record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
4,945 | ornl_14 | ODS steel | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,946 | ornl_14 | ODS steel | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,947 | ornl_14 | ODS steel | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,948 | ornl_14 | Cu-HfO2 | copper_alloy | irradiated | 50 | null | null | null | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,949 | ornl_14 | ODS steel | copper_alloy | unirradiated | 0 | null | null | null | null | 415 | Mechanical Tensile | null | null | null | null | null | null | 340 | 380 | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,950 | ornl_14 | ODS steel | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | 415 | Mechanical Tensile | 100 | 110 | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
4,951 | ornl_14 | Cu-Cr2O3 | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 25 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,952 | ornl_14 | Cu-HfO2 | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,953 | ornl_14 | CuAl25 | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 20 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,954 | ornl_14 | Cu-HfO2 | copper_alloy | unirradiated | 0 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | 380 | 480 | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,956 | ornl_14 | Cu-HfO2 | copper_alloy | irradiated | 100 | 415 | FFTF | neutron | null | null | Electrical | 340 | 410 | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,957 | ornl_14 | Cu-HfO2 | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Electrical | 335 | 405 | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,958 | ornl_14 | Cu-Cr2O3 | copper_alloy | unirradiated | 0 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | 280 | 350 | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,959 | ornl_14 | Cu-Cr2O3 | copper_alloy | irradiated | 50 | 415 | FFTF | neutron | null | null | Electrical | 240 | 320 | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,960 | ornl_14 | Cu-Cr2O3 | copper_alloy | irradiated | 100 | 415 | FFTF | neutron | null | null | Electrical | 200 | 280 | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,961 | ornl_14 | Cu-Cr2O3 | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Electrical | 180 | 250 | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,962 | ornl_14 | CuAl15 + B | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 13.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,965 | ornl_14 | CuAl20, 20% CW | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,966 | ornl_14 | CuAl25, 50% CW | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,967 | ornl_14 | CuAl20, 20% CW | copper_alloy | irradiated | 0 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,968 | ornl_14 | CuAl20, 20% CW | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,969 | ornl_14 | CuAl25, 50% CW | copper_alloy | irradiated | 0 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,970 | ornl_14 | CuAl25, 50% CW | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,971 | ornl_14 | CuAl15 + B, Annealed | copper_alloy | irradiated | 0 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,972 | ornl_14 | CuAl15 + B, Annealed | copper_alloy | irradiated | 100 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,974 | ornl_14 | CuAl25 + Weld | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,976 | ornl_14 | CuAl20, 20% CW | copper_alloy | irradiated | 0 | 415 | FFTF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | 440 | 480 | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,977 | ornl_14 | CuAl15 + B | copper_alloy | unirradiated | 0 | 415 | FFTF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | 320 | 400 | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,978 | ornl_14 | CuAl25, Weld | copper_alloy | unirradiated | 0 | 415 | FFTF | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | 100 | 180 | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,979 | ornl_14 | CuAl25, 50% CW | copper_alloy | irradiated | 150 | 415 | FFTF | neutron | null | null | Mechanical Tensile | 450 | 480 | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,982 | ornl_14 | CuAl25 | copper_alloy | irradiated | 150 | null | null | neutron | null | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,983 | ornl_14 | CuAl25 | copper_alloy | unirradiated | 0 | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 380 | 450 | 28 | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,984 | ornl_14 | CuAl25 | copper_alloy | irradiated | 50 | null | null | neutron | null | null | Mechanical Tensile | 410 | 430 | 22 | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,986 | ornl_14 | Cu-Cr2O3 | copper_alloy | unirradiated | 0 | null | null | null | null | null | Mechanical Tensile | null | null | null | null | null | null | 320 | 420 | 25 | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,988 | ornl_14 | CuAl25 | copper_alloy | irradiated | 104 | 415 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,989 | ornl_14 | CuAl20 | copper_alloy | irradiated | 50 | 415 | null | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | 12 | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,990 | ornl_14 | CuAl20 | copper_alloy | irradiated | 150 | 415 | null | neutron | null | null | Mechanical Tensile | null | null | 5 | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,991 | ornl_14 | Cu-HfO2 | copper_alloy | irradiated | 50 | 415 | null | neutron | null | null | Mechanical Tensile | null | null | 20.5 | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,992 | ornl_14 | Cu-HfO2 | copper_alloy | irradiated | 150 | 415 | null | neutron | null | null | Mechanical Tensile | null | null | 20.5 | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
4,994 | ornl_14 | Marz Cu | copper_alloy | irradiated | 21.2 | 375 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 7 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,996 | ornl_14 | Marz Cu | copper_alloy | irradiated | 95.4 | 423 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 45.4 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,997 | ornl_14 | Cu-5Ni | copper_alloy | irradiated | 12.7 | 375 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.91 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,998 | ornl_14 | Cu-5Ni | copper_alloy | irradiated | 21.2 | 375 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.63 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
4,999 | ornl_14 | Cu-5Ni | copper_alloy | irradiated | 48 | 423 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 30.1 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,000 | ornl_14 | Cu-5Ni | copper_alloy | irradiated | 95.4 | 423 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 50.3 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,001 | ornl_14 | Cu-5Ni (40% CW) | copper_alloy | irradiated | 12.7 | 375 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.37 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,002 | ornl_14 | Cu-5Ni (40% CW) | copper_alloy | irradiated | 21.2 | 375 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.85 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,003 | ornl_14 | Cu-5Ni (40% CW) | copper_alloy | irradiated | 48 | 423 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 22.1 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,004 | ornl_14 | Cu-5Ni (40% CW) | copper_alloy | irradiated | 95.4 | 423 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 35.9 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,005 | ornl_14 | Cu-5Mn | copper_alloy | irradiated | 12.7 | 375 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.004 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,007 | ornl_14 | Cu-5Mn | copper_alloy | irradiated | 48 | 423 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.04 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,008 | ornl_14 | Cu-5Mn | copper_alloy | irradiated | 95.4 | 423 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2.4 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,009 | ornl_14 | Cu-5Mn (40% CW) | copper_alloy | irradiated | 12.7 | 375 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -0.03 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,010 | ornl_14 | Cu-5Mn (40% CW) | copper_alloy | irradiated | 21.2 | 375 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.72 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,011 | ornl_14 | Cu-5Mn (40% CW) | copper_alloy | irradiated | 48 | 423 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.13 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,012 | ornl_14 | Cu-5Mn (40% CW) | copper_alloy | irradiated | 95.4 | 423 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 2 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,013 | ornl_14 | Annealed Pure Copper | copper_alloy | irradiated | 48 | 375 | MOTA 2A/2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,015 | ornl_14 | 40% Cold Worked Copper | copper_alloy | irradiated | 115 | 423 | MOTA 2A/2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 45 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,016 | ornl_14 | Cu-5Ni | copper_alloy | irradiated | 48 | 423 | MOTA 2A/2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 22 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,017 | ornl_14 | Cu-5Mn | copper_alloy | irradiated | 100 | 423 | MOTA 2A/2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,018 | ornl_14 | Pure Cu | copper_alloy | irradiated | 150 | 411 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 75 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,019 | ornl_14 | copper alloys | copper_alloy | irradiated | 7 | 120 | SM-3 | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,020 | ornl_14 | copper alloys | copper_alloy | irradiated | 7 | 250 | SM-3 | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,021 | ornl_14 | copper alloys | copper_alloy | irradiated | 7 | 340 | SM-3 | neutron | null | null | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,022 | ornl_14 | copper alloys | copper_alloy | irradiated | 1 | null | SM-3 | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,023 | ornl_14 | GlidCop Al25 (no B), as-wrought | copper_alloy | irradiated | null | 110 | SM reactor | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,024 | ornl_14 | GlidCop Al25 + B, as-wrought | copper_alloy | irradiated | null | 110 | SM reactor | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,025 | ornl_14 | Cu-Cr-Zr(MZC), CW + aged | copper_alloy | irradiated | null | 250 | SM reactor | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,026 | ornl_14 | Al2O3 | copper_alloy | irradiated | null | 340 | SM reactor | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,027 | ornl_14 | GlidCop A125 | copper_alloy | irradiated | 30 | 350 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | 0 | 6 | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,030 | ornl_14 | GlidCop | copper_alloy | irradiated | 30 | 180 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 2 | 500,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,031 | ornl_14 | GlidCop | copper_alloy | irradiated | null | 350 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | 7,000,000,000,000,000,000,000 | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,032 | ornl_14 | GlidCop Al25 | copper_alloy | irradiated | 30 | 180 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 6 | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,034 | ornl_14 | GlidCop A125 | copper_alloy | irradiated | 30 | 180 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,035 | ornl_14 | MAGT 0.2 | copper_alloy | irradiated | 20 | null | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,036 | ornl_14 | MAGT 0.2 | copper_alloy | irradiated | 7 | 400 | ion_beam | ion | null | 400 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | 6 | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,037 | ornl_14 | GlideCop A125 | copper_alloy | irradiated | 20 | null | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 6 | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,038 | ornl_14 | GlideCop A125 | copper_alloy | irradiated | 16 | 415 | null | neutron | null | 25 | Mechanical Tensile | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,039 | ornl_14 | 316NG | austenitic_steel | unirradiated | null | null | null | null | null | 95 | Mechanical Tensile | null | null | null | null | null | null | 329 | 563 | 16.8 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
5,041 | ornl_14 | 316NG | austenitic_steel | unirradiated | null | null | null | null | null | 95 | Mechanical Tensile | null | null | null | null | null | null | 327 | 568 | 18.1 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
5,042 | ornl_14 | 316NG | austenitic_steel | unirradiated | null | null | null | null | null | 225 | Mechanical Tensile | null | null | null | null | null | null | 260 | 497 | 14.9 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
5,044 | ornl_14 | 316NG | austenitic_steel | unirradiated | null | null | null | null | null | 225 | Mechanical Tensile | null | null | null | null | null | null | 296 | 411 | 10 | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
5,045 | ornl_14 | V-20%Ti | vanadium_alloy | unirradiated | null | 860 | null | null | null | null | Mechanical Hardness | null | null | null | 25 | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,047 | ornl_14 | V-20%Ti aluminized layer | vanadium_alloy | unirradiated | null | 860 | null | null | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,048 | ornl_14 | pure oxide ceramics | ceramic_insulator | irradiated | null | 25 | ion_beam | ion | null | 25 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,050 | ornl_14 | Sapphire | ceramic_insulator | irradiated | 0 | 25 | fission_reactor | neutron | null | 25 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,051 | ornl_14 | Al2O3 | copper_alloy | unirradiated | null | 25 | fission_reactor | neutron | null | 25 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,052 | ornl_14 | Al2O3 | copper_alloy | irradiated | 0 | 25 | fission_reactor | neutron | null | 25 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,053 | ornl_14 | Al2O3 | copper_alloy | unirradiated | null | 25 | fission_reactor | neutron | null | 25 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,054 | ornl_14 | Al2O3 | copper_alloy | irradiated | 0 | 25 | fission_reactor | neutron | null | 25 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,055 | ornl_14 | Spinel | ceramic_insulator | unirradiated | null | 25 | fission_reactor | neutron | null | 25 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,056 | ornl_14 | Spinel | ceramic_insulator | irradiated | 0 | 25 | fission_reactor | neutron | null | 25 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,057 | ornl_14 | AlN | ceramic_insulator | unirradiated | null | 25 | fission_reactor | neutron | null | 25 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,058 | ornl_14 | AlN | ceramic_insulator | irradiated | 0 | 25 | fission_reactor | neutron | null | 25 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,060 | ornl_14 | Si3N4 | ceramic_insulator | irradiated | 0 | 25 | fission_reactor | neutron | null | 25 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,061 | ornl_14 | Al2O3 | copper_alloy | irradiated | 0.001 | 25 | ion_beam | proton | null | 25 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,063 | ornl_14 | Al2O3 | copper_alloy | irradiated | null | 650 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,064 | ornl_14 | MgO | ceramic_insulator | irradiated | null | 650 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,065 | ornl_14 | Al2O3 | copper_alloy | irradiated | 3.2 | 650 | ion_beam | ion | null | 650 | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,066 | ornl_14 | Al2O3 | copper_alloy | irradiated | 21 | 650 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.