record_id int64 332 22.6k | paper_id stringclasses 66
values | material_name stringlengths 1 60 | material_class stringclasses 21
values | irradiation_state stringclasses 2
values | dose_dpa float64 0 400 ⌀ | irradiation_temp_C float64 -273.15 3.1k ⌀ | reactor stringclasses 333
values | particle stringclasses 6
values | helium_appm float64 0.01 400k ⌀ | test_temp_C float64 -273.15 2k ⌀ | experiment_type stringclasses 16
values | yield_strength_mpa_irradiated float64 5 2.65k ⌀ | uts_mpa_irradiated float64 -1 24k ⌀ | elongation_pct_irradiated float64 -7.3 105 ⌀ | hardness_value float64 -45 588k ⌀ | fracture_toughness_mpa_sqrt_m float64 1 1.1k ⌀ | dbtt_k_irradiated float64 -50 1.27k ⌀ | yield_strength_mpa_unirradiated float64 -29 420k ⌀ | uts_mpa_unirradiated float64 -3 13.5k ⌀ | elongation_pct_unirradiated float64 -5 822 ⌀ | volumetric_swelling_pct float64 -60 140 ⌀ | void_diameter_nm float64 0 6.27k ⌀ | void_density_per_m3 float64 0 61,300,000,000,000,010B ⌀ | charpy_energy_j float64 0.1 1.1k ⌀ | confidence_score float64 0.5 1 | reviewed_by_human bool 2
classes | source stringclasses 2
values | grain_size_um float64 0 400 ⌀ | yield_strength_mpa_std float64 0 500 ⌀ | dislocation_loop_diameter_nm float64 1 500 ⌀ | electrical_resistivity_uohm_cm_irradiated float64 -0 42,000B ⌀ |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
5,067 | ornl_14 | Al2O3 | copper_alloy | irradiated | 5 | 25 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,068 | ornl_14 | Al2O3 | copper_alloy | irradiated | 54 | 25 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,069 | ornl_14 | Al2O3 | copper_alloy | irradiated | 90 | 25 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,070 | ornl_14 | Al2O3 | copper_alloy | irradiated | 34 | 25 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,071 | ornl_14 | MgAl2O4 | ceramic_insulator | irradiated | 5 | 25 | ion_beam | ion | null | 25 | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,072 | ornl_14 | Al2O3 | copper_alloy | irradiated | 0.4 | 650 | ion_beam | ion | null | 650 | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,073 | ornl_14 | MgO | ceramic_insulator | irradiated | 3 | 650 | ion_beam | proton | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,074 | ornl_14 | MgO | ceramic_insulator | irradiated | 21 | null | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,075 | ornl_14 | stoichiometric spinel | ceramic_insulator | irradiated | 0.1 | 600 | ion_beam | proton | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,076 | ornl_14 | spinel | ceramic_insulator | irradiated | 14 | null | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,077 | ornl_14 | Al2O3 | copper_alloy | irradiated | 0.01 | null | ion_beam | proton | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,078 | ornl_14 | Al2O3 | copper_alloy | irradiated | null | 25 | ion_beam | ion | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,079 | ornl_14 | Al2O3 | copper_alloy | irradiated | 0.005 | 150 | ion_beam | ion | null | 150 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,080 | ornl_14 | MgAl2O4 | ceramic_insulator | irradiated | 0.005 | 150 | ion_beam | ion | null | 150 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,082 | ornl_14 | Si3N4 | ceramic_insulator | irradiated | 0.005 | 150 | ion_beam | ion | null | 150 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,083 | ornl_14 | Al2O3 | copper_alloy | irradiated | 0.1 | 450 | null | null | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,084 | ornl_14 | MgAl2O4 | ceramic_insulator | irradiated | 0.1 | 450 | null | null | null | null | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,086 | ornl_14 | MgAl2O4 | ceramic_insulator | irradiated | 0.001 | 275 | ion_beam | ion | null | 275 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,087 | ornl_14 | MgAl2O4 | ceramic_insulator | irradiated | 0.001 | 150 | ion_beam | ion | null | 150 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,088 | ornl_14 | Al2O3 | copper_alloy | irradiated | 0.004 | 590 | ion_beam | ion | null | 590 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,089 | ornl_14 | Al2O3 | copper_alloy | irradiated | 0.005 | 500 | ion_beam | ion | null | 500 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,090 | ornl_14 | Al2O3 | copper_alloy | irradiated | 0.003 | 500 | ion_beam | proton | null | 500 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,091 | ornl_14 | Al2O3 | copper_alloy | irradiated | 0.001 | 300 | ion_beam | ion | null | 300 | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,093 | ornl_14 | Spinel (100**) | ceramic_insulator | irradiated | null | 385 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,095 | ornl_14 | Spinel (HP) | ceramic_insulator | irradiated | null | 750 | FFTF | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,096 | ornl_14 | HP | ceramic_insulator | unirradiated | null | 750 | null | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.75 | false | ornl_extraction | null | null | null | null |
5,097 | ornl_14 | HP-3B | ceramic_insulator | irradiated | null | 750 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,098 | ornl_14 | HP-3A | ceramic_insulator | irradiated | null | 750 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,099 | ornl_14 | HP-2B | ceramic_insulator | irradiated | null | 750 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,102 | ornl_14 | 111-1A | ceramic_insulator | irradiated | null | 750 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,104 | ornl_14 | 100-2B | ceramic_insulator | irradiated | null | 750 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,105 | ornl_14 | 100-3D | ceramic_insulator | irradiated | null | 750 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,106 | ornl_14 | Ceramic Specimens | ceramic_insulator | irradiated | null | 750 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,107 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | 1,100 | Mechanical Fracture | null | null | null | null | 15 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
5,108 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | 1,100 | Mechanical Fracture | null | null | null | null | 27 | null | null | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
5,111 | ornl_14 | sapphire | ceramic_insulator | irradiated | null | 590 | LASREF | neutron | null | 615 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,112 | ornl_14 | mineral-insulated electrical cables | ceramic_insulator | irradiated | null | 400 | LASREF | neutron | null | 395 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,113 | ornl_14 | Wesgo 995 Alumina | ceramic_insulator | irradiated | null | 665 | null | neutron | null | 665 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,114 | ornl_14 | Wesgo 995 Alumina | ceramic_insulator | irradiated | null | 615 | null | neutron | null | 615 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,116 | ornl_14 | Wesgo 995 Alumina | ceramic_insulator | irradiated | null | 395 | null | neutron | null | 395 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,117 | ornl_14 | Al2O3 | copper_alloy | irradiated | 0.00001 | 450 | LASREF | neutron | null | 450 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,118 | ornl_14 | Al2O3 | copper_alloy | irradiated | null | 500 | fission reactor | neutron | null | 500 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,120 | ornl_14 | Al2O3 | copper_alloy | irradiated | 0 | 405 | spallation neutron source | neutron | null | 405 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,121 | ornl_14 | Al2O3 | copper_alloy | irradiated | 0 | 490 | spallation neutron source | neutron | null | 490 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,122 | ornl_14 | Al2O3 | copper_alloy | irradiated | null | 560 | null | neutron | null | 560 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,124 | ornl_14 | Al2O3 | copper_alloy | irradiated | null | 355 | null | neutron | null | 355 | Electrical | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,128 | ornl_14 | Al2O3 | copper_alloy | irradiated | null | 827 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,129 | ornl_14 | Al2O3 | copper_alloy | irradiated | null | 742 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.3 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,130 | ornl_14 | Al2O3 | copper_alloy | irradiated | null | 652 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.1 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,131 | ornl_14 | MgAl2O4 | ceramic_insulator | irradiated | null | 827 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.8 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,132 | ornl_14 | MgAl2O4 | ceramic_insulator | irradiated | null | 652 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 0.3 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,133 | ornl_14 | CaPuTi2O7 | ceramic_insulator | irradiated | null | 77 | null | ion | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5.5 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,134 | ornl_14 | CaPuTi2O7 | ceramic_insulator | irradiated | null | 302 | null | ion | null | null | Swelling | null | null | null | null | null | null | null | null | null | 4.3 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,136 | ornl_14 | CaPuTi2O7 | ceramic_insulator | irradiated | 1 | 301.85 | null | ion | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,137 | ornl_14 | crystalline quartz (SiO2) | ceramic_insulator | irradiated | null | 25 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 14 | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,138 | ornl_14 | Macor | ceramic_insulator | irradiated | null | 25 | null | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 1.5 | null | null | null | 0.8 | false | ornl_extraction | 5.5 | null | null | null |
5,139 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | null | Mechanical Hardness | null | null | null | 45.6 | null | null | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,140 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | null | Mechanical Hardness | null | null | null | 44 | null | null | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,141 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | null | Mechanical Hardness | null | null | null | 46.4 | null | null | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,142 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | null | Mechanical Hardness | null | null | null | 43.7 | null | null | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,145 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | null | Mechanical Hardness | null | null | null | 39.7 | null | null | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,146 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | null | Mechanical Hardness | null | null | null | 45.6 | null | null | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,147 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | null | Mechanical Hardness | null | null | null | 34.9 | null | null | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,148 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | null | Mechanical Hardness | null | null | null | 48.2 | null | null | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,150 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | null | Mechanical Hardness | null | null | null | 41.7 | null | null | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,151 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | null | Mechanical Hardness | null | null | null | 43.1 | null | null | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,152 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | null | Mechanical Hardness | null | null | null | 44.5 | null | null | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,154 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | null | Mechanical Hardness | null | null | null | 20.2 | null | null | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,155 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | null | Mechanical Hardness | null | null | null | 43.7 | null | null | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,156 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | null | Mechanical Hardness | null | null | null | 37.2 | null | null | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,158 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | null | Mechanical Hardness | null | null | null | 23.9 | null | null | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,159 | ornl_14 | SiC | SiC_composite | unirradiated | null | null | null | null | null | null | Mechanical Hardness | null | null | null | 42.8 | null | null | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,161 | ornl_14 | SiC/SiC | SiC_composite | unirradiated | null | null | null | null | null | 1,200 | Mechanical Creep | null | null | null | null | null | null | 120 | null | null | null | null | null | null | 0.55 | false | ornl_extraction | null | null | null | null |
5,163 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 13.5 | 365 | Fast Flux Test Facility | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 29 | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,164 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 13.5 | 365 | Fast Flux Test Facility | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 15 | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,165 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 200 | 420 | FFTF/MOTA | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | 5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,166 | ornl_15 | HT9 | RAFM_steel | irradiated | 208 | 400 | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,167 | ornl_15 | 9Cr steel | RAFM_steel | irradiated | 208 | 400 | null | neutron | null | null | Mechanical Creep | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,168 | ornl_15 | 300 series austenitic stainless steel | austenitic_steel | irradiated | 3 | 60 | High Flux Isotope Reactor | neutron | 50 | 60 | Mechanical Fracture | null | null | null | null | 150 | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,170 | ornl_15 | Japanese Primary Candidate Alloy (JPCA) | austenitic_steel | irradiated | 18 | 300 | HFIR | neutron | null | 300 | Mechanical Tensile | null | null | 2 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,171 | ornl_15 | Japanese Primary Candidate Alloy (JPCA) | austenitic_steel | irradiated | 18 | 600 | HFIR | neutron | null | 600 | Mechanical Tensile | null | null | 7 | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,172 | ornl_15 | AMCR alloys | other | irradiated | 46.5 | 511.5 | MOTA-2A and MOTA-2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,173 | ornl_15 | W | tungsten | irradiated | 34 | 511.5 | FFTF/MOTAs 2A and 2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | -2.5 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,174 | ornl_15 | PCA | austenitic_steel | irradiated | 57.5 | 511.5 | FFTF/MOTAs 2A and 2B | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,175 | ornl_15 | V alloy | vanadium_alloy | irradiated | null | null | null | neutron | null | null | Mechanical Charpy | null | null | null | null | null | 203.15 | null | null | null | null | null | null | null | 0.5 | false | ornl_extraction | null | null | null | null |
5,176 | ornl_15 | Nb-1Zr | refractory_metal | irradiated | 111 | 730 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,177 | ornl_15 | Mo-41Re | refractory_metal | irradiated | 111 | 730 | FFTF | neutron | null | null | Swelling | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,178 | ornl_15 | GlidCopTM | copper_alloy | irradiated | 50 | 415 | null | neutron | null | null | Microstructure | null | null | null | null | null | null | null | null | null | null | 32.5 | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,179 | ornl_15 | alumina | ceramic_insulator | irradiated | 0.1 | 80 | HFBR | neutron | null | 80 | Dielectric | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.9 | false | ornl_extraction | null | null | null | null |
5,180 | ornl_15 | MgAl2O4 | ceramic_insulator | irradiated | null | 385 | FFTF-MOTA | neutron | null | null | Mechanical Hardness | null | null | null | null | null | null | null | null | null | 0 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,181 | ornl_15 | MgAl2O4 | ceramic_insulator | irradiated | null | 750 | FFTF-MOTA | neutron | null | null | Mechanical Hardness | null | null | null | null | null | null | null | null | null | 0 | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,182 | ornl_15 | JP9 | other | irradiated | 34 | null | null | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.75 | false | ornl_extraction | null | null | null | null |
5,184 | ornl_15 | JP15 | other | irradiated | 52 | null | null | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.75 | false | ornl_extraction | null | null | null | null |
5,185 | ornl_15 | JP17 | other | irradiated | 3 | 275 | HFIR | neutron | null | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,186 | ornl_15 | JP18 | other | irradiated | 3 | 92.5 | HFIR | neutron | null | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,187 | ornl_15 | JP19 | other | irradiated | 3 | 92.5 | HFIR | neutron | null | null | Mechanical Fracture | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.85 | false | ornl_extraction | null | null | null | null |
5,188 | ornl_15 | HFIR-MFE-JP20 | other | irradiated | 8 | 450 | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,190 | ornl_15 | HFIR-MFE-JP22 | other | irradiated | 35 | 450 | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,191 | ornl_15 | 6OJ-1 | other | irradiated | 11 | null | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
5,192 | ornl_15 | 330J-1 | other | irradiated | 11 | null | HFIR | neutron | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | null | 0.8 | false | ornl_extraction | null | null | null | null |
Subsets and Splits
No community queries yet
The top public SQL queries from the community will appear here once available.