null | null | null | 200 | Mechanical Fracture | null | null | null | null | 299 | null | null | null | null | null | null | null | 499 | 0.55 | false | ornl_extraction | null | null | null | null |
4,886 | ornl_14 | JPCA annealed | austenitic_steel | irradiated | 3 | 60 | HFIR | neutron | null | 22 | Mechanical Fracture | null | null | null | null | 270 | null | null | null | null | null | null | null | 379 | 0.9 | false | ornl_extraction | null | null | null | null |
4,887 | ornl_14 | JPCA annealed | austenitic_steel | irradiated | 3 | 60 | HFIR | neutron | null | 100 | Mechanical Fracture | null | null | null | null | 245 | null | null | null | null | null | null | null | 323 | 0.9 | false | ornl_extraction | null | null | null | null |
4,888 | ornl_14 | JPCA annealed | austenitic_steel | irradiated | 3 | 60 | HFIR | neutron | null | 200 | Mechanical Fracture | null | null | null | null | 208 | null | null | null | null | null | null | null | 242 | 0.9 | false | ornl_extraction | null | null | null | null |
4,889 | ornl_14 | J316 annealed | austenitic_steel | unirradiated | null | null | null | null | null | 22 | Mechanical Fracture | null | null | null | null | 393 | null | null | null | null | null | null | null | 798 | 0.55 | false | ornl_extraction | null | null | null | null |
4,890 | ornl_14 | JPCA cold worked | austenitic_steel | unirradiated | null | null | null | null | null | 22 | Mechanical Fracture | null | null | null | null | 262 | null | null | null | null | null | null | null | 356 | 0.55 | false | ornl_extraction | null | null | null | null |
4,891 | ornl_14 | US316 cold worked | austenitic_steel | unirradiated | null | null | null | null | null | 22 | Mechanical Fracture | null | null | null | null | 85 | null | null | null | null | null | null | null | 37 | 0.55 | false | ornl_extraction | null | null | null | null |
4,894 | ornl_14 | W | tungsten | irradiated | 34 | 520 | FFTF/MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -2.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,895 | ornl_14 | W | tungsten | irradiated | 34 | 600 | FFTF/MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -2.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,896 | ornl_14 | PCA (titanium-modified austenitic stainless steel) | austenitic_steel | irradiated | 15 | 472.5 | EBR-II | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,897 | ornl_14 | PCA | austenitic_steel | irradiated | 36.1 | 423 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.29 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,898 | ornl_14 | PCA | austenitic_steel | irradiated | 36.3 | 520 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.28 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,900 | ornl_14 | PCA-Annealed | austenitic_steel | irradiated | 36.1 | 423 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.51 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,901 | ornl_14 | PCA-Annealed | austenitic_steel | irradiated | 36.3 | 520 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.37 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,902 | ornl_14 | PCA-Annealed | austenitic_steel | irradiated | 32.3 | 600 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.13 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,903 | ornl_14 | PCA-Annealed | austenitic_steel | irradiated | 32.3 | 600 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -1.04 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,904 | ornl_14 | Nb-1Zr | refractory_metal | irradiated | 15 | 431 | FFTF-MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,905 | ornl_14 | Nb-1Zr (Specimen N6EZ) | refractory_metal | irradiated | 47.2 | 431 | FFTF-MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,906 | ornl_14 | Nb-1Zr (Specimen M6EZ) | refractory_metal | irradiated | 105.7 | 431 | FFTF-MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,907 | ornl_14 | Nb-1Zr (Specimen PAE1) | refractory_metal | irradiated | 57.6 | 471 | FFTF-MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,908 | ornl_14 | Nb-1Zr (Specimen PAE6) | refractory_metal | irradiated | 58.1 | 722 | FFTF-MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,909 | ornl_14 | Nb-1Zr | refractory_metal | irradiated | 60 | 645 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,910 | ornl_14 | Nb-1Zr (20% Cold-Worked and Aged 2 hrs at 320 °C) | refractory_metal | irradiated | 110 | 420 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,911 | ornl_14 | Nb-1Zr (Annealed 1 hr at 760 °C and Aged 2 hrs at 320 °C) | refractory_metal | irradiated | 105 | 420 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -1.3 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,912 | ornl_14 | V-20Ti alloy | vanadium_alloy | irradiated | 62 | 600 | Fast Flux Test Facility (FFTF) | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,913 | ornl_14 | V-20Ti | vanadium_alloy | irradiated | 44 | 600 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,914 | ornl_14 | V-20Ti | vanadium_alloy | irradiated | 80 | 600 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,915 | ornl_14 | V-20Ti doped with 120 wppm 10B | vanadium_alloy | irradiated | 42 | 520 | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,916 | ornl_14 | V alloy | vanadium_alloy | irradiated | null | 420 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,917 | ornl_14 | V alloy | vanadium_alloy | irradiated | null | 520 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,918 | ornl_14 | V alloy | vanadium_alloy | irradiated | 29 | null | FFTF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,919 | ornl_14 | V alloy | vanadium_alloy | irradiated | 29 | 425 | FFTF/MOTA | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,921 | ornl_14 | V-Cr-Ti | vanadium_alloy | irradiated | null | 420 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,922 | ornl_14 | V-15Cr-5Ti | vanadium_alloy | irradiated | null | null | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 523.15 | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,923 | ornl_14 | Al2O3 | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,924 | ornl_14 | HfO2-strengthened alloy | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,925 | ornl_14 | copper alloys | copper_alloy | irradiated | 104 | 415 | FFTF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,926 | ornl_14 | CuAl15 + boron | copper_alloy | irradiated | null | 415 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,927 | ornl_14 | CuAl20 | copper_alloy | irradiated | null | 415 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,928 | ornl_14 | CuAl25 | copper_alloy | irradiated | null | 415 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,929 | ornl_14 | Cu-HfO2 | copper_alloy | irradiated | null | 415 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,932 | ornl_14 | ODS steel | copper_alloy | irradiated | null | 415 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,934 | ornl_14 | ODS steel | copper_alloy | irradiated | 50 | null | FFTF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,935 | ornl_14 | ODS steel | copper_alloy | irradiated | 50 | null | FFTF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,936 | ornl_14 | ODS steel | copper_alloy | irradiated | 150 | null | FFTF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,939 | ornl_14 | ODS steel | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 85 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,940 | ornl_14 | Pure Cu | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 80 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,941 | ornl_14 | ODS steel | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 75 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,943 | ornl_14 | ODS steel | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 55 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,944 | ornl_14 | ODS steel | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.