record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
4,698 | ornl_14 | 2 1/4Cr-2WVTi | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 780 | 850 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,699 | ornl_14 | 2 1/4CrV | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 560 | 650 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,700 | ornl_14 | 2 1/4Cr-2W | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 560 | 640 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,701 | ornl_14 | 2 1/4Cr-2WV | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 655 | 730 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,703 | ornl_14 | 2 1/4Cr-2WTi | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 500 | 615 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,704 | ornl_14 | 2 1/4Cr-2WVTi | RAFM_steel | unirradiated | null | null | null | null | null | 25 | Mechanical Tensile | null | null | null | null | null | null | 560 | 650 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,705 | ornl_14 | 2 1/4Cr-2WV | RAFM_steel | unirradiated | null | null | null | null | null | 600 | Mechanical Tensile | null | null | null | null | null | null | 540 | 585 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,707 | ornl_14 | 2 1/4Cr-2WTi | RAFM_steel | unirradiated | null | null | null | null | null | 600 | Mechanical Tensile | null | null | null | null | null | null | 385 | 495 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,708 | ornl_14 | 2 1/4Cr-2WVTi | RAFM_steel | unirradiated | null | null | null | null | null | 600 | Mechanical Tensile | null | null | null | null | null | null | 430 | 505 | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
4,709 | ornl_14 | Type 316 stainless steel | austenitic_steel | irradiated | null | 300 | null | null | 256 | null | Microstructure | null | null | null | null | null | null | 220 | null | null | null | 1.7 | 450,000,000,000,000,000,000 | null | 0.8 | false | ornl_extraction | 70 | null | 2 | null |
4,710 | ornl_14 | PCA | austenitic_steel | irradiated | 178 | 400 | MOTA-1G | neutron | null | 400 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,711 | ornl_14 | PCA | austenitic_steel | irradiated | 178 | 400 | null | null | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,712 | ornl_14 | PCA | austenitic_steel | irradiated | 178 | 400 | null | null | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,713 | ornl_14 | PCA | austenitic_steel | irradiated | 178 | 400 | null | null | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,714 | ornl_14 | PCA | austenitic_steel | irradiated | 178 | 400 | null | null | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,715 | ornl_14 | PCA | austenitic_steel | irradiated | 178 | 400 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,716 | ornl_14 | PCA | austenitic_steel | irradiated | 178 | 400 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,717 | ornl_14 | PCA | austenitic_steel | irradiated | 178 | 400 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,718 | ornl_14 | PCA | austenitic_steel | irradiated | 178 | 400 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,719 | ornl_14 | PCA | austenitic_steel | irradiated | 178 | 400 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,720 | ornl_14 | PCA | austenitic_steel | irradiated | 178 | 400 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,722 | ornl_14 | Stress-affected swelling (140 MPa hoop stress) | other | irradiated | 160 | 400 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 18 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,723 | ornl_14 | Stress-affected swelling (100 MPa hoop stress) | other | irradiated | 160 | 400 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 17 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,724 | ornl_14 | Stress-affected swelling (60 MPa hoop stress) | other | irradiated | 160 | 400 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 14.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,725 | ornl_14 | Stress-affected swelling (0, 30 MPa hoop stress) | other | irradiated | 160 | 400 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 13 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,727 | ornl_14 | Mo | refractory_metal | irradiated | 105.7 | 420 | MOTA | neutron | null | 420 | Swelling | null | null | null | null | null | null | null | null | null | 0.11 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,728 | ornl_14 | Mo | refractory_metal | irradiated | 32.2 | 471 | MOTA | neutron | null | 471 | Swelling | null | null | null | null | null | null | null | null | null | -2.26 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,729 | ornl_14 | Mo | refractory_metal | irradiated | 43.7 | 471 | MOTA | neutron | null | 471 | Swelling | null | null | null | null | null | null | null | null | null | -0.28 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,730 | ornl_14 | Mo | refractory_metal | irradiated | 40.8 | 569 | MOTA | neutron | null | 569 | Swelling | null | null | null | null | null | null | null | null | null | 0.72 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,731 | ornl_14 | Mo | refractory_metal | irradiated | 63.9 | 569 | MOTA | neutron | null | 569 | Swelling | null | null | null | null | null | null | null | null | null | 0.52 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,732 | ornl_14 | Mo | refractory_metal | irradiated | 40.8 | 645 | MOTA | neutron | null | 645 | Swelling | null | null | null | null | null | null | null | null | null | 0.66 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,733 | ornl_14 | Mo | refractory_metal | irradiated | 65.8 | 645 | MOTA | neutron | null | 645 | Swelling | null | null | null | null | null | null | null | null | null | 1.41 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,734 | ornl_14 | Mo | refractory_metal | irradiated | 40.8 | 730 | MOTA | neutron | null | 730 | Swelling | null | null | null | null | null | null | null | null | null | 1.45 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,735 | ornl_14 | Mo | refractory_metal | irradiated | 61.5 | 730 | MOTA | neutron | null | 730 | Swelling | null | null | null | null | null | null | null | null | null | -0.07 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,736 | ornl_14 | Mo-41Re | refractory_metal | irradiated | 47.2 | 420 | MOTA | neutron | null | 420 | Swelling | null | null | null | null | null | null | null | null | null | -0.08 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,737 | ornl_14 | Mo-41Re | refractory_metal | irradiated | 105.7 | 420 | MOTA | neutron | null | 420 | Swelling | null | null | null | null | null | null | null | null | null | 0.28 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,739 | ornl_14 | Mo-41Re | refractory_metal | irradiated | 43.7 | 471 | MOTA | neutron | null | 471 | Swelling | null | null | null | null | null | null | null | null | null | -0.25 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,740 | ornl_14 | Mo-41Re | refractory_metal | irradiated | 40.8 | 569 | MOTA | neutron | null | 569 | Swelling | null | null | null | null | null | null | null | null | null | 1.14 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,741 | ornl_14 | Mo-41Re | refractory_metal | irradiated | 63.9 | 569 | MOTA | neutron | null | 569 | Swelling | null | null | null | null | null | null | null | null | null | 0.12 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,742 | ornl_14 | Mo-41Re | refractory_metal | irradiated | 40.8 | 645 | MOTA | neutron | null | 645 | Swelling | null | null | null | null | null | null | null | null | null | 0.04 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,743 | ornl_14 | Mo-41Re | refractory_metal | irradiated | 65.8 | 645 | MOTA | neutron | null | 645 | Swelling | null | null | null | null | null | null | null | null | null | 0.15 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,745 | ornl_14 | Mo-41Re | refractory_metal | irradiated | 61.5 | 730 | MOTA | neutron | null | 730 | Swelling | null | null | null | null | null | null | null | null | null | -0.49 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,746 | ornl_14 | Pure Molybdenum | refractory_metal | irradiated | 30 | 420 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.8 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,747 | ornl_14 | Pure Molybdenum | refractory_metal | irradiated | 60 | 420 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,748 | ornl_14 | Pure Molybdenum | refractory_metal | irradiated | 60 | 420 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.3 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,751 | ornl_14 | Pure Molybdenum | refractory_metal | irradiated | 60 | 471 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,752 | ornl_14 | Pure Molybdenum | refractory_metal | irradiated | 60 | 471 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.8 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,753 | ornl_14 | Pure Molybdenum | refractory_metal | irradiated | 60 | 569 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,755 | ornl_14 | Pure Molybdenum | refractory_metal | irradiated | 60 | 730 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,756 | ornl_14 | Mo-41Re | refractory_metal | irradiated | 20 | 471 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.3 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,757 | ornl_14 | Mo-41Re | refractory_metal | irradiated | 40 | 471 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.2 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,759 | ornl_14 | Molybdenum | refractory_metal | irradiated | 100 | null | FFTF | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,760 | ornl_14 | MOTA-ZR Pressurized Tube | other | unirradiated | null | 420 | MOTA-2B | neutron | null | 420 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,764 | ornl_14 | MOTA-2B tubes | other | irradiated | null | 519 | MOTA | neutron | null | 519 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,765 | ornl_14 | MOTA-2B tubes | other | irradiated | null | 599 | MOTA | neutron | null | 599 | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,766 | ornl_14 | ISPRA-A | RAFM_steel | irradiated | 34 | 420 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,767 | ornl_14 | ISPRA-B | RAFM_steel | irradiated | 34 | 520 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,768 | ornl_14 | ISPRA-C | RAFM_steel | irradiated | 34 | 600 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,769 | ornl_14 | ISPRA-A | RAFM_steel | irradiated | 35.1 | 423 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.96 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,770 | ornl_14 | ISPRA-A | RAFM_steel | irradiated | 36.3 | 520 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.23 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,771 | ornl_14 | ISPRA-A | RAFM_steel | irradiated | 32.3 | 600 | MOTA-2A | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.15 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,772 | ornl_14 | ISPRA-a | RAFM_steel | irradiated | 35.1 | 423 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.3 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,773 | ornl_14 | ISPRA-a | RAFM_steel | irradiated | 36.3 | 520 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.07 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,774 | ornl_14 | ISPRA-a | RAFM_steel | irradiated | 32.3 | 600 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.99 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,775 | ornl_14 | ISPRA-C | RAFM_steel | irradiated | 35.1 | 423 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.49 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,776 | ornl_14 | ISPRA-C | RAFM_steel | irradiated | 36.3 | 520 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 3.97 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,777 | ornl_14 | ISPRA-C | RAFM_steel | irradiated | 32.3 | 600 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.96 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,778 | ornl_14 | ISPRA-D | RAFM_steel | irradiated | 35.1 | 423 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.28 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,779 | ornl_14 | ISPRA-D | RAFM_steel | irradiated | 36.3 | 520 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.58 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,780 | ornl_14 | ISPRA-D | RAFM_steel | irradiated | 32.3 | 600 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.72 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,781 | ornl_14 | ISPRA-E | RAFM_steel | irradiated | 35.1 | 423 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.52 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,782 | ornl_14 | ISPRA-E | RAFM_steel | irradiated | 36.3 | 520 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.08 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,783 | ornl_14 | ISPRA-E | RAFM_steel | irradiated | 32.3 | 600 | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.58 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,787 | ornl_14 | MnCrC | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 105 | 415 | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,788 | ornl_14 | MnCrCTi | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 145 | 475 | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,789 | ornl_14 | MnCrCW | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 105 | 440 | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,790 | ornl_14 | MnCrCTiW | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 145 | 480 | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,791 | ornl_14 | MnCrCTiBP | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 145 | 485 | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,792 | ornl_14 | MnCrCTiVBP | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 165 | 525 | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,793 | ornl_14 | MnCrCTiWVBP | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 150 | 480 | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,795 | ornl_14 | MnCrC | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 490 | 630 | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,796 | ornl_14 | MnCrCTi | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 545 | 710 | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,798 | ornl_14 | MnCrCTiW | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 565 | 725 | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,799 | ornl_14 | MnCrCTiBP | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 540 | 700 | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,801 | ornl_14 | MnCrCTiWVBP | other | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 580 | 750 | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,802 | ornl_14 | 316 SS | austenitic_steel | unirradiated | null | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 540 | 695 | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
4,803 | ornl_14 | JPCA | austenitic_steel | irradiated | 7.4 | 330 | ORR | neutron | 21 | 330 | Swelling | null | null | null | null | null | null | null | null | null | 0.01 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,804 | ornl_14 | alloy K | other | irradiated | 7.4 | 330 | ORR | neutron | 21 | 330 | Swelling | null | null | null | null | null | null | null | null | null | 0.2 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,805 | ornl_14 | alloy K | other | irradiated | 7.4 | 400 | ORR | neutron | 21 | 400 | Swelling | null | null | null | null | null | null | null | null | null | 0.6 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,806 | ornl_14 | JPCA | austenitic_steel | irradiated | 33 | null | HFIR | neutron | 2,508 | 300 | Swelling | null | null | null | null | null | null | null | null | null | 0.2 | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,807 | ornl_14 | JPCA | austenitic_steel | irradiated | null | 330 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | 40,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,808 | ornl_14 | all alloys | other | irradiated | null | 400 | ORR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | 10,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,809 | ornl_14 | JPCA | austenitic_steel | irradiated | null | 300 | HFIR | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.2 | null | 400,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,810 | ornl_14 | K alloy | other | irradiated | null | 300 | HFIR | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.2 | null | 400,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,811 | ornl_14 | JPCA | austenitic_steel | irradiated | null | 400 | HFIR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | 200,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,812 | ornl_14 | K alloy | other | irradiated | null | 400 | HFIR | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | 200,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,814 | ornl_14 | JPCA | austenitic_steel | irradiated | null | 400 | ORR | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.04 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,815 | ornl_14 | JPCA | austenitic_steel | irradiated | 7.4 | 327 | ORR | neutron | null | 327 | Microstructure | null | null | null | null | null | null | null | null | null | 0.02 | 4 | 10,000,000,000,000,000,000,000 | null | 0.9 | false | ornl_extraction | null | null | 15 | null |
4,816 | ornl_14 | JPCA | austenitic_steel | irradiated | 7.4 | 427 | ORR | neutron | null | 427 | Microstructure | null | null | null | null | null | null | null | null | null | 0.15 | 15 | 20,000,000,000,000,000,000,000 | null | 0.9 | false | ornl_extraction | null | null | 15 | null |
4,817 | ornl_14 | JPCA | austenitic_steel | irradiated | 7.4 | 327 | HFIR | neutron | null | 327 | Microstructure | null | null | null | null | null | null | null | null | null | null | 5 | 200,000,000,000,000,000,000,000 | null | 0.9 | false | ornl_extraction | null | null | 10 | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.